Forming limit curves (FLC) of deep drawing steel sheets have been determined experimentally and calculated on the base of the material tensile properties following the Hill, Swift, Marciniak-Kuczyński and Sing-Rao methods. Only the FLC modeled from a singly linear forming limit stress curve exhibits good consistence with experimental curve. It was established that a linearized limit stress locus describes adequately the actual localized neck conditions for the material chosen in this study. The quantitative X-ray microanalysis of the Fe contents in the sheet surface layer composition was used to determine cracking limit curve (CLC) of electro-galvanized steel sheet. The change in zinc layer (and base sheet metal) thickness was used as a criteria in calculation of the CLC.Krivulje graničnih deformacija (KGD) pri dubokom izvlačenju čeličnih limova su ustrojene eksperimentalno a također su proračunate na temelju svojstava čvrstoće materijala po metodama Hill, Swift, Marciniak-Kuczyński i Sing-Rao. Dobra podudarnost s eksperimentalnom KGD daje jedino KGD dobivena na temelju modela krivulje graničnih deformacija. Utvrđeno je da linearizirano granično naprezanje dovoljno točno opisuje uvjete lokalnog progiba za materijale rabljene u ovom radu. Za određivanje krivulje graničnog prijeloma (KGP) na površini elektrogalvaniziranih cinkom čeličnih limova rabljena je kvantitativna X-zrakama mikroanaliza sadržaja Fe. Izmjene debljine sloja cinka (i osnovnog metala lima) je rabljena kao krivulja za proračun KGP