ABSTRAK
Geokomposit (GeCo) dan geobiokomposit (GeBiCo) telah disintesis secara
reaktif dengan inisiator benzoil peroksida (BPO) dan pelarut ksilena. Limbah
polipropilena (LPP) dipergunakan sebagai matriks polimer. Bentonit komersial
(commercial Bentonite, comBen) sebagai penghambat bakar, sedangkan seng borat
(Zinc Borate, ZB) dipergunakan sebagai aditif penghambat bakar. Serat daun nanas
(Pineapple Leaf Fiber, PaF) dipergunakan sebagai penguat. Asam akrilat yang telah
dicangkokkan pada LPP (LPP-g-AA) dipergunakan sebagai senyawa penggandeng
multifungsional, sedangkan divinil benzena (DVB) dipergunakan sebagai senyawa
penyambung silang. Spektrofotometer FTIR dan XRD dipergunakan untuk
karakterisasi terjadinya interaksi antara bahan-bahan penyusun komposit.
Hasil uji sifat mekanik energi serap (Absorption Energy, AE) dan
ketangguhan impak (Impact Toughness, IT) menunjukkan bahwa geokomposit dan
geobiokomposit mempunyai sifat yang lebih baik dari pada LPP. Geokomposit dan
geobiokomposit juga mempunyai sifat ketahanan bakar lebih baik dari pada LPP hal
ini ditunjukkan dari hasil uji waktu pembentukan nyala (Time To Ignition, TTI) dan
kecepatan bakar (Burning Rate, BR). Hasil uji kalor pembakaran mendukung hasil
uji ketahanan bakar yakni geokomposit dan geobiokomposit mempunyai kalor
pembakaran lebih kecil dari pada LPP.
Kata Kunci: bentonit, geobiokomposit, geokomposit, ketahanan bakar, polipropilena,
serat daun nanas
ABTRACT
Geo-composite (GeCo) and geo-bio-composite (GeBiCo) have been reactively
synthesized by initiator benzoyl peroxide (BPO) using solvent xylene. Recycled
polypropylene (rPP) was used as the matrix polymer. Commercial bentonite
(comBen) was used as a fire retardant, while zinc borate (ZB) was used as an
additive. Pineapple leaf fiber (PaF) was used as a reinforcement. Acrylic acid was
grafted on rPP (rPP-g-AA) used as multifunctional coupling compound, whereas
divinyl benzene (DVB) was used as a crosslinker compound. XRD and FTIR
spectrophotometer were used to characterize the interaction between constituent
composite materials.
Results of testing the mechanical properties of energy absorption (EA) and
impact toughness (IT) showed that geo-composite and geo-bio-composite have better
mechanical properties than the LPP. Geo-composite and geo-bio-composite also have
better fire resistance properties than LPP as indicated from results of the time to
ignition (TTI) and burning rate (BR). Results of heat of combustion supported of
testing the fire resistance, geo-composite and geo-bio-composite have heat of
combustion less than the LPP.
Keywords: bentonite, fire resistence, geocomposite, geobiocomposite, pineapple
fiber, polypropylen