The scientific and industrial interest devoted to polymer/layered silicate
nanocomposites due to their outstanding properties and novel applications resulted
in numerous studies in the last decade. They cover mostly thermoplastic- and
thermoset-based systems. Recently, studies in rubber/layered silicate
nanocomposites were started, as well. It was presented how complex maybe the
nanocomposite formation for the related systems. Therefore the rules governing their
structure-property relationships have to be clarified. In this Thesis, the related
aspects were addressed.
For the investigations several ethylene propylene diene rubbers (EPDM) of polar and
non-polar origin were selected, as well as, the more polar hydrogenated acrylonitrile
butadiene rubber (HNBR). The polarity was found to be beneficial on the
nanocomposite formation as it assisted to the intercalation of the polymer chains
within the clay galleries. This favored the development of exfoliated structures.
Finding an appropriate processing procedure, i.e. compounding in a kneader instead
of on an open mill, the mechanical performance of the nanocomposites was
significantly improved. The complexity of the nanocomposite formation in
rubber/organoclay system was demonstrated. The deintercalation of the organoclay
observed, was traced to the vulcanization system used. It was evidenced by an
indirect way that during sulfur curing, the primary amine clay intercalant leaves the
silicate surface and migrates in the rubber matrix. This was explained by its
participation in the sulfur-rich Zn-complexes created. Thus, by using quaternary
amine clay intercalants (as it was presented for EPDM or HNBR compounds) the
deintercalation was eliminated. The organoclay intercalation/deintercalation detected
for the primary amine clay intercalants, were controlled by means of peroxide curing
(as it was presented for HNBR compounds), where the vulcanization mechanism
differs from that of the sulfur curing.
The current analysis showed that by selecting the appropriate organoclay type the
properties of the nanocomposites can be tailored. This occurs via generating different
nanostructures (i.e. exfoliated, intercalated or deintercalated). In all cases, the
rubber/organoclay nanocomposites exhibited better performance than vulcanizates
with traditional fillers, like silica or unmodified (pristine) layered silicates.The mechanical and gas permeation behavior of the respective nanocomposites
were modelled. It was shown that models (e.g. Guth’s or Nielsen’s equations)
developed for “traditional” vulcanizates can be used when specific aspects are taken
into consideration. These involve characteristics related to the platy structure of the
silicates, i.e. their aspect ratio after compounding (appearance of platelet stacks), or
their orientation in the rubber matrix (order parameter)