CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
Comparative study of electrophoretic deposition of doped BaCeO3-based films on La2NiO4+δ and La1.7Ba0.3NiO4+δ cathode substrates
Authors
A. Farlenkov
E. Kalinina
+3 more
A. Kolchugin
E. Pikalova
N. Pikalova
Publication date
1 January 2019
Publisher
'MDPI AG'
Doi
Cite
Abstract
This paper presents the results of a comparative study of methods to prevent the loss of barium during the formation of thin-film proton-conducting electrolyte BaCe0.89Gd0.1Cu0.01O3-δ (BCGCuO) on La2NiO4+δ-based (LNO) cathode substrates by electrophoretic deposition (EPD). Three different methods of the BCGCuO film coating were considered: the formation of the BCGCuO electrolyte film without (1) and with a protective BaCeO3 (BCO) film (2) on the LNO electrode substrate and the formation of the BCGCuO electrolyte film on a modified La1.7Ba0.3NiO4+δ (LBNO) cathode substrate (3). After the cyclic EPD in six stages, the resulting BCGCuO film (6 μm) (1) on the LNO substrate was completely dense, but the scanning electron microscope (SEM) analysis revealed the absence of barium in the film caused by its intensive diffusion into the substrate and evaporation during the sintering. The BCO layer prevented the barium loss in the BCGCuO film (2); however, the protective film possessed a porous island structure, which resulted in the deterioration of the film's conductivity. The use of the modified LBNO cathode also effectively prevented the loss of barium in the BCGCuO film (3). A BCGCuO film whose conductivity behavior most closely resembled that of the compacts was obtained by using this method which has strong potential for practical applications in solid oxide fuel cell (SOFC) technology. © 2019 by the authors.Government Council on Grants, Russian FederationFunding: This research was funded by the Government of the Russian Federation (Agreement 02.A03.21.0006, Act 211)
Similar works
Full text
Open in the Core reader
Download PDF
Available Versions
Institutional repository of Ural Federal University named after the first President of Russia B.N.Yeltsin