Noble dental alloys are often reused in dental practice by recasting. The aim of this study was to determine if repeated casting of high gold dental alloys has a detrimental effect on alloy microstructure, type of porosity, structure and microhardness. Results showed that recasting procedure had a strong effect on the change of alloy porosity type. It was also found that alloy microhardness increased with the increase of the number of recasting cycles. At the same time the grain growth and changes of the solid solution phases in the microstructure were observed

Cairovic, A. D.

Cvijović-Alagić, Ivana

Maksimović, Vesna

Pantić, Jelena R.

Journal of Mining and Metallurgy Section B Metallurgy

VinaR - Repository of the Vinča Institute of Nuclear Sciences

The recaSTIng effecTS on The hIgh gold denTal alloy
properTIeS
V.M. Maksimovića,*, a.d. Čairovićb, J.r. pantića, I.lj. cvijović-alagića
a University of Belgrade, Institute of Nuclear Sciences “Vinča”, Belgrade, Serbia
b University of Belgrade, School of Dental Medicine, Belgrade, Serbia
(Received 16 July 2013; accepted 20 October 2014)
Abstract
Noble dental alloys are often reused in dental practice by recasting. The aim of this study was to determine if repeated
casting of high gold dental alloys has a detrimental effect on alloy microstructure, type of porosity, structure and
microhardness. Results showed that recasting procedure had a strong effect on the change of alloy porosity type. It was also
found that alloy microhardness increased with the increase of the number of recasting cycles. At the same time the grain
growth and changes of the solid solution phases in the microstructure were observed.
Keywords: high gold dental alloy, recasting, microhardness, XRD analysis, alloy porosity
* Corresponding author: vesnam@vinca.rs
Journal  of  Mining and Metal lurgy,
Section B: Metal lurgy
DOI:10.2298/JMMB130716023M
1. Introduction
A vast number of alloys have been used for
fixed prosthodontic restorations [1,2]. Diverse
factors, such as cost ease of casting and finishing,
various mechanical properties, i.e. elastic modulus
and yield strength, color, accuracy of fit and
concerns regarding alloy corrosion resistance are
making the adequate alloy selection process quite
complex [3]. Dentist is responsible for the
conducted prosthetic therapy, which implies the
knowledge of composition and properties of a
dental alloy after laboratory procedure and before
its implantation into the patients’ mouth. For
decades gold has been used in dental practice to
fabricate cast dental prostheses. The interest in
using gold or precious noble-metal alloys with a
high content of gold, platinum and palladium was
due to theirs high corrosion and tarnishing
resistance, as well as high biocompatibility. In an
attempt to reduce the expense of possible
restorations, gold alloys could be subjected to the
recasting. Recasting, which comprises the alloy re-
melting and re-solidification, may change the
composition and structure of these alloys and thus
affects alloy mechanical properties and castability,
as well as the alloy corrosion resistance [4]. Over
the past 20 years the price of gold has risen
significantly in the world market. The high price of
gold led to a wider use of the precious alloys with a
lower gold content, as well as the basic alloys, in
dental prosthetics. On the other hand, once melted
and cast, precious dental alloys are being remelted
and recast in order to be reused in dental practice.
It is often impossible to determine the exact number
of melting and casting cycles to which alloy is
subjected, since it is not possible to determine the
exact content of the newly added alloy. A dental
alloy repeatedly subjected to melting and casting is
likely to change its chemical composition [5].
Some studies showed that the recasting also
contributes to the change of the dental alloy
biocompatibility due to the lower corrosion
resistance of microalloying elements [6]. Literature
data, regarding the recasting effects on elemental
composition and microstructural characteristics of
high gold dental alloys, are very rare [7].
Recommendations concerning the procedure of
gold alloys recasting vary from adding no new
metal during recasting procedure to adding up to
50% of new metal with previously melted buttons
or sprues removed from castings [8].
Even though majority of dentists would choose
high gold-based alloys for prosthetic therapy for
themselves, there is no rationale reason to claim
that the alloy with high gold percentage is
biologically inert [9,10]. Therefore, the objective of
this work was to investigate the effect of the high
gold dental alloy repeated casting on the alloy
overall porosity, microstructural properties,
crystallographic structure and microhardness, since
these properties can affect alloy biocompatibility.
J. Min. Metall. Sect. B-Metall. 51 (1) B (2015) 55 - 59 
V.M. Maksimović et al. / JMM  51 (1) B (2015) 55 - 59 
2. Materials and Methods
Alloy used in this study was a commercial high
gold dental alloy with the nominal chemical
composition (in wt.%): 75.5-Au, 11.0-Ag, 6.7-Cu, 4.4-
Pt, 1.2-Pd, 1.2-Zn. Test samples were prepered using
patterns and invested in a mold ring with a phosphate
bonded investment for precious alloy. Mold has been
preheated for one hour at 750 °C in furnace. Melting
was performed at temperature 940 ºC and the casting (tc
= 1120 °C) was performed in a casting machine in
accordance with the manufacturer’s instruction. The
molds were cooled at room temperature and after
cutting gating of molds samples were sandblasted. Test
alloy samples were cast in the laboratory induction
furnace in the shape of small disks with the diameter of
10 mm and thickness of 1 mm. High gold dental alloy
samples were examined after a various number of
casting cycles, since they were subjected to one (A1),
four (A4) and eight (A8) melting and casting
sequences. 
The alloy structure and properties were investigated
using light microscopy (LM), scanning electron
microscopy (SEM), energy dispersive spectroscopy
(EDS), X-ray diffraction (XRD) analysis and
microhardness measurements. Samples for
microstructural observations were prepared using the
standard metallographic preparation techniques. The
mixture of 10 ml HNO3 and 30 ml HCl was used as an
etching reagent. The polished and etched samples were
investigated using a LM Carl Ziess Axiovert 25
equipped with the digital Panasonic camera WV-CD50
and a SEM JEOL JSM-6460LV equipped with an EDS
Oxford Instruments INCA X-sight system. The
porosity of recast samples was micrographically
determined in the non-etched condition. For that
purpose ten micrographs of different sections of each
sample were photographed at magnification of 50x.
Porosity percentage of the projected area of examined
sample was calculated by the quantitative image
analysis processing using the standard image analysis
technique with adequate computer software (QWin).
The grain size of samples (A1, A4 and A8) was
determined in etched condition from microphotographs
which were taken at magnification of 50x. The grain
size has been evaluated using intercept method. Total
measured length for all samples was near 50 mm and
the number of  counted grains was about 300 [11].
XRD analysis was carried out on a Siemens D-500
diffractometar with a Ni filter and CuKα radiation
operated at a tube voltage of 35 kV and a tube current
of 20 mA in the theta/2theta mode and at scanning
speeds of 0.02 s-1 and 0.4 min-1. Microhardness
measurements were performed using a Buehler
MicroMet 5101 Vickers hardness tester with a load of
300 gf applied for 10 s. Microhardness results were
obtained as the average values of ten measurements.
3. results and discussion
Most frequently observed defect, present on the
surface of gold-based alloys, is alloy porosity, which
may be caused by two phenomena. The first
phenomenon is appearance of the shrinkage porosity
induced by the volume decrease during liquid to solid
transition, while the second one is the so-called gas
porosity which appears as round shiny pores scattered
on the alloy surface and in the bulk. These defects
cannot be removed by grinding or polishing, because
of the possible exposure of other subsurface pores
[12]. In the early days of dental casting, presence of
shrinkage porosity defects near the sprue attachment
points was not an uncommon. Results of numerous
investigations demonstrated that it was caused by
solidification of the melt in the sprue cutting off the
supply of the melt to the main casting while it was still
undergoing solidification and contraction [13]. This
could be avoided by the selection of appropriate
melting temperature, as well as by suitable design and
dimensions of the sprue. Nevertheless, even with
sprues of good design, it was found that localized
shrinkage porosity still persisted in some castings near
to their surfaces [13]. In this study change of the alloy
properties due to the casting conditions modification
is above all indicated with the linear increase of alloy
microhardness with the increase of casting cycle
number, as it is shown in Fig. 1. Namely, the change
of alloy microhardness with the number of recasting
cycles follows the ascending order 160 MPa → 179
MPa →194 MPa and after the eighth recast sequence
it is observed that the microhardness is increased
more than 20 % in regard to its value determined after
the first one (Fig. 1). Further, it is well known that
linear contractions of at least 1.25 % can be expected
during the liquid to solid transition of the dental noble
alloys [14], which in turn influences the alloy porosity
occurrence. Change of the overall porosity (including
shrinkage and gas porosity) of the recast high gold
dental alloy and the typical dendritic microstructures
of the recast alloy samples are shown in Figs. 1 and 2,
respectively. Two types of porosity may be
distinguished, i.e. the presence of shrinkage porosity
is dominant after first recasting sequence (Fig. 2a),
while in the other samples the presence of gas
porosity is clearly revealed (Figs. 2b and c). Porosity
varies from 0.4 % for A4 sample to 0.9 % in the case
of A1 sample. The increase of gas porosity is mainly
connected with the reduction of zinc content in the
alloy. Namely, it is well known that during multiple
melting and casting comes to reduction in the content
of the zinc and copper. Zinc acts as an oxygen
scavenger during melting to minimize the oxidation of
the other elements in the alloy. Zinc prevents oxygen
from forming gas porosity in the casting [4]. The grain
growth with recasting was also detected (Figs. 2 and
56
3). The change of average grain size and the number
of counted grains with increase of number of recasting
were given in Table 1.
Presence of the pores at the A4 alloy sample grain
boundaries was distinguished (Fig. 3b) due to the
higher content of impurities and oxides, which are
sites of first corrosive attack during etching.
EDS analysis of all samples was conducted and in
that purpose several different positions in the same
grain were analyzed, as it is shown in Table 2. The
EDS point analysis indicates the presence of the
chemical composition inhomogeneity between two
adjacent grains, especially when platinum, palladium
and zinc are concerned.
Recasting results in appearance of the new grains
with size that may differ from the original one (Table
1). When the melting temperature and casting
conditions are maintained uniform, i.e. the same for
all samples as it is the case in this study, the new grain
size depends mainly on the concentration of the grain
formation nuclei. Although generally the impurities
may facilitate grains nucleation, which might lead to
the decrease of the grain size, in this study the grain
size increased with each consecutive recasting
sequence (Fig. 2). For example, Horasawa and Marek
observed that in the case of the silver-palladium alloy
the grain size has increased steadily with the increase
of the number of recasting cycles [4]. Concentration
of inclusions and impurities, such as oxides, nitrides
and carbides, rapidly increases during the multiple
casting of the noble alloys resulting in the
microhardness increase (Fig. 1). Bearing this fact in
mind, it may be concluded that the increased
concentration of impurities during multiple casting
may be regarded as a rather important factor
influencing the increase of microhardness. These
impurities act as a barrier to dislocation motion
V.M. Maksimović et al. / JMM  51 (1) B (2015) 55 - 59 57
Sample A1 A4 A8
Mean grain size (μm) 179.4 249.7 274.3
Counted grains 313 233 225
A1 sample A4 sample A8 sample
100
120
140
160
180
200
220
 HV0.3
 Porosity
Recast high gold dental alloy
M
ic
ro
ha
rd
ne
ss
, H
V
0.
3 /
 M
Pa
0.0
0.2
0.4
0.6
0.8
1.0
Po
ro
si
ty
 / 
%
Figure 1. Recasting effect on the microhardness and
porosity of the high gold dental alloy.
Table 1. The average grain size and number of counted
grains in A1, A4 and A8 samples in as-cast
condition. 
Figure 3. SEM micrographs showing microstructural features and grain boundaries of the high gold dental alloy. (a) A1,
(b) A4 and (c) A8 alloy samples.
Figure 2. LM micrographs showing microstructure of the high gold dental alloy. (a) A1, (b) A4 and (c) A8 alloy samples.
a) b) c)
a) b) c)
causing the hardening of the matrix [4]. In the same
time, solid solution effects must not be neglected.
Investigated high gold dental alloy is multiphase
alloy, since it contains different elements with
different chemical affinity. Every change in the
elements ratio influences change in the alloy structure
and properties. Gold-silver, gold-palladium and gold-
platinum form solid solutions in all proportions. On
the other hand, the ratio of silver and copper is very
sensible because silver and copper have limited
solubility in the solid state. 
The XRD patterns of the alloy samples subjected
to the recasting are shown in Fig. 4. As can be seen,
peaks characteristic for gold-palladium-platinum
solid solution are present in the XRD patterns and
correspond to          cubic crystal structure. The intense
peaks observed at approximately 40o, 45o, 66.5o, 80o
and 84o represent (111), (200), (220), (311) and (222)
Bragg reflections, respectively. With the increase of
the casting sequence number, intensity of gold rich
solid solution peaks changes and some peaks
completely disappear after the eighth recasting cycle
(peaks which correspond to the reflections from the
(200) and (311) planes). However, XRD analysis of
the alloy sample after eight consecutive recasts
revealed presence of the palladium rich solid solution
(Fig. 4). The crystallite size of the gold-palladium-
platinum rich solid solution was calculated for all
samples (A1, A4 and A8) using line broadening
information and Scherrer’s formula. The crystallite
sizes were calculated using peaks broadening profile
of (111) peak at 2θ ≈ 40˚ and Sherrer’s formula given
in Eq. 1:
(1)
where λ is wavelength (1.5418 Å) and β is full
V.M. Maksimović et al. / JMM  51 (1) B (2015) 55 - 59 58
Table 2. The chemical composition of the single grain (in wt.%) determined by EDS analysis.
Spectrum
chemical composition / wt.%
cu Zn pd ag pt au
1 6.93 0.65 - 11.68 - 80.74
2 6.61 1.15 - 11.23 1.26 79.75
3 5.78 0.99 1.53 9.94 2.53 79.23
Mean 6.44 0.93 0.51 10.95 1.26 79.91
± s.d. ± 0.59 ± 0.26 ± 0.88 ± 0.90 ± 1.26 ± 0.77
mFm3
qb
l
cos
9.0=d
30 40 50 60 70 80 90 100
0
500
1000
1500
2000
2500
3000
3500
4000
4500
A8
A4
A1
(222)
(311)
(220)
(200)
(111)
 
 
In
te
ns
ity
 / 
a.
u.
2q / degree
30 35 40 45 50
0
100
200
300
400
500
600
700
800
 
 
SS2
SS2
SS1
SS1
In
te
ns
ity
 / 
C
ps
2q / degree
30 35 40 45 50
0
2000
4000
6000
8000
10000
12000
tt
SS
SS
 
 
t
In
te
ns
ity
 / 
C
ps
2q / degree
- peaks from Kb  radiation
Figure 4. XRD analysis of A1, A4 and A8 alloy samples in
the as-cast condition.
Figure 5. XRD patterns of (a) A4 and (b) A8 alloy samples
obtained using the slow scan mode.
a)
b)
width half maximum (FWHM) of the corresponding
peak. The calculated crystallite sizes of the all
obtained gold-palladium-platinum solid solutions are
around 17 nm, as it was reported in the literature [15-
18].
Further XRD analysis showed (Fig. 5a) that after
the fourth recasting sequence two solid solutions are
present in the alloy microstructure: gold-palladium-
platinum solid solution (SS1) and platinum-silver
solid solution (SS2). On other hand, further increase
of the casting sequence number causes separation of
the gold-palladium-platinum rich solid solution (SS)
(Fig. 5b). Thus, it is reasonable to suppose that
disappearance of some peaks and appearance of SS1
and SS2 solid solutions peaks on the recorded alloy
XRD patterns, together with increased concentration
of impurities, may also affect the increase of alloy
microhardness (see Fig. 1) during the increase of
casting sequence number (A4 and A8 samples).
4. conclusions
From the presented results it can be concluded that
the recasting procedure changes the microstructure,
crystallographic structure and microhardness of the
high gold dental alloy. Microstructure analysis
showed that the grain growth occurred during
recasting and that two types of porosity were
distinguished. The microhardness increase was
induced not only by the increase of impurities
concentration, but also by the disappearance and
appearance of different phases during recasting
sequence. Generally, results of this study indicate that
this type of high gold dental alloy may be safely used
in recast condition only after it was subjected to a
small number of recasting cycles. Further
investigation will be focused on the corrosion
behavior of a high gold dental alloy after repeated
casting.
acknowledgment 
This research was supported by the Ministry of
Education, Science and Technological Development
of the  under grant III 45012.
references
[1] J.C. Wataha, J. Prosthet. Dent., 83 (2000) 223.
[2] C. Manaranche, H. Hornberger, Dent. Mater., 23
(2007) 1428.
[3] J.C. Wataha, R.L.Messer, Dent. Clin. N. Am., 48
(2004) 499.
[4] N. Horasawaa, M. Marek, Dent. Mater., 20 (2004) 352.
[5] M. Peraire, J. Martinez-Gomis, J.M. Anglada, J. Bizar,
J. Salsench, F.J. Gil, Int. J. Prosthodont., 20 (2007) 286.
[6] R. Rudolf, J. Kramberger, T. Zupančič-Hartner, A.
Marić Dragaš, V. Lazić, Stom. Glas. S., 53 (2006) 236.
[7] D. Stamenković, A. Čairović, M. Čolić, R. Rudolf, K.
Radović, I. Đorđević, Acta Veterinaria 59 (2009) 641.
[8] A.S. Al-Hiyasat, H. Darmani, J. Prosthet. Dent., 93
(2005) 158.
[9] I. Galić, J. Živko-Babić, Z. Shauperl, J. Vukšić, Acta
Stomatol. Croat., 42 (2008) 255.
[10] K.F. Leinfelder, J. Am. Dent. Assoc., 128 (1997) 37.
[11] A. Maltais, D. Dube, M.Fiset, G. Laroche, S. Turgeon,
Met. Charact. 52 (2004) 103.
[12] G.M. Ingo, C. Riccucci, G. Chiozzini, J. Am. Ceram.
Soc., 84 (2001) 1839.
[13] D. Ott, C.J. Raub, W.S. Rapson, Gold Bull., 18 (1985)
98.
[14] K.J. Anusavice, Phillips’ science of dental materials -
10th edition, Philadelphia, Pennsylvania, W.B.
Saunders Company, 1996, p. 517.
[15] K. Kosso, T. Saito,  Kawashima, Dent.Mater.J., 31
(2012) 669.
[16] T. Tani, K. Udoh, K. Yasuda, G. Van Tendeloo, J. Van
Landuyt, J. Dent. Res., 70 (1991) 1350.
[17] W.B. Lui, J.N. Wang, Dent. Mater., 23 (2007) 1136.
[18] T. Shiraishi, M. Ohta, J. Mater. Sci. - Mater. M., 13
(2002) 979.
V.M. Maksimović et al. / JMM  51 (1) B (2015) 55 - 59 59


The Recasting Effects on the High Gold Dental Alloy Properties

Čairović, Aleksandra

Pantić, J.R.

School of dental Medicine dIgitaL archivE

The recaSTIng effecTS on The hIgh gold denTal alloyproperTIeSV.M. Maksimovića,*, a.d. Čairovićb, J.r. pantića, I.lj. cvijović-alagićaa University of Belgrade, Institute of Nuclear Sciences “Vinča”, Belgrade, Serbiab University of Belgrade, School of Dental Medicine, Belgrade, Serbia(Received 16 July 2013; accepted 20 October 2014)AbstractNoble dental alloys are often reused in dental practice by recasting. The aim of this study was to determine if repeatedcasting of high gold dental alloys has a detrimental effect on alloy microstructure, type of porosity, structure andmicrohardness. Results showed that recasting procedure had a strong effect on the change of alloy porosity type. It was alsofound that alloy microhardness increased with the increase of the number of recasting cycles. At the same time the graingrowth and changes of the solid solution phases in the microstructure were observed.Keywords: high gold dental alloy, recasting, microhardness, XRD analysis, alloy porosity* Corresponding author: vesnam@vinca.rsJournal  of  Mining and Metal lurgy,Section B: Metal lurgyDOI:10.2298/JMMB130716023M1. IntroductionA vast number of alloys have been used forfixed prosthodontic restorations [1,2]. Diversefactors, such as cost ease of casting and finishing,various mechanical properties, i.e. elastic modulusand yield strength, color, accuracy of fit andconcerns regarding alloy corrosion resistance aremaking the adequate alloy selection process quitecomplex [3]. Dentist is responsible for theconducted prosthetic therapy, which implies theknowledge of composition and properties of adental alloy after laboratory procedure and beforeits implantation into the patients’ mouth. Fordecades gold has been used in dental practice tofabricate cast dental prostheses. The interest inusing gold or precious noble-metal alloys with ahigh content of gold, platinum and palladium wasdue to theirs high corrosion and tarnishingresistance, as well as high biocompatibility. In anattempt to reduce the expense of possiblerestorations, gold alloys could be subjected to therecasting. Recasting, which comprises the alloy re-melting and re-solidification, may change thecomposition and structure of these alloys and thusaffects alloy mechanical properties and castability,as well as the alloy corrosion resistance [4]. Overthe past 20 years the price of gold has risensignificantly in the world market. The high price ofgold led to a wider use of the precious alloys with alower gold content, as well as the basic alloys, indental prosthetics. On the other hand, once meltedand cast, precious dental alloys are being remeltedand recast in order to be reused in dental practice.It is often impossible to determine the exact numberof melting and casting cycles to which alloy issubjected, since it is not possible to determine theexact content of the newly added alloy. A dentalalloy repeatedly subjected to melting and casting islikely to change its chemical composition [5].Some studies showed that the recasting alsocontributes to the change of the dental alloybiocompatibility due to the lower corrosionresistance of microalloying elements [6]. Literaturedata, regarding the recasting effects on elementalcomposition and microstructural characteristics ofhigh gold dental alloys, are very rare [7].Recommendations concerning the procedure ofgold alloys recasting vary from adding no newmetal during recasting procedure to adding up to50% of new metal with previously melted buttonsor sprues removed from castings [8].Even though majority of dentists would choosehigh gold-based alloys for prosthetic therapy forthemselves, there is no rationale reason to claimthat the alloy with high gold percentage isbiologically inert [9,10]. Therefore, the objective ofthis work was to investigate the effect of the highgold dental alloy repeated casting on the alloyoverall porosity, microstructural properties,crystallographic structure and microhardness, sincethese properties can affect alloy biocompatibility.J. Min. Metall. Sect. B-Metall. 51 (1) B (2015) 55 - 59 V.M. Maksimović et al. / JMM  51 (1) B (2015) 55 - 59 2. Materials and MethodsAlloy used in this study was a commercial highgold dental alloy with the nominal chemicalcomposition (in wt.%): 75.5-Au, 11.0-Ag, 6.7-Cu, 4.4-Pt, 1.2-Pd, 1.2-Zn. Test samples were prepered usingpatterns and invested in a mold ring with a phosphatebonded investment for precious alloy. Mold has beenpreheated for one hour at 750 °C in furnace. Meltingwas performed at temperature 940 ºC and the casting (tc= 1120 °C) was performed in a casting machine inaccordance with the manufacturer’s instruction. Themolds were cooled at room temperature and aftercutting gating of molds samples were sandblasted. Testalloy samples were cast in the laboratory inductionfurnace in the shape of small disks with the diameter of10 mm and thickness of 1 mm. High gold dental alloysamples were examined after a various number ofcasting cycles, since they were subjected to one (A1),four (A4) and eight (A8) melting and castingsequences. The alloy structure and properties were investigatedusing light microscopy (LM), scanning electronmicroscopy (SEM), energy dispersive spectroscopy(EDS), X-ray diffraction (XRD) analysis andmicrohardness measurements. Samples formicrostructural observations were prepared using thestandard metallographic preparation techniques. Themixture of 10 ml HNO3 and 30 ml HCl was used as anetching reagent. The polished and etched samples wereinvestigated using a LM Carl Ziess Axiovert 25equipped with the digital Panasonic camera WV-CD50and a SEM JEOL JSM-6460LV equipped with an EDSOxford Instruments INCA X-sight system. Theporosity of recast samples was micrographicallydetermined in the non-etched condition. For thatpurpose ten micrographs of different sections of eachsample were photographed at magnification of 50x.Porosity percentage of the projected area of examinedsample was calculated by the quantitative imageanalysis processing using the standard image analysistechnique with adequate computer software (QWin).The grain size of samples (A1, A4 and A8) wasdetermined in etched condition from microphotographswhich were taken at magnification of 50x. The grainsize has been evaluated using intercept method. Totalmeasured length for all samples was near 50 mm andthe number of  counted grains was about 300 [11].XRD analysis was carried out on a Siemens D-500diffractometar with a Ni filter and CuKα radiationoperated at a tube voltage of 35 kV and a tube currentof 20 mA in the theta/2theta mode and at scanningspeeds of 0.02 s-1 and 0.4 min-1. Microhardnessmeasurements were performed using a BuehlerMicroMet 5101 Vickers hardness tester with a load of300 gf applied for 10 s. Microhardness results wereobtained as the average values of ten measurements.3. results and discussionMost frequently observed defect, present on thesurface of gold-based alloys, is alloy porosity, whichmay be caused by two phenomena. The firstphenomenon is appearance of the shrinkage porosityinduced by the volume decrease during liquid to solidtransition, while the second one is the so-called gasporosity which appears as round shiny pores scatteredon the alloy surface and in the bulk. These defectscannot be removed by grinding or polishing, becauseof the possible exposure of other subsurface pores[12]. In the early days of dental casting, presence ofshrinkage porosity defects near the sprue attachmentpoints was not an uncommon. Results of numerousinvestigations demonstrated that it was caused bysolidification of the melt in the sprue cutting off thesupply of the melt to the main casting while it was stillundergoing solidification and contraction [13]. Thiscould be avoided by the selection of appropriatemelting temperature, as well as by suitable design anddimensions of the sprue. Nevertheless, even withsprues of good design, it was found that localizedshrinkage porosity still persisted in some castings nearto their surfaces [13]. In this study change of the alloyproperties due to the casting conditions modificationis above all indicated with the linear increase of alloymicrohardness with the increase of casting cyclenumber, as it is shown in Fig. 1. Namely, the changeof alloy microhardness with the number of recastingcycles follows the ascending order 160 MPa → 179MPa →194 MPa and after the eighth recast sequenceit is observed that the microhardness is increasedmore than 20 % in regard to its value determined afterthe first one (Fig. 1). Further, it is well known thatlinear contractions of at least 1.25 % can be expectedduring the liquid to solid transition of the dental noblealloys [14], which in turn influences the alloy porosityoccurrence. Change of the overall porosity (includingshrinkage and gas porosity) of the recast high golddental alloy and the typical dendritic microstructuresof the recast alloy samples are shown in Figs. 1 and 2,respectively. Two types of porosity may bedistinguished, i.e. the presence of shrinkage porosityis dominant after first recasting sequence (Fig. 2a),while in the other samples the presence of gasporosity is clearly revealed (Figs. 2b and c). Porosityvaries from 0.4 % for A4 sample to 0.9 % in the caseof A1 sample. The increase of gas porosity is mainlyconnected with the reduction of zinc content in thealloy. Namely, it is well known that during multiplemelting and casting comes to reduction in the contentof the zinc and copper. Zinc acts as an oxygenscavenger during melting to minimize the oxidation ofthe other elements in the alloy. Zinc prevents oxygenfrom forming gas porosity in the casting [4]. The graingrowth with recasting was also detected (Figs. 2 and563). The change of average grain size and the numberof counted grains with increase of number of recastingwere given in Table 1.Presence of the pores at the A4 alloy sample grainboundaries was distinguished (Fig. 3b) due to thehigher content of impurities and oxides, which aresites of first corrosive attack during etching.EDS analysis of all samples was conducted and inthat purpose several different positions in the samegrain were analyzed, as it is shown in Table 2. TheEDS point analysis indicates the presence of thechemical composition inhomogeneity between twoadjacent grains, especially when platinum, palladiumand zinc are concerned.Recasting results in appearance of the new grainswith size that may differ from the original one (Table1). When the melting temperature and castingconditions are maintained uniform, i.e. the same forall samples as it is the case in this study, the new grainsize depends mainly on the concentration of the grainformation nuclei. Although generally the impuritiesmay facilitate grains nucleation, which might lead tothe decrease of the grain size, in this study the grainsize increased with each consecutive recastingsequence (Fig. 2). For example, Horasawa and Marekobserved that in the case of the silver-palladium alloythe grain size has increased steadily with the increaseof the number of recasting cycles [4]. Concentrationof inclusions and impurities, such as oxides, nitridesand carbides, rapidly increases during the multiplecasting of the noble alloys resulting in themicrohardness increase (Fig. 1). Bearing this fact inmind, it may be concluded that the increasedconcentration of impurities during multiple castingmay be regarded as a rather important factorinfluencing the increase of microhardness. Theseimpurities act as a barrier to dislocation motionV.M. Maksimović et al. / JMM  51 (1) B (2015) 55 - 59 57Sample A1 A4 A8Mean grain size (μm) 179.4 249.7 274.3Counted grains 313 233 225A1 sample A4 sample A8 sample100120140160180200220 HV0.3 PorosityRecast high gold dental alloyMi cr oh ar dn es s,  HV0 .3 / MP a0.00.20.40.60.81.0P or os it y /  %Figure 1. Recasting effect on the microhardness andporosity of the high gold dental alloy.Table 1. The average grain size and number of countedgrains in A1, A4 and A8 samples in as-castcondition. Figure 3. SEM micrographs showing microstructural features and grain boundaries of the high gold dental alloy. (a) A1,(b) A4 and (c) A8 alloy samples.Figure 2. LM micrographs showing microstructure of the high gold dental alloy. (a) A1, (b) A4 and (c) A8 alloy samples.a) b) c)a) b) c)causing the hardening of the matrix [4]. In the sametime, solid solution effects must not be neglected.Investigated high gold dental alloy is multiphasealloy, since it contains different elements withdifferent chemical affinity. Every change in theelements ratio influences change in the alloy structureand properties. Gold-silver, gold-palladium and gold-platinum form solid solutions in all proportions. Onthe other hand, the ratio of silver and copper is verysensible because silver and copper have limitedsolubility in the solid state. The XRD patterns of the alloy samples subjectedto the recasting are shown in Fig. 4. As can be seen,peaks characteristic for gold-palladium-platinumsolid solution are present in the XRD patterns andcorrespond to          cubic crystal structure. The intensepeaks observed at approximately 40o, 45o, 66.5o, 80oand 84o represent (111), (200), (220), (311) and (222)Bragg reflections, respectively. With the increase ofthe casting sequence number, intensity of gold richsolid solution peaks changes and some peakscompletely disappear after the eighth recasting cycle(peaks which correspond to the reflections from the(200) and (311) planes). However, XRD analysis ofthe alloy sample after eight consecutive recastsrevealed presence of the palladium rich solid solution(Fig. 4). The crystallite size of the gold-palladium-platinum rich solid solution was calculated for allsamples (A1, A4 and A8) using line broadeninginformation and Scherrer’s formula. The crystallitesizes were calculated using peaks broadening profileof (111) peak at 2θ ≈ 40˚ and Sherrer’s formula givenin Eq. 1:(1)where λ is wavelength (1.5418 Å) and β is fullV.M. Maksimović et al. / JMM  51 (1) B (2015) 55 - 59 58Table 2. The chemical composition of the single grain (in wt.%) determined by EDS analysis.Spectrumchemical composition / wt.%cu Zn pd ag pt au1 6.93 0.65 - 11.68 - 80.742 6.61 1.15 - 11.23 1.26 79.753 5.78 0.99 1.53 9.94 2.53 79.23Mean 6.44 0.93 0.51 10.95 1.26 79.91± s.d. ± 0.59 ± 0.26 ± 0.88 ± 0.90 ± 1.26 ± 0.77mFm3qblcos9.0=d30 40 50 60 70 80 90 100050010001500200025003000350040004500A8A4A1(222)(311)(220)(200)(111)  I nt en si t y /  a .u .2q / degree30 35 40 45 500100200300400500600700800  SS2SS2SS1SS1I nt en si t y /  Cp s2q / degree30 35 40 45 50020004000600080001000012000ttSSSS  tI nt en si t y /  Cp s2q / degree- peaks from Kb  radiationFigure 4. XRD analysis of A1, A4 and A8 alloy samples inthe as-cast condition.Figure 5. XRD patterns of (a) A4 and (b) A8 alloy samplesobtained using the slow scan mode.a)b)width half maximum (FWHM) of the correspondingpeak. The calculated crystallite sizes of the allobtained gold-palladium-platinum solid solutions arearound 17 nm, as it was reported in the literature [15-18].Further XRD analysis showed (Fig. 5a) that afterthe fourth recasting sequence two solid solutions arepresent in the alloy microstructure: gold-palladium-platinum solid solution (SS1) and platinum-silversolid solution (SS2). On other hand, further increaseof the casting sequence number causes separation ofthe gold-palladium-platinum rich solid solution (SS)(Fig. 5b). Thus, it is reasonable to suppose thatdisappearance of some peaks and appearance of SS1and SS2 solid solutions peaks on the recorded alloyXRD patterns, together with increased concentrationof impurities, may also affect the increase of alloymicrohardness (see Fig. 1) during the increase ofcasting sequence number (A4 and A8 samples).4. conclusionsFrom the presented results it can be concluded thatthe recasting procedure changes the microstructure,crystallographic structure and microhardness of thehigh gold dental alloy. Microstructure analysisshowed that the grain growth occurred duringrecasting and that two types of porosity weredistinguished. The microhardness increase wasinduced not only by the increase of impuritiesconcentration, but also by the disappearance andappearance of different phases during recastingsequence. Generally, results of this study indicate thatthis type of high gold dental alloy may be safely usedin recast condition only after it was subjected to asmall number of recasting cycles. Furtherinvestigation will be focused on the corrosionbehavior of a high gold dental alloy after repeatedcasting.acknowledgment This research was supported by the Ministry ofEducation, Science and Technological Developmentof the  under grant III 45012.references[1] J.C. Wataha, J. Prosthet. Dent., 83 (2000) 223.[2] C. Manaranche, H. Hornberger, Dent. Mater., 23(2007) 1428.[3] J.C. Wataha, R.L.Messer, Dent. Clin. N. Am., 48(2004) 499.[4] N. Horasawaa, M. Marek, Dent. Mater., 20 (2004) 352.[5] M. Peraire, J. Martinez-Gomis, J.M. Anglada, J. Bizar,J. Salsench, F.J. Gil, Int. J. Prosthodont., 20 (2007) 286.[6] R. Rudolf, J. Kramberger, T. Zupančič-Hartner, A.Marić Dragaš, V. Lazić, Stom. Glas. S., 53 (2006) 236.[7] D. Stamenković, A. Čairović, M. Čolić, R. Rudolf, K.Radović, I. Đorđević, Acta Veterinaria 59 (2009) 641.[8] A.S. Al-Hiyasat, H. Darmani, J. Prosthet. Dent., 93(2005) 158.[9] I. Galić, J. Živko-Babić, Z. Shauperl, J. Vukšić, ActaStomatol. Croat., 42 (2008) 255.[10] K.F. Leinfelder, J. Am. Dent. Assoc., 128 (1997) 37.[11] A. Maltais, D. Dube, M.Fiset, G. Laroche, S. Turgeon,Met. Charact. 52 (2004) 103.[12] G.M. Ingo, C. Riccucci, G. Chiozzini, J. Am. Ceram.Soc., 84 (2001) 1839.[13] D. Ott, C.J. Raub, W.S. Rapson, Gold Bull., 18 (1985)98.[14] K.J. Anusavice, Phillips’ science of dental materials -10th edition, Philadelphia, Pennsylvania, W.B.Saunders Company, 1996, p. 517.[15] K. Kosso, T. Saito,  Kawashima, Dent.Mater.J., 31(2012) 669.[16] T. Tani, K. Udoh, K. Yasuda, G. Van Tendeloo, J. VanLanduyt, J. Dent. Res., 70 (1991) 1350.[17] W.B. Lui, J.N. Wang, Dent. Mater., 23 (2007) 1136.[18] T. Shiraishi, M. Ohta, J. Mater. Sci. - Mater. M., 13(2002) 979.V.M. Maksimović et al. / JMM  51 (1) B (2015) 55 - 59 59

English

The recasting effects on the high gold dental alloy properties

Repository of the Vinča Nuclear Institute (VinaR)

The recaSTIng effecTS on The hIgh gold denTal alloyproperTIeSV.M. Maksimovića,*, a.d. Čairovićb, J.r. pantića, I.lj. cvijović-alagićaa University of Belgrade, Institute of Nuclear Sciences “Vinča”, Belgrade, Serbiab University of Belgrade, School of Dental Medicine, Belgrade, Serbia(Received 16 July 2013; accepted 20 October 2014)AbstractNoble dental alloys are often reused in dental practice by recasting. The aim of this study was to determine if repeatedcasting of high gold dental alloys has a detrimental effect on alloy microstructure, type of porosity, structure andmicrohardness. Results showed that recasting procedure had a strong effect on the change of alloy porosity type. It was alsofound that alloy microhardness increased with the increase of the number of recasting cycles. At the same time the graingrowth and changes of the solid solution phases in the microstructure were observed.Keywords: high gold dental alloy, recasting, microhardness, XRD analysis, alloy porosity* Corresponding author: vesnam@vinca.rsJournal  of  Mining and Metal lurgy,Section B: Metal lurgyDOI:10.2298/JMMB130716023M1. IntroductionA vast number of alloys have been used forfixed prosthodontic restorations [1,2]. Diversefactors, such as cost ease of casting and finishing,various mechanical properties, i.e. elastic modulusand yield strength, color, accuracy of fit andconcerns regarding alloy corrosion resistance aremaking the adequate alloy selection process quitecomplex [3]. Dentist is responsible for theconducted prosthetic therapy, which implies theknowledge of composition and properties of adental alloy after laboratory procedure and beforeits implantation into the patients’ mouth. Fordecades gold has been used in dental practice tofabricate cast dental prostheses. The interest inusing gold or precious noble-metal alloys with ahigh content of gold, platinum and palladium wasdue to theirs high corrosion and tarnishingresistance, as well as high biocompatibility. In anattempt to reduce the expense of possiblerestorations, gold alloys could be subjected to therecasting. Recasting, which comprises the alloy re-melting and re-solidification, may change thecomposition and structure of these alloys and thusaffects alloy mechanical properties and castability,as well as the alloy corrosion resistance [4]. Overthe past 20 years the price of gold has risensignificantly in the world market. The high price ofgold led to a wider use of the precious alloys with alower gold content, as well as the basic alloys, indental prosthetics. On the other hand, once meltedand cast, precious dental alloys are being remeltedand recast in order to be reused in dental practice.It is often impossible to determine the exact numberof melting and casting cycles to which alloy issubjected, since it is not possible to determine theexact content of the newly added alloy. A dentalalloy repeatedly subjected to melting and casting islikely to change its chemical composition [5].Some studies showed that the recasting alsocontributes to the change of the dental alloybiocompatibility due to the lower corrosionresistance of microalloying elements [6]. Literaturedata, regarding the recasting effects on elementalcomposition and microstructural characteristics ofhigh gold dental alloys, are very rare [7].Recommendations concerning the procedure ofgold alloys recasting vary from adding no newmetal during recasting procedure to adding up to50% of new metal with previously melted buttonsor sprues removed from castings [8].Even though majority of dentists would choosehigh gold-based alloys for prosthetic therapy forthemselves, there is no rationale reason to claimthat the alloy with high gold percentage isbiologically inert [9,10]. Therefore, the objective ofthis work was to investigate the effect of the highgold dental alloy repeated casting on the alloyoverall porosity, microstructural properties,crystallographic structure and microhardness, sincethese properties can affect alloy biocompatibility.J. Min. Metall. Sect. B-Metall. 51 (1) B (2015) 55 - 59 V.M. Maksimović et al. / JMM  51 (1) B (2015) 55 - 59 2. Materials and MethodsAlloy used in this study was a commercial highgold dental alloy with the nominal chemicalcomposition (in wt.%): 75.5-Au, 11.0-Ag, 6.7-Cu, 4.4-Pt, 1.2-Pd, 1.2-Zn. Test samples were prepered usingpatterns and invested in a mold ring with a phosphatebonded investment for precious alloy. Mold has beenpreheated for one hour at 750 °C in furnace. Meltingwas performed at temperature 940 ºC and the casting (tc= 1120 °C) was performed in a casting machine inaccordance with the manufacturer’s instruction. Themolds were cooled at room temperature and aftercutting gating of molds samples were sandblasted. Testalloy samples were cast in the laboratory inductionfurnace in the shape of small disks with the diameter of10 mm and thickness of 1 mm. High gold dental alloysamples were examined after a various number ofcasting cycles, since they were subjected to one (A1),four (A4) and eight (A8) melting and castingsequences. The alloy structure and properties were investigatedusing light microscopy (LM), scanning electronmicroscopy (SEM), energy dispersive spectroscopy(EDS), X-ray diffraction (XRD) analysis andmicrohardness measurements. Samples formicrostructural observations were prepared using thestandard metallographic preparation techniques. Themixture of 10 ml HNO3 and 30 ml HCl was used as anetching reagent. The polished and etched samples wereinvestigated using a LM Carl Ziess Axiovert 25equipped with the digital Panasonic camera WV-CD50and a SEM JEOL JSM-6460LV equipped with an EDSOxford Instruments INCA X-sight system. Theporosity of recast samples was micrographicallydetermined in the non-etched condition. For thatpurpose ten micrographs of different sections of eachsample were photographed at magnification of 50x.Porosity percentage of the projected area of examinedsample was calculated by the quantitative imageanalysis processing using the standard image analysistechnique with adequate computer software (QWin).The grain size of samples (A1, A4 and A8) wasdetermined in etched condition from microphotographswhich were taken at magnification of 50x. The grainsize has been evaluated using intercept method. Totalmeasured length for all samples was near 50 mm andthe number of  counted grains was about 300 [11].XRD analysis was carried out on a Siemens D-500diffractometar with a Ni filter and CuKα radiationoperated at a tube voltage of 35 kV and a tube currentof 20 mA in the theta/2theta mode and at scanningspeeds of 0.02 s-1 and 0.4 min-1. Microhardnessmeasurements were performed using a BuehlerMicroMet 5101 Vickers hardness tester with a load of300 gf applied for 10 s. Microhardness results wereobtained as the average values of ten measurements.3. results and discussionMost frequently observed defect, present on thesurface of gold-based alloys, is alloy porosity, whichmay be caused by two phenomena. The firstphenomenon is appearance of the shrinkage porosityinduced by the volume decrease during liquid to solidtransition, while the second one is the so-called gasporosity which appears as round shiny pores scatteredon the alloy surface and in the bulk. These defectscannot be removed by grinding or polishing, becauseof the possible exposure of other subsurface pores[12]. In the early days of dental casting, presence ofshrinkage porosity defects near the sprue attachmentpoints was not an uncommon. Results of numerousinvestigations demonstrated that it was caused bysolidification of the melt in the sprue cutting off thesupply of the melt to the main casting while it was stillundergoing solidification and contraction [13]. Thiscould be avoided by the selection of appropriatemelting temperature, as well as by suitable design anddimensions of the sprue. Nevertheless, even withsprues of good design, it was found that localizedshrinkage porosity still persisted in some castings nearto their surfaces [13]. In this study change of the alloyproperties due to the casting conditions modificationis above all indicated with the linear increase of alloymicrohardness with the increase of casting cyclenumber, as it is shown in Fig. 1. Namely, the changeof alloy microhardness with the number of recastingcycles follows the ascending order 160 MPa → 179MPa →194 MPa and after the eighth recast sequenceit is observed that the microhardness is increasedmore than 20 % in regard to its value determined afterthe first one (Fig. 1). Further, it is well known thatlinear contractions of at least 1.25 % can be expectedduring the liquid to solid transition of the dental noblealloys [14], which in turn influences the alloy porosityoccurrence. Change of the overall porosity (includingshrinkage and gas porosity) of the recast high golddental alloy and the typical dendritic microstructuresof the recast alloy samples are shown in Figs. 1 and 2,respectively. Two types of porosity may bedistinguished, i.e. the presence of shrinkage porosityis dominant after first recasting sequence (Fig. 2a),while in the other samples the presence of gasporosity is clearly revealed (Figs. 2b and c). Porosityvaries from 0.4 % for A4 sample to 0.9 % in the caseof A1 sample. The increase of gas porosity is mainlyconnected with the reduction of zinc content in thealloy. Namely, it is well known that during multiplemelting and casting comes to reduction in the contentof the zinc and copper. Zinc acts as an oxygenscavenger during melting to minimize the oxidation ofthe other elements in the alloy. Zinc prevents oxygenfrom forming gas porosity in the casting [4]. The graingrowth with recasting was also detected (Figs. 2 and563). The change of average grain size and the numberof counted grains with increase of number of recastingwere given in Table 1.Presence of the pores at the A4 alloy sample grainboundaries was distinguished (Fig. 3b) due to thehigher content of impurities and oxides, which aresites of first corrosive attack during etching.EDS analysis of all samples was conducted and inthat purpose several different positions in the samegrain were analyzed, as it is shown in Table 2. TheEDS point analysis indicates the presence of thechemical composition inhomogeneity between twoadjacent grains, especially when platinum, palladiumand zinc are concerned.Recasting results in appearance of the new grainswith size that may differ from the original one (Table1). When the melting temperature and castingconditions are maintained uniform, i.e. the same forall samples as it is the case in this study, the new grainsize depends mainly on the concentration of the grainformation nuclei. Although generally the impuritiesmay facilitate grains nucleation, which might lead tothe decrease of the grain size, in this study the grainsize increased with each consecutive recastingsequence (Fig. 2). For example, Horasawa and Marekobserved that in the case of the silver-palladium alloythe grain size has increased steadily with the increaseof the number of recasting cycles [4]. Concentrationof inclusions and impurities, such as oxides, nitridesand carbides, rapidly increases during the multiplecasting of the noble alloys resulting in themicrohardness increase (Fig. 1). Bearing this fact inmind, it may be concluded that the increasedconcentration of impurities during multiple castingmay be regarded as a rather important factorinfluencing the increase of microhardness. Theseimpurities act as a barrier to dislocation motionV.M. Maksimović et al. / JMM  51 (1) B (2015) 55 - 59 57Sample A1 A4 A8Mean grain size (μm) 179.4 249.7 274.3Counted grains 313 233 225A1 sample A4 sample A8 sample100120140160180200220 HV0.3 PorosityRecast high gold dental alloyMicrohardness, HV0.3 / MPa0.00.20.40.60.81.0Porosity / %Figure 1. Recasting effect on the microhardness andporosity of the high gold dental alloy.Table 1. The average grain size and number of countedgrains in A1, A4 and A8 samples in as-castcondition. Figure 3. SEM micrographs showing microstructural features and grain boundaries of the high gold dental alloy. (a) A1,(b) A4 and (c) A8 alloy samples.Figure 2. LM micrographs showing microstructure of the high gold dental alloy. (a) A1, (b) A4 and (c) A8 alloy samples.a) b) c)a) b) c)causing the hardening of the matrix [4]. In the sametime, solid solution effects must not be neglected.Investigated high gold dental alloy is multiphasealloy, since it contains different elements withdifferent chemical affinity. Every change in theelements ratio influences change in the alloy structureand properties. Gold-silver, gold-palladium and gold-platinum form solid solutions in all proportions. Onthe other hand, the ratio of silver and copper is verysensible because silver and copper have limitedsolubility in the solid state. The XRD patterns of the alloy samples subjectedto the recasting are shown in Fig. 4. As can be seen,peaks characteristic for gold-palladium-platinumsolid solution are present in the XRD patterns andcorrespond to          cubic crystal structure. The intensepeaks observed at approximately 40o, 45o, 66.5o, 80oand 84o represent (111), (200), (220), (311) and (222)Bragg reflections, respectively. With the increase ofthe casting sequence number, intensity of gold richsolid solution peaks changes and some peakscompletely disappear after the eighth recasting cycle(peaks which correspond to the reflections from the(200) and (311) planes). However, XRD analysis ofthe alloy sample after eight consecutive recastsrevealed presence of the palladium rich solid solution(Fig. 4). The crystallite size of the gold-palladium-platinum rich solid solution was calculated for allsamples (A1, A4 and A8) using line broadeninginformation and Scherrer’s formula. The crystallitesizes were calculated using peaks broadening profileof (111) peak at 2θ ≈ 40˚ and Sherrer’s formula givenin Eq. 1:(1)where λ is wavelength (1.5418 Å) and β is fullV.M. Maksimović et al. / JMM  51 (1) B (2015) 55 - 59 58Table 2. The chemical composition of the single grain (in wt.%) determined by EDS analysis.Spectrumchemical composition / wt.%cu Zn pd ag pt au1 6.93 0.65 - 11.68 - 80.742 6.61 1.15 - 11.23 1.26 79.753 5.78 0.99 1.53 9.94 2.53 79.23Mean 6.44 0.93 0.51 10.95 1.26 79.91± s.d. ± 0.59 ± 0.26 ± 0.88 ± 0.90 ± 1.26 ± 0.77mFm3qblcos9.0=d30 40 50 60 70 80 90 100050010001500200025003000350040004500A8A4A1(222)(311)(220)(200)(111)  Intensity / a.u.2q / degree30 35 40 45 500100200300400500600700800  SS2SS2SS1SS1Intensity / Cps2q / degree30 35 40 45 50020004000600080001000012000ttSSSS  tIntensity / Cps2q / degree- peaks from Kb  radiationFigure 4. XRD analysis of A1, A4 and A8 alloy samples inthe as-cast condition.Figure 5. XRD patterns of (a) A4 and (b) A8 alloy samplesobtained using the slow scan mode.a)b)width half maximum (FWHM) of the correspondingpeak. The calculated crystallite sizes of the allobtained gold-palladium-platinum solid solutions arearound 17 nm, as it was reported in the literature [15-18].Further XRD analysis showed (Fig. 5a) that afterthe fourth recasting sequence two solid solutions arepresent in the alloy microstructure: gold-palladium-platinum solid solution (SS1) and platinum-silversolid solution (SS2). On other hand, further increaseof the casting sequence number causes separation ofthe gold-palladium-platinum rich solid solution (SS)(Fig. 5b). Thus, it is reasonable to suppose thatdisappearance of some peaks and appearance of SS1and SS2 solid solutions peaks on the recorded alloyXRD patterns, together with increased concentrationof impurities, may also affect the increase of alloymicrohardness (see Fig. 1) during the increase ofcasting sequence number (A4 and A8 samples).4. conclusionsFrom the presented results it can be concluded thatthe recasting procedure changes the microstructure,crystallographic structure and microhardness of thehigh gold dental alloy. Microstructure analysisshowed that the grain growth occurred duringrecasting and that two types of porosity weredistinguished. The microhardness increase wasinduced not only by the increase of impuritiesconcentration, but also by the disappearance andappearance of different phases during recastingsequence. Generally, results of this study indicate thatthis type of high gold dental alloy may be safely usedin recast condition only after it was subjected to asmall number of recasting cycles. Furtherinvestigation will be focused on the corrosionbehavior of a high gold dental alloy after repeatedcasting.acknowledgment This research was supported by the Ministry ofEducation, Science and Technological Developmentof the  under grant III 45012.references[1] J.C. Wataha, J. Prosthet. Dent., 83 (2000) 223.[2] C. Manaranche, H. Hornberger, Dent. Mater., 23(2007) 1428.[3] J.C. Wataha, R.L.Messer, Dent. Clin. N. Am., 48(2004) 499.[4] N. Horasawaa, M. Marek, Dent. Mater., 20 (2004) 352.[5] M. Peraire, J. Martinez-Gomis, J.M. Anglada, J. Bizar,J. Salsench, F.J. Gil, Int. J. Prosthodont., 20 (2007) 286.[6] R. Rudolf, J. Kramberger, T. Zupančič-Hartner, A.Marić Dragaš, V. Lazić, Stom. Glas. S., 53 (2006) 236.[7] D. Stamenković, A. Čairović, M. Čolić, R. Rudolf, K.Radović, I. Đorđević, Acta Veterinaria 59 (2009) 641.[8] A.S. Al-Hiyasat, H. Darmani, J. Prosthet. Dent., 93(2005) 158.[9] I. Galić, J. Živko-Babić, Z. Shauperl, J. Vukšić, ActaStomatol. Croat., 42 (2008) 255.[10] K.F. Leinfelder, J. Am. Dent. Assoc., 128 (1997) 37.[11] A. Maltais, D. Dube, M.Fiset, G. Laroche, S. Turgeon,Met. Charact. 52 (2004) 103.[12] G.M. Ingo, C. Riccucci, G. Chiozzini, J. Am. Ceram.Soc., 84 (2001) 1839.[13] D. Ott, C.J. Raub, W.S. Rapson, Gold Bull., 18 (1985)98.[14] K.J. Anusavice, Phillips’ science of dental materials -10th edition, Philadelphia, Pennsylvania, W.B.Saunders Company, 1996, p. 517.[15] K. Kosso, T. Saito,  Kawashima, Dent.Mater.J., 31(2012) 669.[16] T. Tani, K. Udoh, K. Yasuda, G. Van Tendeloo, J. VanLanduyt, J. Dent. Res., 70 (1991) 1350.[17] W.B. Lui, J.N. Wang, Dent. Mater., 23 (2007) 1136.[18] T. Shiraishi, M. Ohta, J. Mater. Sci. - Mater. M., 13(2002) 979.V.M. Maksimović et al. / JMM  51 (1) B (2015) 55 - 59 59

Noble dental alloys are often reused in dental practice by recasting. The aim
   of this study was to determine if repeated casting of high gold dental alloys
   has a detrimental effect on alloy microstructure, type of porosity, structure
   and microhardness. Results showed that recasting procedure had a strong
   effect on the change of alloy porosity type. It was also found that alloy
   microhardness increased with the increase of the number of recasting cycles.
   At the same time the grain growth and changes of the solid solution phases in
   the microstructure were observed.</jats:p

The Recasting Effects on the High Gold Dental Alloy Properties

Abstract

Similar works

Full text

Available Versions

VinaR - Repository of the Vinča Institute of Nuclear Sciences

School of dental Medicine dIgitaL archivE

Repository of the Vinča Nuclear Institute (VinaR)

Crossref