The Ag-In-Sb ternary system presents one of the possible lead-free solder candidates. Therefore, the results of thermodynamic study of the alloys in the Ag-In-Sb alloys, obtained using general solution model, are presented in the paper. Obtained data for partial and integral molar thermodynamic quantities in the temperature interval 1000-1200K are given. The characterization of these alloys have been done using DTA, XRD, SEM and optic microscopy, which enabled the construction of the Ag-In-Sb phase diagram in the concentration range up to 60 wt. % Ag

B. Marjanović

D. Manasijević

D. Živković

M. Cocić

Ž. Kamberović

Hrčak - Portal of scientific journals of Croatia

METALURGIJA 46 (2007) 3, 151-156 151D. ???????? et al.: ?????????????? ??????????????????????????????????? ??????????????Received - Primljeno: 2006-04-11??????????????????????????????????????????????????????????????????????????????????? ? ??? ????????????????????????????????????????????????????????????????=111??? ? ????? ???? ??????? ? ???? ? ?????? ?? ? ??? ?? ?????????????? ?? ???????????? ?? ??????????? ????????????????? ?????-???????? ????????? ???? ??????? ?? ??????????? ?????????? ????????????????????????? ????????????? ????????? ????????????????? ?? ??????????????????????????????????THERMODYNAMIC AND STRUCTURAL INVESTIGATION OF THE Ag-In-Sb SYSTEMINTRODUCTION?????????? ??????????????????????????????????????? ????????????????? ??? ?????????? ???????? ???? ???????????? ??????????????????????????????????????????????????????????????????????????????????????????????????????????????????????-??????????????????????????????????????????????????????????????????????????????????????????????????????????????????????? ???????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????? ?? ???????? ???????????????????? ??? ?????? ????? ????????????????????????? ?????????? ?????????????????? ??????????????? ???? ????????? ????????????? ???????????? ????????????????????????????????? ???????????????? ???? ????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????? ?????????????????????????????????????????????????????????????????? ???????????????????????????????????????????????????????????????????????????????????-??????????????????????????????????????????????????????????????????????????????????????????????? ??????????????????????????????? ?????????????????????????????????????????????????????????????????????????????????????????????????? ????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????? ?????????????????????? ???????????????? ???????????????????????????????????????????????????????????????????????????????????????? ??????????????? ?????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????? ??? ????????????????? ???? ????????????? ??????? ?????????????????????????????????????? ?? ????? ?????????????????????????????????????????????? ???????????????????????????????? ???????????????????????????????????????????????? ??? ?????????????? ????????? ??? ??????????????? ????????????????? ????????????? ??? ???? ??????? ?????????? ??????????????????????????????????? ???????????? ??????????????????????????????????????????????????????????????????????????????????????????? ????????????????EXPERIMENTAL????????????? ??????????????? ?????????? ??? ????? ????????????????????????????????????????????????The Ag-In-Sb ternary system presents one of the possible lead-free solder candidates. Therefore, the results of thermodynamic study of the alloys in the Ag-In-Sb alloys, obtained using general solution model, are presented in the paper. Obtained data for partial and integral molar thermodynamic quantities in the temperature interval 1000-1200K are given. The characterization of these alloys have been done using DTA, XRD, SEM and optic microscopy, which enabled the construction of the Ag-In-Sb phase diagram in the concentration range up to 60 wt. % Ag.Key words: thermodynamics, lead-free solder alloys, Ag-In-Sb systemTermodinamska i strukturna ispitivanja Ag-In-Sb sustava. Ag-In-Sb ternarni sustav predstavlja potencijalni novi bezolovni materijal za lemljenje. U ovom radu su prikazani rezultati termodinamskog ispitivanja presijeka ???????????????????????????? ?????????????????????????????????????????????????????????????????????????????-???????????????????????????????????????????????????????????????????????????????????????????????? ???????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????? ??????????????????? termodinamika, bezolovni materijali za lemljenje, Ag-In-Sb sustavMETALURGIJA 46 (2007) 3, 151-156152D. ???????? et al.: ?????????????? ??????????????????????????????????? ????????????????????????????????????????????????????? ??????-???????????????????????????????????????????? ????????????????????????????????? ?2?3???????????????????????????????????????? ?????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????? ????????????????????????? ???????-????? ??????????? ??????????? ?????????? ??????????????????????? ???? ?????????????????????????????3 + 100 ml H2?2 + 100 ml H2???????????????????? 2?2? ?????????????????????????????????????????????????????????????????????????????????? ???????????????????????????????????????? ??????????????????????????????????????????? ????????????? ?????????????????????? ?????????????????????????????????????????????????????????????????????????????????????THEORETICAL FUNDAMENTALS ???????????? ???????????????????? ????????????? ???????????? ?????????????? ??????????? ?????? ??? ?????? ???-?????????????????????????????????????????????? ???????????????????????????????????????????????????????????? ??????????????????????????? ? ? ?20 1 21 2 12 12 1 2 12 1 2EG x x A A x x A x x? ?? ? ? ? ? ?? ?? ?? ? ? ?20 1 22 3 23 23 2 3 23 2 3x x A A x x A x x? ?? ? ? ? ?? ?? ?? ? ? ?20 1 23 1 31 31 3 1 31 3 1 1 2 3,x x A A x x A x x fx x x? ?? ? ? ? ? ?? ?? ?where 0 1 2,  ,  ij ij ijA A A ???????????????? ???????????????????ij”???????????????????????????????????????????????????????????????????????????????????????????????????????????? ?0 1Eij i j ij ij i jG X X A A X X?? ? ? ???? ? ? ?22 ... ,nnij i j ij i jA X X A X X ?? ? ? ? ? ??where Xi  and Xj?????????????? ???????????????????????????i”?????j??????ij????????????????? ????????????f????????????????????????????????????????????????????? ? ? ? ? ?? ?2 112 12 12 3 1 2 122 1 2 1 2f A x x x A? ?? ?? ? ? ? ? ?? ?? ? ? ? ? ?? ?2 123 23 23 1 2 3 232 1 2 1 2A x x x A? ?? ?? ? ? ? ?? ?? ? ? ? ? ?? ?2 131 31 31 2 3 1 312 1 2 1 2 ,A x x x A? ?? ?? ? ? ? ?? ? (3)where ?ij???????????????????????????????????????????i called ?????????????????????????????,iiji j??? ??? (4)where? ?12I 12 13 10d ,XiE EXiG G X???? ? ???? ?12II 21 23 20d ,XiE EXiG G X???? ? ???? ?12III 31 32 30dXiE EXiG G X???? ? ???(5)and1(12) 1 3 12 ,X x x ?? ?2(23) 2 1 23,X x x ?? ?3(31) 3 2 31.X x x ?? ? (6)?????????????????????????GE and EijG? ??????????????????????????? ???????????? ???????????????????????????????????????????????????????????? ?????x1, x2, x3??????????????????? ??????????????????????????????????????????????????????????RESULTS AND DISCUSSION???? ????????????????????????????????????????????????????????????????????????????????????????????????????????????????-???????????? ???????????????? ?????????? ???? ????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????? ??????????????????????????????????????? ??????? ?????????? ,EijG? ? ???? ???? ??????????????????????????? ????????????????????????????????? ?????(1)(2)METALURGIJA 46 (2007) 3, 151-156 153D. ???????? et al.: ?????????????? ??????????????????????????????????? ?????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????-???????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????? ????????????????????????????????????? ????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????-??????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????? ????? ????????????????????????????? ??????????????? ?????????????????????????????????????????????????????? ?????????????????????????????????????????????????????????????????????????????????????????????3 2Ag Ag????? ??????EG x x? ? ?Ag?????? ??????? ?? ??????x T? ? ?3 2Ag Ag????? ??????EG x x? ? ?Ag?????? ??????? ?? ??????x T? ? ?3 2Ag Ag9745,3 509,17EG x x? ? ?Ag???? ??????? ?? ??????x T? ? ??????????????????????????????????????????????????????-??????????????????????????????????????????????????????????????????????????????????????? ?????? ???????????????????????????????? ??? ???? ??????????? ?????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????? ??????????????????????????????????????????????????? ??????????? ???????????? ???????? ???????????? ????? ????? ???? ?????? ??????????? ?????????? ??? ???????????????????????????? ?????????????????????????????????????????????????????????????????????????????????????????????????????????? ??????????????????????????????????????? ???????????????????????????????????????????????????????????????????????????????????????METALURGIJA 46 (2007) 3, 151-156154D. ???????? et al.: ?????????????? ??????????????????????????????????? ?????????????????????????????????????????????????????????????????????????????????? ??? ?????????????????????????????????????????????xAg?????????????????????????????????????????????????????????????? ???????????????????????????? ????????? ???-????????????????????????????????????????????????????????????????????????????????????????????????????????????? ?? ??????????????????????????? ??????????????????????????????? ??????????????????????????? ???? ???????????????????????????????????????? ?????? ??????-???????????????????????????????????????????????????????????????????? ?????????? ??? ???? ???????? ?????????? ???????????????????????????????????????????????????????????????????????????????????????????????? ?????????????????????????METALURGIJA 46 (2007) 3, 151-156 155D. ???????? et al.: ?????????????? ??????????????????????????????????? ??????????????????????????????????????????????????????????????????????????????????????????????????2???????????????????????????????????? ????? ?????? ???????????? ????????????????????????????????????????????????????????????????????????????????????????? ??? ??????????? ??????? ??????????????? ???????????????????????????? ????????????? ????? ???????????????????????????????????????????????????????????????????????? ????????????????????????????????????? ?????? ?????????????????????????????????????????????? ????????????????????????????? ??????????????????? ????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????? ?????????????-?????????? ??? ???? ?????????????????????????????????? ???????????????? ????????????? ????? ???????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????? ?????????????? ????????????????????????????????????????????????????????????????????? ???????????????? ?????????? ????????? ?????? ???????????????????????????????????????????????????????? ???????????????CONCLUSIONS???????????????????????????????????????????????????????????????????????????????????????????????? ????????????????????????????????????????????????????????????????????????made:???????????????????????????????????????????????????????????????????????? ?????? ???????????????????????????? ?-????????????????????????????????????????????????????????????????????? ???????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????METALURGIJA 46 (2007) 3, 151-156156D. ???????? et al.: ?????????????? ??????????????????????????????????? ??????????????REFERENCES? ???? ??? ?? ?????? ???????????????????????????????????????????????????????????????????????????????????????????????????? ????????????????????? ???? ????????????????????????????????????????????? ???? ??? ?? ?????? ?? ?? ???? ?? ?? ?????? ?? ?? ????????? ?? ???????????????????????????????????????????????????? ???? ???????????????????????????????????????? ???? ?????? ?????????????? ?? ???????? ??????????????????? ???????????????????? ??????? ??????? ??????????????????????????????????? ???? ??? ???????????????? ?????????????????? ??????????????? ???????????????????????????????????? ???? ????????????????????????????? ??????????? ???????????? ??????????????????????????????????????? ?????????????????????????????????????????????????????????????????????????????? ???? ?????????????????????????????????????? ??????????????????????????? ???? ???????????????????????????????????????????????????????????????????????????????????????????????? ???????????????? ??????????????? ??????????????????????????????????????????????????????? ???? ??????????? ??????????????????????????????? ???? ??????????????? ???????????????????????????? ???? ?????? ??????? ???? ??????????????????????Acknowledgment????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????? ????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????? ???????????????????????-?????????????????????????????????????????????????????????????????? ??? ???? ????????????? ???????? ??? ??????????????????????????????????????????????????????????????? ?????????????????????????????????????????????????????????????????? ????????????????????xAg=0.622 ??????????????????????????????????????????????????????????? ?????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????? ????????????????????????????????????????????????? ???? ???????????,???????????????????????????????? ???? ??????????????????????????????? ????????????????????????? ???? ?????? ??????? ?????????????? ????????????????? ???? ?????? ??????? ???? ???????????????????????? ???? ?????????????????????????? ?????????????????????? ???? ??? ??? ?? ?????????? ???????? ????????????????????????????????? ???? ????????????????????????????? ????????????????????????? ???? ??? ?? ??????????????? ?? ??????????????????????? ?????????????????149.? ???? ??? ?????? ?? ?????????????????? ??????????????? ??????? ?????????????????????????????????????????????? ??????????????????????? ???? ????????????????????????????????? ??????????????????????? ???? ??? ??????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????????? ??????????????????????????????????? ???? ???????????????????????????????????????????????????????????????????????????????? ?????????????????????????????? ???? ??? ????????? ?? ?? ??????????? ?? ?? ???? ?? ????????????????????1276.? ???? ??? ?? ?????????? ???????????????????????? ?????????????? 139 ????????????? ???? ??????????? ?????????????????????????????????????? 70 (1966), 207.? ???? ??????????????????????????????????? ?????????????????????????????????????????????7 (1970), 51.? ???? ?????????????? ??????????? ?????????64 (1973), 496.? ???? ?????????????????????????????????????????????????? ???? ??? ????? ?? ??????????? ?? ????????????????????? ???????????????1175.? ???? ??????????????????????????????????????????????? ????????????????(1996), 155.? ???? ????????????????????????????????????????????????????????????? ???? ????????????????????????????????????.? ???? ???????????? ???????????????? ?????????????????????????????? ???? ???????????????????????????????????????????????????????????? ???? ?????????????????????????????????????????????????

Thermodynamic and Structural Investigation of the Ag-In-Sb System

HRČAK - Portal of Croatian Scientific and Professional Journals

METALURGIJA 46 (2007) 3, 151-156 151D.  et al.: Received - Primljeno: 2006-04-11=111-THERMODYNAMIC AND STRUCTURAL INVESTIGATION OF THE Ag-In-Sb SYSTEMINTRODUCTION--EXPERIMENTALThe Ag-In-Sb ternary system presents one of the possible lead-free solder candidates. Therefore, the results of thermodynamic study of the alloys in the Ag-In-Sb alloys, obtained using general solution model, are presented in the paper. Obtained data for partial and integral molar thermodynamic quantities in the temperature interval 1000-1200K are given. The characterization of these alloys have been done using DTA, XRD, SEM and optic microscopy, which enabled the construction of the Ag-In-Sb phase diagram in the concentration range up to 60 wt. % Ag.Key words: thermodynamics, lead-free solder alloys, Ag-In-Sb systemTermodinamska i strukturna ispitivanja Ag-In-Sb sustava. Ag-In-Sb ternarni sustav predstavlja potencijalni novi bezolovni materijal za lemljenje. U ovom radu su prikazani rezultati termodinamskog ispitivanja presijeka - termodinamika, bezolovni materijali za lemljenje, Ag-In-Sb sustavMETALURGIJA 46 (2007) 3, 151-156152D.  et al.: -2 3-3 + 100 ml H2 2 + 100 ml H2 2 2THEORETICAL FUNDAMENTALS -20 1 21 2 12 12 1 2 12 1 2EG x x A A x x A x x20 1 22 3 23 23 2 3 23 2 3x x A A x x A x x20 1 23 1 31 31 3 1 31 3 1 1 2 3,x x A A x x A x x fx x xwhere 0 1 2,  ,  ij ij ijA A A ij”0 1Eij i j ij ij i jG X X A A X X22 ... ,nnij i j ij i jA X X A X Xwhere Xi  and Xj i”j ij f2 112 12 12 3 1 2 122 1 2 1 2f A x x x A2 123 23 23 1 2 3 232 1 2 1 2A x x x A2 131 31 31 2 3 1 312 1 2 1 2 ,A x x x A (3)where ij i called ,iiji j (4)where12I 12 13 10d ,XiE EXiG G X12II 21 23 20d ,XiE EXiG G X12III 31 32 30dXiE EXiG G X(5)and1(12) 1 3 12 ,X x x2(23) 2 1 23,X x x3(31) 3 2 31.X x x (6)GE and EijGx1, x2, x3RESULTS AND DISCUSSION-,EijG(1)(2)METALURGIJA 46 (2007) 3, 151-156 153D.  et al.: --3 2Ag AgEG x xAgx T3 2Ag AgEG x xAgx T3 2Ag Ag9745,3 509,17EG x xAgx T-METALURGIJA 46 (2007) 3, 151-156154D.  et al.: xAg--METALURGIJA 46 (2007) 3, 151-156 155D.  et al.: 2-CONCLUSIONSmade:-METALURGIJA 46 (2007) 3, 151-156156D.  et al.: REFERENCESAcknowledgment-xAg=0.622 ,149.1276. 139  70 (1966), 207.7 (1970), 51.64 (1973), 496.1175.(1996), 155..

English

The Ag-In-Sb ternary system presents one of the possible lead-free solder candidates. Therefore, the results of thermodynamic study of the alloys in the Ag-In-Sb alloys, obtained using general solution mode!, are presented in the paper. Obtained data for partial and integral molar thermodynamic quantities in the temperature interval 1000-1200K are given. The characterization of these alloys have been done using DTA, XRD, SEM and optic microscopy, which enabled the construction of the Ag-In-Sb phase diagram in the concentration range up to 60 wt. % Ag

Živković, Dragana

Manasijević, Dragan

Kamberović, Željko

Cocić, Mira

Marjanović, B.

TechnoRep

Thermodynamic and structural investigation of the Ag-In-Sb system

Živković, D.

Manasijević, D.

Kamberović, Ž.

Cocić, M.

Directory of Open Access Journals

http://doaj.org/search?source=%7B%22query%22%3A%7B%22bool%22%3A%7B%22must%22%3A%5B%7B%22term%22%3A%7B%22id%22%3A%22b7673663f11d4ac59038402e9deb2508%22%7D%7D%5D%7D%7D%7D

Thermodynamic and Structural Investigation of the Ag-In-Sb System

Abstract

Similar works

Full text

Available Versions

Hrčak - Portal of scientific journals of Croatia

HRČAK - Portal of Croatian Scientific and Professional Journals

TechnoRep

Directory of Open Access Journals