CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
Use of near infrared spectroscopy to detect non-recoverable collapse caused by tension wood in Eucalyptus globulus
Authors
Maximilian Wentzel-Vietheer
Publication date
1 January 2012
Publisher
Abstract
© 2012 Maximilian Wentzel-VietheerEucalyptus globulus is widely planted around the world. The wood is mainly used for fibreboard, paper and firewood. Use for sawn and engineered wood products can be limited because of the development of non-recoverable collapse caused by tension wood, which can severely distort wood surfaces and affect sawing and drying performance, leading to increased processing costs, lower yield (recovery) and thus reduced product value. In tension wood, cellulose content, microfibril angle (MFA), density, and stiffness (MOE) are altered compared to normal wood. The study investigated the calibration and application of near infrared (NIR) spectroscopy to measure these wood properties and detect non-recoverable collapse. Radial, bark to pith, wood cores were sampled from 175 trees in a 20 year old E. globulus silvicultural trial at Tostaree, Victoria, Australia. NIR spectra were measured at 1 mm intervals along the cores after drying to 12% estimated moisture content (EMC). Tangential shrinkage of the cores was measured at 8 points across each core after reconditioning to 12% MC. Spectra were measured on an additional 20 cores that were also analysed using SilviScan-3 to measure MFA, density and MOE, and NIR Partial Least Squares (PLS) Regression calibrations were developed. The calibrations were used to predict wood properties in the 175 cores, which were then related to the measured tangential shrinkage and non-recoverable collapse. NIR-predicted wood properties at points of non-recoverable collapse were consistent with the presence of tension wood (i.e. high cellulose, low MFA, high density and high MOE). Cellulose content and MOE were the best multiple regression predictors of tangential shrinkage. An NIR calibration developed to directly predict tangential shrinkage qualitatively identified zones of high shrinkage, but tended to under-predict measured shrinkage values. Tangential shrinkage, or the incidence of high tangential shrinkage, was not or only weakly correlated with tree size, height to diameter ratio, or lean. Silvicultural treatments (thinning intensity, fertilizer application) did not affect tangential shrinkage or tension wood formation. Generally, the incidence of non-recoverable collapse was greater in the wood grown since age 10 years. The study demonstrated that NIR predicted wood properties can be used to detect non-recoverable collapse caused by tension wood. The methodology has potential use in plantation and log assessment, wood processing, and tree breeding
Similar works
Full text
Available Versions
University of Melbourne Institutional Repository
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:jupiter.its.unimelb.edu.au...
Last time updated on 06/01/2019