Heggested, K.

Holm, J. L.

Sørensen, Ole Toft

Previous studies on the ceria-gadolinia system have mainly been done on oxides rich in ceria. The purpose of the present work is therefore to establish how the conductivity, density and structure depend on the gadolinia content especiallyat high doping levels. Five different compositions were examined: Ce1-x Gdxo2-x/2 with x = 0.1, 0.3, 0.5, 0.7 and 0.9. Oxide powders of these compositions were prepared by homogeneous precipitation of carbonates by hydrolysis of urea followed by calcination in air. Specimens were prepared by pressing and sintering in air at 1550 °C.Conductivity measurements on discs cut from the sintered specimens in the temperature range 400 - 900 °C showed that the oxygen-ion conductivity decreases with increasing gadolinia content with a corresponding increase of the activation enthalpy for oxygen-ion migration. A model describing the variation of the theoretical density in this system is presented. From this model the densities of the sintered specimens was found to be in the range 93-99% TD. Finally X-ray diffraction on the calcined powders showed that fcc single-phase material exists up to about x = 0.4 after which a bcc phase is formed

Online Research Database In Technology

                       General rights Copyright and moral rights for the publications made accessible in the public portal are retained by the authors and/or other copyright owners and it is a condition of accessing publications that users recognise and abide by the legal requirements associated with these rights.  • Users may download and print one copy of any publication from the public portal for the purpose of private study or research. • You may not further distribute the material or use it for any profit-making activity or commercial gain • You may freely distribute the URL identifying the publication in the public portal   If you believe that this document breaches copyright please contact us providing details, and we will remove access to the work immediately and investigate your claim.     Downloaded from orbit.dtu.dk on: Dec 18, 2017Electrical Conductivity, Defect Structure and Density in the Ceria Gadolinia SystemHeggested, K.; Holm, J. L.; Sørensen, Ole ToftPublication date:1985Document VersionPublisher's PDF, also known as Version of recordLink back to DTU OrbitCitation (APA):Heggested, K., Holm, J. L., & Sørensen, O. T. (1985). Electrical Conductivity, Defect Structure and Density inthe Ceria Gadolinia System.  (Risø-M; No. 2478).RISØ-M-2478 ELECTRICAL CONDUCTIVITY, DEFECT STRUCTURE AND DENSITY IN THE CERIA - GADOLINIA SYSTEM X XX K. Heggestad , J.L. Holm and O. Toft Sørensen xPresent address: Laboratoire de l'Electrochimie et Thermodynamique des Materiaux, Universite Paris XII, France XX Technical University, Trondheim, Norway Abstract. Previous studies on the ceria-gadolinia system have mainly been done on oxides rich in ceria. The purpose of the present work is therefore to establish how the conductivity, density and structure depend on the gadolinia content especially at high doping levels. Five different compositions were examined: Ce, Gd 02_ ,_ with x = 0.1, 0.3, 0.5, 0.7 and 0.9. Oxide powders of these compositions were prepared by homogeneous precipitation of carbonates by hydrolysis of urea followed by calcination in air. Specimens were prepared by pressing and sintering in air at 1550 C. Conductivity measurements on discs cut from the sintered specimens in the temperature range 400 - 900 C showed that the oxygen-ion conductivity decreases with increasing gadolinia content with a corresponding increase of the activation enthalpy for oxygen-ion migration. A model describing the variation of the theoretical density in this system is presented. From this model the densities of the sintered specimens was found to be in the range 93-99% TD. (Continued on next page) March 1985 Risø National Laboratory, DK-4000 Roskilde, Denmark Finally X-ray diffraction on the calcined powders showed that fee single-phase material exists up to about x = 0.4 after which a bec phase is formed INIS Descriptors; ACTIVATION ENERGY; CERIUM OXIDES; CRYSTAL DEFECTS; DENSITY; DOPED MATERIALS; GADOLINIUM OXIDES; IONIC CONDUCTIVITY Poster presented at Euchem Conference on Solid State Chemistry and Electrochemistry, Oxford, March 1984 ISBN 87-550-1097-0 ISSN 0418-6435 Risø Repro 1985 CONTENTS Page SUMMARY 5 BACKGROUND 7 THEORY 8 MODEL FOR CALCULATION OF THEORETICAL DENSITY IN THE SYSTEM 10 EXPERIMENTAL 12 HOMOGENEOUS PRECIPITATION 14 RESULTS 17 DISCUSSION 18 CONCLUSIONS 23 - 5 -SUMMARY Gadolinia-doped cer ia i s one of the best oxygen-ion conductors known today. The ionic conduc t iv i t i e s obtained for these oxides a t low dopant c o n c e n t r a t i o n s ( 4 - 8 roole% Gd01<5) are con-s i d e r a b l y higher than t h o s e obta ined for the doped z irconium oxides and they are therefore of i n t e r e s t for low-temperature (500 - 600°C) oxygen sensors , fuel c e l l s and e l e c t r o l y z e r s . The d e f e c t r e s p o n s i b l e for t h e high c o n d u c t i v i t y i n t h e s e o x i d e s i s , as for the doped zirconium ox ides , oxygen vacancies formed by doping w i t h o x i d e s w i t h a l i o v a l e n t c a t i o n s of a lower v a -lence than that of the host ca t ions . In the case of high doping l e v e l s (50% or h i g h e r ) , however, t h e s i t u a t i o n i s r eversed . Here the system can be considered as ceria-doped gadol inia in which the predominant defect i s i n t e r s t i t i a l oxygen. Previous s t u d i e s on t n e s e o x i d e s have mainly been on o x i d e s r i c h in cer ia whereas, to the knowledge of the authors, no systematic s tudies have h i therto been done on oxides with a high gadolinia c o n t e n t . The purpose of the p r e s e n t work i s t h e r e f o r e t o e s -tab l i sh how the conduct iv i ty , dens i ty and structure depend on the gadolinia concentration e s p e c i a l l y at high doping l e v e l s . Five d i f ferent compositions were examined. If the s t o i c h i o -metr i c formula of o x i d e s in t h i s system i s expres sed as Ce^. x G d x°2-x /2 ' t n e compositions covered in the present work corre-spond t o x r 0 . 1 , 0 . 3 , 0 .5 , 0.7 and 0.9 . Powders of doped oxides were prepared by homogeneous prec ip i ta t ion of carbonates by hydrolysis of urea fol lowed by ca lc inat ion in a i r . Specimens were prepared by pressing and s in ter ing in a ir at 1550°C. EDAX measurements showed t h a t a good homogeneity was obta ined by t h i s process. The structure of the specimens was determined by X-ray d i f f r a c t i o n , whereas the e l e c t r i c a l propert ies were de-termined in a ir in the temperature range 400 - 900°C by 2-probe ac-measurements on d i s c s cut from the s intered specimens. F i -n a l l y , the d e n s i t i e s of the s intered specimens were determined by buoyancy measurements , and from a model d e s c r i b i n g the - 6 -variation of the theoretical density in this system the per-centage of the theoretical densities obtained could be deter-mined. The results obtained in this work indicate: (a) that the oxygen-ion conductivity decreases with increasing gadolinia content. The interstitial oxygen formed at higher doping levels thus cannot contribute to the conductivity probably due to geometrical factors; (b) that the activation enthalpy for oxy-gen-ion migration increases with increasing gadolinia content (c) that the process developed for the fabrication of specimens can give sintered densities in the range 93 - 99% TD, and finally (d) that fee single-phase m ^rial exists up to about x = 0.4 after which a bec phase is formed. The monoclinic Gd203 phase could only be detected for x> 0.95. This work is part of Mr. Heggestad's thesis research for his Master degree at the Technical University of Trondheim, Norway. It was presented as a poster at the Euchem Conference on Solid State Chemistry and Electrochemistry, Oxford, March 1984. This poster is reproduced in the present report. BACKGROUND ' ~ The purpose of this work is to develop alternatives to stabilized zirconia as oxygen ion conductors. Ceria has several advantages compared to zirconia: - Recent works show that ceria doped with approximately 5 moleZ gadolinia has a better conductivity then stabilized zirc-onia at temperatures lower than 800°C - Ceria needs less doping than zirconia to achieve optimal conductivity. - Pure ceria possess the fluorite struc-ture and can accommodate large amounts of doping. This is an advantage for the study of defect interactions as a function of doping level. - The electrical properties of compositions with more than 50 moleZ gadolinia have not been fully investigated before. The conductivity drops as the gadolinia con-tent increase towards 50 moleZ. Our aim is to see if this trend continues throughout the system. THEORY It is convenient to divide the system into three parts: -CeQ2doped with GdQls. All compositions up to about 40 moleZ GdOl5 keep the fluorite structure of pure CeOz. The defect reaction is: 2GdOU5-> 2Gd'tM + 30o + VJ Oxygen vacancies are the charge carriers. -GdOls doped with Ce02. It is here reported (see below), that com-positions with more than 75 moleZ Gd01 have the cubic gadolinia structure. The defect reaction suggested is: 2Ce09 -> 2Ce' +30+0" Z Gd o i In this case the interstitial oxygen is the charge carrier. -Compositions containing between 40 and 75 moleZ GdOJS consist of two phases; one with 40 moleZ GdO, _, the other with 75 moleZ CdOt .. 1.9 1.5 THEORY - 9 -The electrical conductivity can be expressed by the general equation: (T=A/Texp (åS/k) exp CåH/kT) A, AS and AH will depend on the degree of defect interactions. Table I and II lists the three terms for VQ and 0, respectively. In both tables it is assumed either complete defect association or -dissociation. The defect interaction equation in the two cases is, for V0 and 0i respectively: Table I: Va A (K/dhm en) J i ssoc. def: ez a\ v 0 n0 /2k \ssoc. def: e2 a\ »QN^ /4k AScaV) *Sm AS. ^ ASD AH<«V) AH. AH tfttt, Table II: 0, A (K/ohM CM) lissoc. def: e2a\ vQnQ/8k tssoc. def: ezOovo^cd /J®* AS<«V) AS. AS. +AS„ ^HdV) AH. *HU+*H0 msmigration, D-dissoci at i on. MODEL FOR CALCULATION OF THEORETICAL DENSITY IN THE SYSTEM. The model is based on the general equations d=l. 66020 TA/V ZA: weight sum of all atoms in the unit celL V: volume of unit cell (A3) 1. 66020: converts amu/A3 to g/ccm. This is applied in the two one-phase regions: Reg i on 1: Ce^ _r Gdn Q>,n/? - x-0-0. 4 The term ZA for this region is: I.A-CC1 -x) Ap +xA^ )4+(l -x/4) AD8 Cm Gd o Region 2: Gd^Cey015^/2 . y=0-0. 25 ZA-((l-y)AM +yAu )4+(l+y/3)A06 Region 3: The model assumes a linear increase in the 75 moleZ GdOl5 phase from 0 to 100Z in the two-phase region. The density is: d=dn __ C+dn Jl -C) 0.75 0.40 C is fraction of the 75 moleZ Gd0l5 phase. 1 7.70 7.60 t 7.50 s 7.40 7.30 7.20 REGION 2 Th«or«tical density in tho my•torn, according to tho nod«) presented in this work. 0.0 .1 . 2 . 3 .4 .6 .7 .8 .9 1.0 ML, COMPOSITION. X-> GdOh5 EXPERIMENTAL - 5 compositions were prepared containing 10. 30. 50. 70 and 90 moleZ Gd0lm5 respect-ively. The precipitated powder was cal-cined at 800°C overnight and pressed to pellets at 3tons/cm2 pressure. The pellets were sintered at 1600°C for 1 hour. Three samples were cut of each composition; the lengths being approximately 0, 75. 1.0 and 1,5mm, The samples were cut from the same sintered pellet. Each sample was coated with platinum paste and fired at 900°C, - The frequency dependent impedance was meas-ured using a 1250 Solartron Frequency Re-sponse Analyser, The measurements were all within the frequency range 65kHz-WOmHz. and the temperature range 350-900°C. - The two photos show the sample holder. - 13 -HOMOGENEOUS PRECIPITATION This method is based on the hydrolysis of urea, which provide carbonate ions for the precipitation of the metal carbonates. The hydrolysis can be expressed by the following equation: H2NC0NH2 + 2H20 -> 2NH\ + CO\~ The advantage is that the precipitation takes place simultaneously in the whole reaction volume. This is because the hydrolysis does not occur at room temperature, but requires heating. This means that the urea and the metal nitrates may be dissolved together, and then heated. Precipitation starts when the solution reaches the boiling point, at approximately 103°C. In this work the precipitation time was 6hrs, and the yield was between 93 and 97Z of the theoretical. - 15 -STRUCTURE OF (Ce^xGdx)Oz-^ SOLID SOLUTIONS. X-ray analysis at room temperature showed: 0=x 0<x<0. 4 0. 4<x<0. 75 0. 75<x<0. 95 0. 95<x<l x=i fee fee, single phase. fcc+bcc. two phases. bee, single phase. bcc+monocl inic, two phases. monoclinie (high temp. ) , single phase. LATTICE PARAMETER OF (Ce^GdJO^ SOLID SOLUTIONS The lattice parameters were determined by extrapolation using the Nelson & Riley method. The unit cell for the cubic struc-ture of CdOus consists of eight fee cells (cation lattice). Only half of the lattice parameter of this large cell is shown here. •o I o o s. •o a $ *? o g « in i + -o u "o o I 16 -% *** 9 O O i o _ _ o ai a 3 L -« •o æ *» •• * • o i X I - I V ) o ** »>* « . Ul • • " D O . . f O I D x o r» «• g .o t K S) •** >** >s"" i en « •» o <M • - i O > .«-• o o . O "O .O O £ -~ x . o .2 -o f SS «313MVaVd 33U1VH RESULTS - TABLE I. Densities given in percent of theoretical value (ZTO): moleX GdOls: 10 ZTD : 98.6 30 95.8 50 92.9 70 98.4 90 98.5 - TABLE II. Activation enthalpy H for the five compositions. Two values are listed for the specimens containing 10 and 30 moleZ Gd015. These represent stage II and III respectively. H is calculated from the regression line and is valid within ±0.5 in the final digit. moleZ GdOy s 10 30 50 70 90 H (eV) 0. 35 (st. ID 0. 70 (st. Ill) 0. 53 (st. II) 1. 08 (st. Ill) 1.38 1.56 1.68 DISCUSSION The figure shows the Arrhenius-plot for the three samples of the composition with 90 moleZ Gd0ls. The sample length is 0. 75mm(El), 1. 0mm(E2), and 1. 5mm (E3). As can be seen from the figure the conductivity seems to increase with the length, and this effect is observed for all compositions. It is assumed that this is caused by a low degree of porosity in the electrodes, resulting in an inhomogeneous current flow near these. With the approxi-mation that the electrodes of the samples are equal one sees that this effect becomes less important with increasing sample length. The Solartron sees the current inhomogenei ty caused by lack of triple points as an extra resistance in the material. To compensate for this a 'true conductivity' has been calculated. The formula used is: IAT[ - a 2 p r y y / a 2 - v 1 means sample length, pis resistivity and <T't is the true conductivity. The subscript indicates the sample number with increasing length J->3. Changing the subscripts 2 by 3 gives (T't',and the average of these two <T'ts is taken as the true conductivity. - 19 -o • S ~ ?"n.3 3 1 bl bl (M m bl b l i d r r r t w *» • • • < 4* • I O I 4 I • I \ O O O o ri i in ri i o ri i in ri i e V i iflui DISCUSSION The figure shows the Arrhenius-plot for one of the samples of the 10 moleZ GdOh5 compo-sition. This plot contains all the typical features for the 10 and 30 moleZ Gd0lm5 compo-sitions. - The lattice conductivity show two linear regions within this temperature range, the higher called stage II and the lower stage III. Stage II is connected with dissociated defects, hence the activation enthalpy for migration is lower than in stage III, the defect association range. - This plot has a relatively well defined break point between stages II and III. This transition region usually covers a wider temperature interval. - The grain boundaries give a considerable contribution to the total conductivity. As can be seen from the plot it is the domi-nating factor below 700°C for this speci-men. The grain boundary conductivity in-creases from 10 to 30 moleZ GdQlmS. For the other compositions, no grain boundary effect occur. Thus it seems that the lattice- and the grain boundary conductivity, varies in-versely with composition. in - 21 -fe S > * 8.2 S 0 • i "3.5 o 1 - • 3 o < 3 s o - s S • • a fc b "O > c T: o u b>4 i 4 O o o o ri o oi o * o d o « i a IN! I a ri i a V i o ri i ID"! - 22 "O >»o O l O 4» % > •— •** 4* 4> o o z% o- § < o • 4* O 4> •»» ••» 4> 4* . o — g-g 8 - C O ) 4» O O • o • o O 4» « o o • -C O > 4» • LOG CONDUCTIVITY in o •o o A I X f <At>)H 'A3H3N3 N0I1VAU3V CONCLUSIONS - It is confirmed that doped ceria has a ionic conductivity that rivals that of stabilized zirconia at lower temperatures (down to 550-60Q°C). - The ionic conductivity decrease monoton-ously in the range 10 to 90 moleZ Gd01 5. - The correspondance between activation enthalpy and conductivity previously ob-served is verified in this work. It is not possible here to decide the optimal conductivity. - Considering the high densities of the sin-tered pellets, it can be concluded that preparation of powders by homogeneous pre-cipitation is a very attractive method. Risø National Laboratory Risø-M-EH 00 I Title and author(s) Electrical Conductivity, Defect Structure and Density in the Ceria - Gadolinia System K. Heggestad , J.L. Holm and 0. Toft Sørensen Present address: Laboratoire de l'Electaxchimie et Therncdynamique des Materiaux, Universite, Paris XII, France Technical University, Trondheim, Norway Group's own registration number(s) 23 pages tables + illustrations Ms-03-12 Department or group METALLURGY Abstract Previous studies on the ceria-gadolinia system have mainly been done on oxides rich in ceria. The pur-pose of the present work i s therefore to establish how the conductivity, density and structure depend on the gadolinia content especially at high doping levels. Five different compositions were examined: Ce^_x Gdx02_x/9 with x = 0.1, 0.3, 0.5, 0.7 and 0.9. Oxide powders of these compositions were prepared by homo-geneous precipitation of carbonates by hydrolysis of urea followed by calcination in air. Specimens were prepared by pressing and sintering in air at 1550°C. Conductivity measurements on discs cut from the sintered specimens in the temperature range 400 -900°C showed that the oxygen-ion conductivity de-creases with increasing gadolinia content with a corresponding increase of the activation enthalpy for oxygen-ion migration. A model describing the variation of the theoretical density in this system is presented. From this model the densities of the sintered specimens was found to be in the range 93 -99% TD. Finally X-ray diffraction on the calcined powders showed that fee single-phase material exists up to about x - 0.4 after which a bec phase i s formed. Copies to Available on request from Risø Library, Risø National Laboratory (Risø Bibliotek), Forsøgsanlæg Risø), DK-4000 Roskilde, Denmark Telephone: (03) 37 12 12, ext. 2262. Tfclex: 43116 

Electrical Conductivity, Defect Structure and Density in the Ceria Gadolinia System

http://orbit.dtu.dk/ws/files/87946224/ris_m_2478.pdf

Electrical Conductivity, Defect Structure and Density in the Ceria Gadolinia System

Abstract