Društvo za ispitivanje i istraživanje i konstrukcija Srbije, Beograd
Abstract
Reinforcement corrosion due to carbonation is one of the main deterioration mechanisms of reinforced concrete structures. The key parameter in the model of carbonation applied in service life design methodology is the carbonation resistance of concrete. This property of the material is tested on accelerated tests, which consider exposure to relatively high concentration of CO2, measurement of the carbonation depth and it’s correlation with the designed concrete cover. The paper presents the results of accelerated carbonates tests conducted in conditions of CO2 concentration of 1%, 2% and 4%, on the concrete samples made with natural and recycled aggregates. Test results show the effect of CO2 concentration change on the kinetics of the carbonation process.Korozija armature usled karbonatizacije je jedan od osnovnih mehanizama oštećenja armiranobetonskih konstrukcija. U aktuelnim proračunskim modelima karbonatizacije, na kojima je zasnovana metodologija projektovanja prema upotrebnom veku konstrukcije, ključni parametar je karbonatizaciona otpornost betona. Ovo svojstvo materijala ispituje se ubrzanim testovima koji podrazumevaju izloženost relativno visokim koncentracijeama CO2, a zatim se dubina tako karbonatizovane zone dovodi u vezu sa projektovanom dubinom u uslovima realne izloženosti. U radu su prikazani rezultati ubrzanih karbonatizocionih testova sprovedenih u uslovima koncentracije CO2 od 1%, 2% i 4% na betonima spravljenim sa prirodnim i recikliranim agregatom. Rezultati ispitivanja ukazuju na efekte promene koncentracije CO2 na kinetiku procesa karbonatizacije