The aim of this study is the investigation of micro-structural behaviour of a Mat. No. 1.2379 (EN-X160CrMoV121; AISI D2) cold work tool steel after remelting with a precise pulsed Nd:YAG laser. The investigated steel is one of the most hard to weld tool steels, due to large amount of alloying elements. The analysis was done on single spots remelted with specific laser pulse shape and parameters, assuring crack-less solidification. Re-solidifi ed areas were investigated with microscopy, hardness measurements, X-ray spectroscopy and diffraction method. Laser treatment causes rapid solidification leading into a formation of a fine dendritic microstructures containing high amount of retained austenite causing a significant decrease of hardness.Namjena ove studije je ispitivanje ponašanja mikro strukture alatnoga čelika za rad na hladno Mat. No.1.2379 (ENX160CrMoV121; AISI D2) po pretaljivanju s preciznim pulsiranim Nd:YAG laserom. Zbog velike količine legirnih elemenata istraživani materijal spada u grupu vrlo teško zavarljivih alatnih čelika. Analiza je provedena na pojedinim pretaljenim točkama korištenjem specifi čnog oblika i parametara laserskog impulsa koji osiguravaju skrućivanje bez pukotina. Pretaljena područja su ispitivana mikroskopom, mjerenjem mikro tvrdoće, rendgenskom spektroskopijom i defrakcijskom metodom. Tretman laserom uzrokvao je brzo skrućivanje koja dovodi do formiranja fi ne dendritičke strukture s velikim udjelom zaostalog austenita što uzrokuje bitno smanjivanje tvrdoće