The synthesis of poly-5,7-diallyl-25,26,27,28-tetrahydroxycalix[4]arene were performed in experimental series

as follows: (1) Cyclotetramerization of p-t-butylphenol with NaOH and paraformaldehyde to p-butylcalix[4]arene, (2)

Debutylation of p-butylcalix[4]arene using AlCl3 and phenol to tetrahydroxycalix[4]arene, (3) Allylation reaction using

allylbromide to diallyloxy-dihydroxycalix[4]arene, (4) Claisen rearrangement reaction, (5) Cationic polymerization to

diallylcalix[4]arenes. All of the synthesized products were analyzed by means of IR spectrometer and 1H-NMR

spectrometer. The result of 25,27-diallyloxy-26,28-dihydroxycalix[4]arene synthesis was white crystals having m.p.

205-207 °C in 80.95% yield. The synthesis of 5,7-diallyl-25,26,27,28-tetrahydroxy-calix[4]arene gave light yellow

crystals having m.p. 214-216 °C in 78.67% yield. The polymerization gave poly(5,7-diallyl-25,26,27,28-tetrahydroxycalix[

4]arene) having m.p. 338-340 °C, in 60% yield. Its estimated has a relative molecular weight of 18,738

g/mol with the number of unit repetition about 37 monomer units.

Keywords: Diallylation, polymerization, Poly-5,7-diallyl-25,26,27,28-tetrahydroxycalix[4]aren

Firdaus, Maulidan

Handayani, Desi Suci

Jumina,

Triana , Kusumaningsih

English

Sebelas Maret Institutional Repository

Indo. J. Chem., 2010, 10 (1), 127 - 131    Desi Suci Handayani et al.127*  Corresponding author. Email address : desi_sh2006@yahoo.co.id** Postgraduate Student of Chemistry Department, Faculty of Mathematic and Natural Sciences, Universitas Gadjah MadaSYNTHESIS OF POLY-5,7-DIALLYL-25,26,27,28-TETRAHYDROXYCALIX[4]ARENEDesi Suci Handayani1.*.**, Jumina2, Maulidan Firdaus1, Triana Kusumaningsih11Department of Chemistry, Faculty of Mathematics and Natural Sciences, Sebelas Maret University, Jl. Ir. Sutami 36A Kentingan Surakarta 57126, Indonesia2Department of Chemistry, Faculty of Mathematics and Natural Sciences, Universitas Gadjah Mada, Sekip Utara, Yogyakarta 55281, IndonesiaReceived December 16, 2009; Accepted January 12, 2010ABSTRACTThe synthesis of poly-5,7-diallyl-25,26,27,28-tetrahydroxycalix[4]arene were performed in experimental series as follows: (1) Cyclotetramerization of p-t-butylphenol with NaOH and paraformaldehyde to p-butylcalix[4]arene, (2) Debutylation of p-butylcalix[4]arene using AlCl3 and phenol to tetrahydroxycalix[4]arene, (3) Allylation reaction using allylbromide to diallyloxy-dihydroxycalix[4]arene, (4) Claisen rearrangement reaction, (5) Cationic polymerization to diallylcalix[4]arenes. All of the synthesized products were analyzed by means of IR spectrometer and 1H-NMR spectrometer. The result of 25,27-diallyloxy-26,28-dihydroxycalix[4]arene synthesis was white crystals having m.p. 205-207 °C in 80.95% yield. The synthesis of 5,7-diallyl-25,26,27,28-tetrahydroxy-calix[4]arene gave light yellow crystals having m.p. 214-216 °C in 78.67% yield. The polymerization gave poly(5,7-diallyl-25,26,27,28-tetra-hydroxycalix[4]arene) having m.p. 338-340 °C, in 60% yield. Its estimated has a relative molecular weight of 18,738 g/mol with the number of unit repetition about 37 monomer units.Keywords: Diallylation, polymerization, Poly-5,7-diallyl-25,26,27,28-tetrahydroxycalix[4]areneINTRODUCTIONCalixarenes are belonging to macrocyclic molecules for example crown ether and cyclodextrin [1]. These compounds have active groups arranged in unique molecular geometry in the form of vase or pot in which can be used as host of cation, anion, and neutral molecule [2]. Calixarenes in water system can also be utilized as a surfactant and acid catalyst [3].Based on its characteristic structure and its function of calixarenes structures, this compound has many great attentions in supramolecular chemistry especially for the synthesis of its derivative. Haverlock et al. [4] had been synthesized calix[4]arene-bis(benzocrown-6) which was reported having transport ability for Francium ion. Synthesis of  5,17-bis[(4-nitrophenill)(azo)phenill]-26,28-bis(1-propyloxy)-25,27-calix[4] monocrown-6 was synthesized and was reported able to trap metal cation i.e. Li+, Na+, K+, Rb+, Cs+, Ag+, Mg2+, Ca2+, dan Sr2+ [5]Functionalized calixarenes have previously been prepared by the direct substitution route [6] and the p-Claisen rearrangement route [7-8]; the present work adds another procedure for introducing various groups onto the p-position of the calixarene framework. p-tert-Butylcalix[4]arene (Fig. 1 (1)) can be prepared in good yield by the base-induced condensation of tert-butylphenol and formaldehyde [9]. Aluminum chloride-catalyzed removal of the tert-butyl groups proceeds in excellent yield [7-8].Monoalkylation of calix[4]arenes to the corresponding monoalkyl ethers 2 (Fig. 1) can be performed directly by reaction with an excess of alkylating agent in the presence of 1.2 equivalents of a weak base (CsF) in N,N-dimethylformamide (DMF) [10], as an alternative for the selective dealkylation of di- or tetraalkylated calix[4]arenes with Me3SiI [11]. Astronger base like K2CO3 in acetonitrile gave not only the monoalkyl ethers (2) but also the 1,3-dialkyl ethers (3) (Fig. 1). Selective alkylation of two diametrically located phenol rings is possible in good yields by reacting calix[4]arenes with 2 equivalents of alkylating agent in acetonitrile, in the presence of 1 equivalent of K2CO3 [12-13]. All the products (3) are obtained in the cone conformation and further alkylation does not take place. Alkylation of calix[4]arenes with an excess of NaH in DMF and 2.2 equivalents of alkylating agent leads to the 1,2-dialkoxycalix[4]arenes (Fig. 2 (4)) (in the cone conformation) in acceptable yields, besides tetrasubstituted calix[4]arenes and starting material [14]. Among the upper rim functionalized methods, Gutsche and his coworker reported that the allyl group could be introduced by the Claisen rearrangement route (5) [8].It has been mentioned that the ability of calixarenes to function as host molecules, extractant, adsorbent, and complexing agent are due to the presenceIndo. J. Chem., 2010, 10 (1), 127 - 131    Desi Suci Handayani et al.128Fig 1. Structures of (1) p-t-butylcalix[4]arene, (2) monoallyloxycalix[4]arene, (3) 1,3-diallyloxycalix[4]areneFig 2. structures of 1,2-diallyloxycalix[4]arene (4) and diallylcalix[4]arene (5)of cavity and donor atoms in the molecule. Accordingly, it could be expected that such functions would be greatly enhanced when the molecule does exist in a polymeric state. This occurs as the total volume of the cavity and the number of donor atoms in calixarene polymeric materials would be exponentially multiplied compared to those of calixarene monomer. This is the reason why we are interested to synthesize polypropylcalix[4]arene polymers. Based on this phenomenon, this research was carried out to synthesize calix[4]arene polymers having two allyl groups. Due to the existence of the two allyl groups, cross link reaction between calix[4]arene was taken place. This makes the molecules immobile and it can be predicted that the adsorption process for heavy metal cation will be higher.EXPERIMENTAL SECTIONMaterialsMost of organic compounds utilized in this research were commercial products of high purity purchased from Merck, and used as such without any further purification.InstrumentationStructure identifications were performed using infra red spectrometer (IR Shimadzu 8201 PC) and 1H-NMR spectra were recorded at room temperature on JEOL-MY500 spectrometer. The relative molecular weight a polymer could be determined using Ubbelohde viscometer.ProcedureSynthesis of p-tert-butylcalix[4]arenep-t-butyl-calix[4]arene was prepared according reported to procedures reported previously [15]. Recrystallization from CH3Cl and CH3OH afforded 57.83% of a white crystal: m.p 343-345 °C (literature 344-346 °C); FTIR (KBr/cm-1) OH 3178.5, c=c 3024 and 1604.7, CH2 1456.8, CH3 1361.7.Synthesis of 25,26,27,28-tetrahydroxycalix[4]arenePowdered agregrat of p-t-butylcalix[4]arene(13.3 g; 20 mmol) was dissolved in 125 mL toluene in a three neck round bottom flask equipped with a nitrogen flow pipe. In the mixture was added 9.02 g (96 mmol) powdered phenol and 14 g (105 mmol) AlCl3anhydrous. The mixture was stirred at room temperature for 1 h under slow nitrogen atmosphere. The mixture was cooled at ice bath and 250 mL HCl 0.2 N solution was added to be followed by stirring for 30 min. Organic layer was collected. The excess of toluene was evaporated and methanol was added until a solid was formed. Recrystallization from CH3Cl and CH3OH afforded 6.16 g (72.64%) of a white crystal: m.p 310-312.5 °C; FTIR (KBr/cm-1) OH 3159, c=c 1593.1 and CH2 1456.8.Synthesis of 25,27-dialliloxy-26,28-dihydroxycalix-[4]arene25,26,27,28-tetrahydroxycalix[4]arene (1.06 g, 2.5 mmol) was dissolved in acetonytrile. K2CO3 (0.34 g, 3 mmol) and allylbromide (0.67 g, 5.6 mmol) were then added. The mixture was refluxed for 24 h under nitrogen atmosphere (the reaction was monitored using TLC until the starting material spot disappear). The solvent was removed, the residu was dissolved in chloroform and washed with diluted HCl, and solvent was then removed. The product was recrystallized from CH3Cl and CH3OH afforded 1.02 g (80.95%) of a white crystals: m.p 205-207 °C; FTIR (KBr/cm-1) OH 3410.15, c=c 1651.07,  987.55 and 925.83 (specific for vinyl group); 1HNMR (500 MHz, CDCl3) δ : 8.0027 (-OH, 4H), 7.2595–6.6631 (H Ar, 12H), 6.2756-6.2414 (-CH allyl, 2H), 5.8124–5.4139 (=CH2 Vinyl, 4 H), 4.5596–Indo. J. Chem., 2010, 10 (1), 127 - 131    Desi Suci Handayani et al.1294.3114 (-CH2- bridge, 8H), and 3.4021–3.37464 (-CH2-allyl, 4H).Synthesis of 5,17-diallyl-25,26,27,28-tetrahydroxycalix[4]arene25-27-dialliloxy-26,28-dihydroxycalix[4]arene (1.5 g)was dissolved in 20 mL N,N-diethylanilin and refluxed for 3 h. The mixture was cooled and poured in 20 mL ice water. Concentrated HCl (25 mL) was then added and the obtained solid was filtered. The solid was recrystallized using dichloromethane-methanol afforded 1.18 g (78.67%) of a light yellow crystals : m.p 214-216 °C; FTIR (KBr/cm-1) OH 3179.97, c=c 1635.64 and 1604.77,  995.27 (specific for vinyl group); 1HNMR (500 MHz, CDCl3) δ : 10.2260 (-OH, 4H), 7.0787-6.7584 (H aromatic, 10 H), 5.8931-5.8588 (-CH allyl, 2 H), 5.0790-5.0949 (-CH2- allyl, 4 H), 4.2760-3.4998 (-CH2-bridge, 8 H), and 3.2016-3.1882 (=CH2 vinyl, 4 H).Polymerization reaction5,17-diallyl-25,26,27,28-tetrahydroxycalix[4]arene(0.15 g) was dissolved in 15 mL chloroform in a 100 mL three neck round bottom flask equipped with condensor and a nitrogen flow pipe. Concentrated Sulfuric acid (0.4 mL) was then added (it was done 4 times every 30 min for polymerization process each 0.1 mL). Polymerization was performed for 5 h (the reaction was monitored using TLC). The polymerization was terminated by adding 0.5 methanol. Chloroform layer was washed using water until neutral, dried over Na2SO4 anhydrous, evaporated the solvent and dried in an exicator. The product was brown solid afforded 60%: m.p 338-340 °C; FTIR (KBr/cm-1) OH 3178.69, c=c 1604.77. The disappearances of vinyl (-CH=CH2) group at 995.27 cm-1 as well as absorption at 1635.64 cm-1.Relative molecular weight of poly-5,17-diallyl-25,26,27,28-tetrahydroxy-calix[4]areneMolecular weight determination of poly-5,7-diallyl-25,26,2728-tetrahydroxy-calix[4]arene was done by ubdelahde viscometry methods based on time flow measuring in chloroform as the solvent. Various concentration had been made in 0.075; 0.150; 0.300; dan 0.600 g/L.RESULT AND DISCUSSIONThe synthesis of p-t-butilkaliks[4]arene was carried out using a previously reported method [15]. The synthesis was performed using p-t-butylphenol, formaldehyde and NaOH as the catalyst. The scheme of the reaction depicted in Fig. 3.Fig 3. Reaction scheme of p-t-butil fenol synthesisFig 4. Debutylation of p-t-butylcalix[4]areneFig 5. Allyloxy of 25,26,27,28-tetrahydroxycalix[4]areneDebutylation is a Friedel-Craft alkylation (retro Friedel-Craft alkylation). Dealkylation of 4 tertier butyl groups of p-t-butylcalix[4]arene to 25,26,27,28-tetra hydroxycalix[4]arene is taken place in this reaction. The scheme of the reaction is depicted in Fig. 4. The dissapearence of absorption at 1361.7 cm-1 (for methyl group) at tertier butyl group indicated that the debutylation was taken place.Gutsche and his co-workers reported that the calixarene allyl ethers were able to transform to the corresponding p-allylcalixarenes by the heat-induced Claisen rearrangement [8]. It is assumed that the partially p-allyl substituted calix[4]arenes could also be prepared from the corresponding partially allyloxylated calix[4]arenes in the same rearrangement. The two diallyl ethers were prepared according to the general procedures reported by Reinhoudt and his co-workersfor the calix[4]arene's 1,2-dialkyl ethers and 1,3-dialkyl ethers [14,16]. Calix[4]arene 1,3-diallyl ether 2 was prepared by refluxing calix[4]arene with allyl bromide in CH3CN in the presence of K2CO3. The reaction scheme is ilustrated in Fig. 5.Indo. J. Chem., 2010, 10 (1), 127 - 131    Desi Suci Handayani et al.130Table 1. sp/C for Molecular Weight DeterminationConc (g/mL) t (second) η rel η sp η sp / c0 10.500.000075 12.43 1.183809524 0.183809524 2450.790.00015 14.98 1.426666667 0.426666667 2844.440.0003 20.67 1.968571429 0.968571429 3228.570.0006 35.60 3.39047619 2.39047619 3984.13Fig 6. Claisen rearrangement of 25,27-diallyloxy-26,28-dihydroxycalix[4]areneFig 7. Polymerization of 5,7-diallyl-25,26,2728-tetrahydroxycalix[4]areneFig 8. Graphic correlation of C versus sp/C of poly-5,7-diallyl-25,26,2728-tetrahydroxycalix[4]arene solution in chloroformClaisen rearrangement of 25,27-diallyloxy-26,28-dihydroxycalix[4]arene was taken place using the presence of N,N-diethyllaniline. The reaction was refluxed at 217 °C for 3 h. The solid product separated after excess HCl addition to remove the remaining N,N-diethylaniline. The obtained solid was then recrystallized using chloroform-methanol and 5,7-diallyl-25,26,2728-tetrahydroxycalix[4]arene was obtained. The reaction scheme is illustrated in Fig. 6.Based on FTIR and HNMR analyses, it can be concluded that Claisen rearrangement was taken place and 5,7-diallyl-25,26,2728-tetrahydroxycalix[4]arene was synthesized. HNMR spectra from the starting ethers, and the upfield shift of the allylic methylene hydrogen (from δ = 3.4 to δ = 3.2) indicated that allyl moieties had been transferred from the lower rim to the upper rim.Polymerisazition of 5,7-diallyl-25,26,2728-tetra-hydroxylcalix[4]arenePolymerization of 5,7-diallyl-25,26,2728-tetrahydroxycalix[4]arene using H2SO4 as the catalyst was carried out at room temperature (29 °C) under nitrogen atmosphere. The scheme of the reaction is depicted in Fig. 7.The disappearances of vinyl (-CH=CH2) group at 995.27 cm-1 as well as absorption at 1635.64 cm-1 showed that the polymerization was taken place.Relative molecular weight of poly-5,7-diallyl-25,26,27,28-tetrahydroxy-calix[4]areneObservation result for time flow in various concentration of poly-5,7-diallyl-25,26,2728-tetrahydroxycalix[4]arene and clhoroform solvent were calculated from relatively viscosity (r), specific viscosity (sp) and relatively reductive viscosity (sp/C), as presented in Table 1.Furthermore, based on Table 1, it can be obtained information about intrinsic viscosity from polymer solution which had been made using Huggins equation: 2'sp k CC          . Based on the equation, it can be made a graphic spCversus concentration (C). By extrapolation to zero concentration, the intercept, intrinsic viscosity, [η] of poly-5,7-diallyl-25,26,2728-Indo. J. Chem., 2010, 10 (1), 127 - 131    Desi Suci Handayani et al.131tetrahydroxycalix[4]arene can be obtained as illustrated in Fig. 8.The obtained intrinsic viscosity value is then added Mark-Houwink equation, avKM    . K and a is a constant which is depend on the polymer type and solvents. Based on Brandrup [17], K and a value for a certain polymer polypropylene polymer in chloroform at 30 °C are 2.18 x 10-2 mL/g and 0.725, respectively. By adding [η], K, and a values to Mark-Houwink equation, it can be obtain that the relative molecular weight (Mv) and total repeated unit (n) of poly-5,7-diallyl-25,26,2728-tetrahydroxycalix[4]arene are 18,738 g/mol and 37, respectively.CONCLUSIONPoly-5,7-diallyl-25,26,2728-tetrahydroxycalix[4]arenecan be synthesized by the following steps: (1) cyclotetramerization to p-t-b-calix[4]arene, (2) Debutylation to 25,26,27,28-tetrahydroxycalix[4]arene, (3) allylation to 25,27-diallyloxy-26,28-dihydroxycalix[4]arene, (4) Claisen rearrangement to 5,7-diallyl-25,26,27,28-tetrahydroxycalix[4]arene and (5) Polymerization. Poly-5,7-dallyl-25,26,27,28-tetrahydroxycalix[4]arene synthesized product was a solid having m.p. 338-340 °C, and molecular weight 18,738 g/mol with repeated unit : 37.ACKNOWLEDGEMENTThe financial support from Indonesian Directorate General of Higher Education in the form of Hibah Bersaing 2009 is greatly appreciated.REFERENCES1. Bohmer, V., 1995, Review, Angew. Chem., Int. Ed.Engl., 34, 713-745.2. Linane, P. and Shinkai, S., 1994, Chem. Ind., 811-814.3. Shinkai, S., Mori, S., Koreishi, H., Tsubaki, T., andManabe, O., 1986, J. Am. Chem. Soc., 108, 2409-2416.4. Haverlock, T.J., Mirzadeh, S., and Moyer, B.A., 2003, J. Am. Chem. Soc., 125, 1126-1127.5. Kim, J.Y., Kim, G., Kim, C.R., Lee, S.H., Lee, J.H., and Kim, J.S., 2003, J. Org. Chem., 68, 1933-1937.6. Gutsche, C.D. and Pagoria P.F., 1985, J. Am. Chem. Soc., 50, 5795-5802.7. Gutsche, C.D., Levine, J.A., and Sujeeth, P.K., 1985, J. Org. Chem.,50, 5802-5805.8. Gutsche, C.D. and Lin, L.G., 1986, Tetrahedron, 42, 1633-1640.9. Gutsche, C.D., Iqbal, M., and Stewart, D., 1986, J. Org. Chem., 51,742-745.10. Groenen, L.C., Ruel, B.H.M., Casnati, A., Verboom, W., Pochini, A., Ungaro, R., Harkema,S., and Reinhoudt, D.N., 1991, Tetrahedron,47,8379-8384.11. Casnati, A., Arduini, A., Ghidini, E., Pochini, A., and Ungaro, R., 1991, Tetrahedron, 47, 2221-2228.12. Van Loon, J.-D., Arduini, A., Verboom, W., Ungaro,R., van Hummel, G.J., Harkema, S., and Reinhoudt, D.N., 1989, Tetrahedron Lett., 30,2681-2684.13. Collins, E.M., McKervey, M.A., and Harris, S.J., 1989, J. Chem. Soc., Perkin Trans., 1, 372-374.14. Groenen, L.C, Ruel, B.H.M., Casnati, A., Timmerman, P., Verboom, W., Harkema, S., Pochini, A., Ungaro, R., and Reinhoudt, D.N., 1991, Tetrahedron Lett., 32, 2675-2678.15. Gutsche, C.D., Dhawan, B., No, K.H., dan Muthukrishnan, R., 1981, J. Am. Chem. Soc., 103,3782-3792.16. Van Loon, J.-D., Arduini, A., Coppi, L., Verboom, W., Pochinl, A., Ungaro, R., Harkema, S.,; Reinhoudt, D.N., 1990, J. Org. Chem., 55, 5639-5646.17. Brandrup, J., Immergut, E.H., and McDowel, W., 1975, Polymer Handbook, John Wiley and Sons, USA.

SYNTHESIS OF POLY-5,7-DIALLYL-25,26,27,28-TETRAHYDROXYCALIX[4]ARENE

http://eprints.uns.ac.id/13448/1/Publikasi_Jurnal(43).pdf

SYNTHESIS OF POLY-5,7-DIALLYL-25,26,27,28-TETRAHYDROXYCALIX[4]ARENE

Abstract