Wulff, Anders Christian

Afhandlingen præsenterer et forskningsarbejde med det formål at undersøge vigtige problemstillinger i forbindelse med fremstilling af metalbånd med en stærk krystallografisk terningtekstur. Disse bånd anvendes til superledende coated conductors og forsøgene er udført med valsede og varmebehandlede (rekrystalliserede) Ni-5at.%W bånd, der er påført et keramisk Gd2Zr2O7 bufferlag. Overfladeruhed og krystallografisk tekstur er karakteriseret for prøver i henholdsvis kolddeformeret og rekrystalliseret tilstand og indflydelsen af poleringsbetingelser er kortlagt. En detaljeret undersøgelse af overfladen har omfattet indflydelsen af korngrænse-fordybninger, der opstår under varmebehandlingen. Det blev endvidere konstateret at graden af terningtekstur, indenfor en 5° afvigelse fra den ideelle krystallografiske terningorientering, var særdeles afhængig af overfladeruheden efter valsning.Mikrostruktur, krystallografisk tekstur og topografi blev undersøgt, i et Ni-5at.%W bånd med en stærk terningtekstur, før og efter en varmebehandling (henholdsvis tilstand A1 og A2), der simulerede en varmebehandling af et bufferlag. Mikrostrukturen i tilstand A1 var karakteriseret ved et højt antal lavvinkel korngrænser og følgende begrænset andel af korngrænser med højere misorienteringsvinkler, inklusiv Σ3 korngrænser. En klar sammenhæng blev observeret mellem dybden af korngrænse-fordybninger og typen af korngrænse. De mindste fordybninger blev observeret ved kohærente tvillingkorngrænser og lavvinkel korngrænser, mens store korngrænsefordybninger blev registreret ved højvinkel, inkohærente samt ikke-tvilling Σ3 korngrænser. En lignende tendens blev observeret mellem den gennemsnitlige inklinationsvinkel ved korngrænsevæggene i fordybningerne og korngrænse-typen. Tilstand A2 var karakteriseret ved en lidt grovere mikrostruktur samt en skarpere terning tekstur og højere andel af lavvinkel korngrænser. Den gennemsnitlige dybde af fordybninger ved højvinkel korngrænser steg markant, undtagen for kohærente tvilling-korngrænser. Store forskelle blev også observeret mellem (i) fordybninger af korngrænser karakteriseret som stationære, der typisk udviklede dybere grøfter, og (ii) fordybninger ved grænser karakteriseret som migrerende var betydelig reduceret. Migrerende korngrænser efterlod fordybninger i overfladen af materialet når de flyttede til en ny position, hvor de dannede nye korngrænse-fordybninger. Der blev ikke observeret nogen signifikant ændring i den gennemsnitlige overfladeruhed på trods af disse lokale topografiske forskelle. Mikrostruktur, krystallografisk tekstur, hårdhed samt magnetiske egenskaber blev studeret i en ny type Ni-Cu-W metalbånd. En legering med 5 at.% Cu i Ni-5at.%W viste en stærkt reduceret Curie temperatur og mætnings-masse-magnetisering, uden nogen væsentlige ændringer i mikrostrukturog tekstur sammenlignet med Ni-5at.%W. Kun en lille reduktion blev observeret i hårdheden som funktion af kobberindholdet. Et forøget kobberindhold (10-15 at.%) resulterede i en fortsat reduktion af Curie temperaturen og af mætnings-masse-magnetiseringen, men også en stærkt forringet terningtekstur, samt en forøget andel af højvinkel korngrænser. Konklusionen pa denne undersøgelse er at stærkt teksturerede Ni-5Cu-5W metalbånd er et muligt kandidatmateriale til brug i fremtidige superledende coated conductors.This thesis presents the results of a study aimed at investigating important fabrication aspects of reel-to-reel processing of metal substrates for coated conductors and identifying a new substratecandidate material with improved magnetic properties. The eect of mechanical polishing on surface roughness and texture in Ni-5at.%W tapes in the cold-rolled condition was studied as a function of polishing grade. The surface roughness of the tape in the polished and annealed condition, and after subsequent coating with a Gd2Zr2O7 buer layer was investigated taking grain boundaries into account. It was observed that the initial mean surface roughness decreased after annealing except after very ne polishing. Additionally, the roughness of the buer layers were found to increase slightly for the ne polished substrates. Grain boundary grooving was observed to impose a lower limit for the mean surface roughness. Fractions of cube texture within deviations of 5o from the ideal cube orientation, in the annealed substrates, were found to be very sensitive to the surface roughness before annealing. Microstructure, texture and topography were studied in a strongly cube-textured Ni-5at.%W substrate before and after an additional annealing (condition A1 and A2, respectively) simulating a buer layer crystallisation heat treatment. Condition A1 was characterised by a high fraction of cube texture, a high fraction of low angle grain boundaries and a low fraction of 3 boundaries. A strong correlation was observed between the grain boundary groove depth and boundary type. Coherent twin boundaries and low angle grain boundaries were characterised by the smallest average groove depth while signicantly deeper grooves were observed at other boundary types. A similar correlation was observed between the inclination angle at groove walls and the boundary type. The microstructure was slightly coarser in condition A2 and it was accompanied by a cube texture strengthening and an increase in the fraction of low angle grain boundaries. The average depth of grain boundary grooves increased considerably at boundaries characterised by large misorientation angles, except for coherent twin boundaries. Signicant changes were observed between the groove depth at stationary boundaries which generally increased in depth and the grooves at migrating boundaries which typically became shallower compared to condition A1. Furthermore, migrating boundaries were found to abandon grooves and generate grooves at new positions. Despite the observed changes in the extent of grain boundary grooving, the mean surface roughness was almost identical before and after the additional annealing. Microstructure, texture, hardness and magnetic properties have been studied in a series of new Ni-Cu-W substrates. Adding 5 at.% copper to Ni-5at.%W was observed to substantially decrease the Curie temperature and the saturation mass magnetisation without signicantly modifying the microstructure and texture compared with Ni-5at.%W. The hardness of this Ni- 5Cu-5W substrate was only slightly less than the hardness of the reference Ni-5at.%W substrate. Further increasing the Cu-content was observed to result in a great decrease in the Curie temperature and saturation mass magnetisation values, but also a signicant decrease in the fraction of cube texture and the fraction of low angle grain boundaries. Finally, a Ni-5Cu-5W substrate may be a good candidate material as a substrate in future coated conductors

Online Research Database In Technology

Cube-textured metal substrates for reel-to-reel processing of coated conductors

http://orbit.dtu.dk/ws/files/51481665/Thesis_Wulff.pdf

Cube-textured metal substrates for reel-to-reel processing of coated conductors

Abstract

Similar works

Full text

Available Versions

Online Research Database In Technology