This paper provides dynamic increase factors (DIF) in compression for two different High Performance Concretes (HPC), 100 MPa and 160 MPa, respectively. In the experimental investigation 2 different Split Hopkinson Pressure Bars are used in order to test over a wide range of strain rates, 100 sec1 to 700 sec-1. The results are compared with the CEB Model Code and the Spilt Hopkinson Pressure Bar technique is briefly de-scribed

Online Research Database In Technology

                       General rights Copyright and moral rights for the publications made accessible in the public portal are retained by the authors and/or other copyright owners and it is a condition of accessing publications that users recognise and abide by the legal requirements associated with these rights.  • Users may download and print one copy of any publication from the public portal for the purpose of private study or research. • You may not further distribute the material or use it for any profit-making activity or commercial gain • You may freely distribute the URL identifying the publication in the public portal   If you believe that this document breaches copyright please contact us providing details, and we will remove access to the work immediately and investigate your claim.     Downloaded from orbit.dtu.dk on: Dec 16, 2017Dynamic Increase Factors for High Performance Concrete in Compression using SplitHopkinson Pressure BarRiisgaard, Benjamin; Ngo, Tuan; Mendis, Priyan; Georgakis, Christos T.; Stang, HenrikPublished in:Fracture Mechanics of Concrete and Concrete StructuresPublication date:2007Document VersionPublisher's PDF, also known as Version of recordLink back to DTU OrbitCitation (APA):Riisgaard, B., Ngo, T., Mendis, P., Georgakis, C., & Stang, H. (2007). Dynamic Increase Factors for HighPerformance Concrete in Compression using Split Hopkinson Pressure Bar. In Fracture Mechanics of Concreteand Concrete Structures1 INTRODUCTION 1.1 Strain rate dependency It is today well-known and accepted that the dy-namic behavior of concrete and concrete like materi-als are strain-rate dependent. (Grote and Park, 2001)  Compared with statically behavior, increases in strength, strain capacity and fracture energy are ob-served when such materials are exposed to impact loads (Lok and Zhao, 2004). The term DIF (Dy-namic Increase Factor) is used to describe the rela-tive strength enhancement.  Figure 1. Various strain rate regions. 1.2 Split Hopkinson Pressure Bar The dynamic strength enhancement for concrete was first observed by Abrams in 1917 (Bischoff and Perry, 1991) and it has been generally accepted that concrete and concrete like materials are strain rate sensitive and the constitutive model of such materi-als under dynamic loading should include strain-rate effects.   Split Hopkinson pressure bar (SHPB) technique has been widely used to measure the dynamic strength enhancement at high strain-rates in the range of 101sec-1 to 103 sec-1.     Figure 2. Typical setup for a SHPB device. 1.3 CEB Model Code The most comprehensive model for predicting the strain rate enhancement of concrete is presented by the CEB Model Code (Comite Euro-International du Beton - Federation Internationale de la Precontrainte, 1990) 1.026/cd cssDIF f fαεε = =    for ε  ≤ 30 s-1           (1)                1/3/cd cssDIF f f εγε = =         for ε  ≥ 30 s-1             (2)  The CEB DIF formulation for concrete has been accepted by most researchers as an accurate repre-sentation of the strength enhancement. The formula-Dynamic Increase Factors for High Performance Concrete in Compression using Split Hopkinson Pressure Bar B. Riisgaard NIRAS Consulting Engineers and Planners, Denmark                                 Centre for Protective Structures and Materials, Technical University of Denmark T. Ngo & P. Mendis Department of Civil and Environmental Engineering, The University of Melbourne C.T. Georgakis & H. Stang Department of Civil Engineering, Technical University of Denmark    ABSTRACT: This paper provides dynamic increase factors (DIF) in compression for two different High Per-formance Concretes (HPC), 100 MPa and 160 MPa, respectively. In the experimental investigation 2 different Split Hopkinson Pressure Bars are used in order to test over a wide range of strain rates, 100 sec1 to 700 sec-1. The results are compared with the CEB Model Code and the Spilt Hopkinson Pressure Bar technique is briefly described.  tion takes a bilinear relation between DIF and log(ε ) with a change in slope at strain-rate of 30 s-1.   (Malvar and Ross, 1998)         2 SPLIT HOPKINSON PRESSURE BAR 2.1 How the SHPB works The principle of a SHPB device is shown in Figure 2. The axial compression impact is caused by the striker bar impinging the incident bar. When this oc-curs, an incident stress pulse is developed. The pulse propagates along the incident bar to the interface be-tween the bar and the specimen. At this point, the pulse is both reflected and transmitted. The reflected wave propagates back along the incident bar and the transmitted wave attenuates in the specimen and into the transmitter bar. Both the incident and the re-flected waves are measured by a strain gauge mounted on the surface at mid-length of the incident bar. Similarly, the transmitted wave is measured by a strain gauge on the surface at mid-length of the transmitter bar. (Li and Meng, 2003)    Figure 3. Interfaces between pressure bars and specimen.  The circular specimens are placed between the two long horizontally aligned pressure bars which serve as the medium for the propagation of elastic pulses as well as for measuring the stress-time history. Fig-ure 3 and Figure 4.   Figure 4. Strain gauge measured wave initiated strains in the SHPB setup. Interfaces at location a and b. Incident, reflected and transmitted, respectively. 2.2 How to read the data A typical output from a SHPB test is shown in Fig-ure 5.      Figure 5. Output from SHPB test.  All three waves, εi(t), εr (t) and εt(t), are measured at the gauge locations, situated at some distance away from the interface. Therefore, an appropriate time-shifting procedure must be undertaken to transfer the strain histories from the gauge locations to the inter-faces Figure 6.    Figure 6. Time-shifted output from SHPB test.  To calculate the specimen stress and the dynamic in-crease factor, Hooke’s law is used to determine the stress of the pressure bars from the measured strain values. Based on (Linholm and Bunshah, 1971) summery of SHPB technique following strain rate, strain and stress history with respect to time, can be calculated, respectively, as   [ ]0( ) ( ) ( ) ( )i r tct t t tLε ε ε ε= − −  (3) [ ]00( ) ( ) ( ) ( )ti r tct t t t dtLε ε ε ε= − −∫  (4) [ ]( ) ( ) ( ) ( )2 i r tsAEt t t tAσ ε ε ε= + +  (5) 2.3 Experimental program For obtaining dynamic increase factors (DIF) for HPC in a wide range of strain rates, two different Split Hopkinson Pressure Bars has been used in this test. A 50 mm SHPB for strain rates in the range of 100 sec-1 to 300 sec-1 and a 22 mm SHPB for strain rates in the range of 600 sec-1 to 700 sec-1. Dimen-sions of specimen are shown in Table 1.   Table 1  Specimen dimension.  Test ID # Specimen diameter, D [mm] Specimen length, L [mm]  L/D Pressure bar diameter [mm] 22 15 10 0.67 22 50 50 50 1.00 50  HPC specimens of two different strengths and 4 different mix proportions have been prepared for this test. The 50mm specimens for the 50mm SHPB were cored out of a 500 x 500 x 150mm slab. The 15 mm specimen for the 22 mm SHPB were cast in cyl-inders. All specimens were cured in water for 28 days at a temperature of 20o C. The mix proportions for all tested HPC are shown in Table 2 and Table 3.  Table 2  Mix proportions for 15mm specimen (kg/m3).  fcs [MPa] Binder* Water Bauxite [1-3mm] Sand [1-3mm] 100 1139 201 433 867 160 1163 193 1300 0 * Densit Binder (ready mix)   Table 3  Mix proportions for 50mm specimen (kg/m3).  fcs [MPa] Cement Silica Fume Silica Flower Aggregate [8mm] 100 500 50 0 1270 160 657 202 202 0  fcs [MPa] Sand [1-3mm] Water Super plasticiser  100 630 135 20  160 965 130 43  3 RESULTS Results from the experimental investigation are pre-sented in Table 4 and Figure 8. DIF indicates the dy-namic increase factors in compression for the tested HPC.    Table 4. Experimental results.  Test ID fcs [MPa] Strain rate [1/sec] fcd [MPa] DIF  01-22 100 710* 336 3.36* 02-22 100 777* 322 3.22* 03-22 100 856* 335 3.35* 04-22 100 722* 340 3.40* 05-22 100 749* 340 3.40*      06-22 160 679* 354 2.36* 07-22 160 674* 338 2.25* 08-22 160 544* 408 2.33* 09-22 160 611* 409 2.34* 10-22 160 516* 433 2.47*      01-50 100 102 184 1.84 02-50 100 145 188 1.88 03-50 100 197 211 2.11 04-50 100 298 240 2.40      05-50 160 81 187 1.17 06-50 160 187 226 1.41 07-50 160 267 241 1.50 * Indicates an average has been used in the plot in Figure 8.  It can be seen that the compressive strength for the 100 MPa HPC increases to 340 MPa at a strain rate of approximately 700 sec-1 and the compressive strength for 160 MPa HPC increases to approxi-mately 400 MPa at a strain rate of approximately 600 sec-1.   Also in Figure 8 the dynamic increase factors from the constitutive CEB Model Code are pre-sented for 100 MPa and 160 MPa, respectively. It can be observed that the CEB Model Code give matching results for the 100 MPa HPC but overes-timates the dynamic strength enhancement for the 160 MPa HPC.   Figure 8. Plot of experimental results of the dynamic increase factors (DIF) compared with dynamic increase factors (DIF) derived from the CEB concrete model. 4 DISCUSSION  The physical mechanisms about the strength en-hancement for concrete have yet not been fully un-derstood. At least two factors, the viscoelastic char-acter of the hardened concrete and the time-dependent micro-crack growth, may contribute to macroscopic strain rate dependent strength en-hancement.   The fact that concrete and concrete like materials are hydrostatic dependent could also cause the dy-namic strength enhancement seen using the SHPB device. In the SHPB test lateral confinement could wrongly be initiated from both the contact surface and the lateral inertia during the impact and because of hydrostatic dependency lead to incorrect dynamic increase factors.   As expected the dynamic strength increases with increase in strain rate. Also, as expected, the 160 MPa HPC is less sensitive to high strain rate loading than the 100 MPa HPC. A literature study revealed that no SHPB tests had earlier been conducted on concrete with strength over 100 MPa. Also revealed by that study, is that no constitutive models had been proposed for deriving the dynamic increase factor for concrete over 100 MPa.  The presented results was compared with an existing constitutive model for dynamic strength enhancement, and indicates that existing constitutive models only are usable for compressive strengths up to 100 MPa.   Although this programme is based on a limited number of tests only, it is recommended that new constitutive models for deriving dynamic strength enhancement for HPC are developed. In addition ex-tra SHPB tests and special setup will be required to determine the dynamic tensile strength of HPC. 5 CONCLUSION An experimental investigation of the dynamic be-haviour of High Performance Concretes (HPC) has been conducted using two different Split Hopkinson Pressure Bar devices. The statically compressive strengths of the tested HPC are 100 MPa and 160 MPa, respectively. The specimen has been tested at strain rates in the range of 100 sec-1 to 700 sec-1.   The dynamic increase factor (DIF) for compres-sive strength due to strain rate effects is between 1.84 and 3.40 for 100 MPa HPC, and between 1.17 and 2.47 for 160 MPa HPC, respectively.  Comparing the results with the constitutive CEB Model Code shows accordance for the 100 MPa HPC but only accordance in a very slight extent for the 160 MPa HPC.    It is recommended that new and more accurate constitutive models for deriving dynamic strength enhancement for HPC are developed.  6 NOTATION AND REFERENCES The following symbols and equations are used in this paper:  A  = cross-section area of pressure bar As  = cross-section area of specimen D  = specimen diameter E   = Young’s modulus of pressure bar      L   = length of specimen c0  = wave velocity in pressure bar fcd   = dynamic compressive strength  fcs   = static compressive strength fts   = static tensile strength fcd/ fcs = compressive DIF ftd/ fts = tensile DIF      f’co  = 10 MPa      t   = time     ε      = strain  ε       = strain rate (dynamic)  sε   = strain rate (static) log γ = 6.156 α – 2      α   = 1/(5+9 fcs / f’co)    Bischoff, P. H. and Perry, S. H. Compression behaviour of concrete at high strain-rates. Materials and Structures [24], 425-450. 1991. Comite Euro-International du Beton - Federation Internationale de la Precontrainte. CEB-FIP Model Code 90 Redwood Books, Trowbridge, Wiltshire, Great Britain. 1990.  Grote, D. L., Park, S. W., and Zhou, M. Dynamic behavior of concrete at high strain rates and pressures: I. experimental characterization. International Journal of Impact Engineer-ing 25[9], 869-886. 2001.  Li, Q. M. and Meng, H. About the dynamic strength enhance-ment of concrete-like materials in a split Hopkinson pres-sure bar test. International Journal of Solids and Structures 40[2], 343-360. 2003.  Linholm, U. S. and Bunshah, R. F. High strain rate tests - Measurement of mechanical properties. Interscience, New York 5, 199-216. 1971.  Lok, T. S. and Zhao, P. J., 2004, Impact response of steel fiber-reinforced concrete using a split Hopkinson pressure bar: Journal of Materials in Civil Engineering, v. 16, p. 54-59. Malvar, L. J. and Ross, C. A., 1998, Review of strain rate ef-fects for concrete in tension: Aci Materials Journal, v. 95, p. 735-739.   

Dynamic Increase Factors for High Performance Concrete in Compression using Split Hopkinson Pressure Bar

http://orbit.dtu.dk/ws/files/2899083/DIF_HPC_FraMCoS_ver_2.0.pdf

Dynamic Increase Factors for High Performance Concrete in Compression using Split Hopkinson Pressure Bar

Abstract