                       General rights Copyright and moral rights for the publications made accessible in the public portal are retained by the authors and/or other copyright owners and it is a condition of accessing publications that users recognise and abide by the legal requirements associated with these rights.  • Users may download and print one copy of any publication from the public portal for the purpose of private study or research. • You may not further distribute the material or use it for any profit-making activity or commercial gain • You may freely distribute the URL identifying the publication in the public portal   If you believe that this document breaches copyright please contact us providing details, and we will remove access to the work immediately and investigate your claim.     Downloaded from orbit.dtu.dk on: Dec 18, 2017Stamp deformation during nanopattern thermal imprinting on a double-curvedsubstrateCech, Jiri; Christiansen, Alexander Bruun; Taboryski, Rafael J.Publication date:2011Document VersionPublisher's PDF, also known as Version of recordLink back to DTU OrbitCitation (APA):Cech, J., Christiansen, A. B., & Taboryski, R. J. (2011). Stamp deformation during nanopattern thermalimprinting on a double-curved substrate. Poster session presented at 37th International Conference on Microand Nano Engineering, Berlin, Germany.Stamp deformation during nanopattern thermal imprinting on a double-curved substrateJiri Cecha, Alexander Bruun Christiansena, Rafael Josef TaboryskiaMotivationNanopatterning of double-curved surfaces remains to be great microfabrication challenge, but successful testing and control of such methods would allow various applications such as nanopatterning of injection mold cavities for low cost antireflective treatment of portable electronics optics. Another application is surface wetting control on affordable medical devices. This would require good understanding of stamp deformation, including deformation on high curvature (low radius) surfaces. Cheng[1] created 600 nm pattern on curved surface with 57 mm radius, while an proximately 800 nm patterns was created by capillary force lithography on spherical substrate with 49 mm radius by Zhang[2]  and Choi[3] used soft stamp to imprint 350 nm pattern on substrate with radius as little as 10 mm.    Jiri.Cech@nanotech.dtu.dk +45 61 79 29 00345 Ørsteds Plads, 2800 Kgs. LyngbyDenmarkAcknowledgmentProject is funded by DTU Nanotech, the Danish National Advanced Technology Foundation (HTF), the Copenhagen Graduate School for Nanoscienceand Nanotechnology (C:O:N:T). Surface tools have been manufactured by the Kaleido Technology ApS, polystyrene injection molding was done at InMold BioSystems.ResultsSubmicron patterns were transfered onto PMMA using PDMS stamp and onto PS using Zeonorfoils.References[1] F. S. Cheng, S. Y. Yang, S. C. Nian, and L. A. Wang. Soft mold and gasbag pressure mechanism for patterning submicron patterns onto a large concave substrate. Journal of Vacuum Science & Technology B, 24(4):1724–1727, July-August 2006.[2] D. Zhang, W. Yu, T. Wang, Z. Lu, and Q. Sun. Fabrication of diffractive optical elements on 3-D curved surfaces by capillary force lithography. Optics Express, 18(14):15009–15016, July 2010.[3] W. M. Choi and O. O. Park. The fabrication of submicron patterns on curved substrates using apolydimethylsiloxane film mould. Nanotechnology, 15(12):1767–1770, December 2004.AFM of nanopattern imprinted on spherical polymer substrate surface, average height of structures is 64 nm. Pattern is hexagonal array of pillarsConfocal microscopy reconstructed surface image of spherical PS substrate surface after thermal imprinting with Zeonor COP foil. Pattern is optical grating.Positions of deformation analysis points and deformation of unsupported PS macrostructure.ConclusionUnit cell size have been characterized on stamp and on collected AFM data at deformation analysis points on polymer replica for 2 extreme cases, very thick and very thin PDMS soft stamp.  There are two distinctly different stretching regimes, one for thick stamp and another for thickness comparable with height of curved substrate protrusion. However, results for combination of PS and Zeonor foils are more complex and not yet fully understood, primarily due to deformation of macrostructures and  magnitude  of XY anisotropy observed by AFM as shown.MethodWe used much higher curvatures (radius of 1.0 and 0.5 mm) to facilitate observation of bending and stretching of the employed soft stamps. We tested and compared 2 stamp materials, SilgardPDMS in two thicknesses and Zeonor COP foils 50, 100 and 188 um thick and 2 different polymer substrates, spun coated 350k PMMA and injection molded PS. Imprinted substrates have been characterized using laser scanning confocal microscopy, tapping mode AFM and SEM and pattern period was evaluated in different zones/regions of sample, using special software.

Stamp deformation during nanopattern thermal imprinting on a double-curved substrate

http://orbit.dtu.dk/ws/files/5795849/MNE2011-Cech%5B1%5D.pdf

Stamp deformation during nanopattern thermal imprinting on a double-curved substrate

Abstract

Similar works

Full text

Available Versions

Online Research Database In Technology