CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
Microstructure and thermal fatigue resistance of Co-Cr-W alloy coating by laser cladding
Authors
朱天辉
虞钢
+6 more
何秀丽
李少霞
宁伟健
郑彩云
王高飞
刘昊
Publication date
1 January 2006
Publisher
Abstract
针对钢质热负荷部件易产生热疲劳损伤的问题,采用同步送粉激光熔覆工艺,在活塞用中碳钢38Mn VS6表面制备了Co-Cr-W抗热疲劳合金涂层。利用光学显微镜、SEM、EDS及XRD对熔覆层显微组织和成分分布进行了分析,利用显微硬度计和实验室开发的激光热疲劳实验平台对熔覆层的显微硬度和热疲劳性能进行了测试。结果表明,熔覆层与基体冶金结合,无气孔、裂纹等缺陷。由于固溶强化、弥散强化效应,熔覆层具有较高的强度。送粉率为5.9 g/min时,涂层显微硬度在530~590 HV0.1之间,是基体硬度的2倍左右;熔覆层试样抗热疲劳性能相较于基体材料试样得到了显著的提高
Similar works
Full text
Available Versions
University of Birmingham Research Portal
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:pure.atira.dk:publications...
Last time updated on 01/02/2019
University of Birmingham Research Portal
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:pure.atira.dk:openaire_cri...
Last time updated on 14/12/2019
Institute Of Mechanics,Chinese Academy of Sciences
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:dspace.imech.ac.cn:311007/...
Last time updated on 12/02/2018