The aim of this research was to investigate thermal conductivity of rod
material and rotation speed on globular structure forming in rheocasting
process.he rheocasting was a semisolid casting methods which gave the shear
force at semisolid phase to produce globular microstructure.
The raw material used in the research was hypoeutectic aluminum that
containing 6.23% Si. The material of rod used carbon, low carbon steel and
copper. The variations of rotation speed used in this research were 100 rpm, 150
rpm and 200 rpm. The value of roundness and grain size were calculated using
image analysis program.
It was observed that the maximum value of roundness was 0.666 and the
grain size was 69.25 µm occurred at 200 rpm of rotation speed using carbon rod.
Keywords: rheocasting, rotation speed, rod material, globular, form factor
Penelitian ini bertujuan untuk mengetahui pengaruh konduktivitas thermal
bahan batang pengaduk dan kecepatan putar terhadap pembentukan struktur
globular pada proses rheocasting. Rheocasting merupakan salah satu metode
pengecoran semisolid yang memberikan gaya geser saat logam cair berada pada
fasa semisolid untuk menghasilkan struktur mikro globular.
Bahan baku penelitian ini adalah aluminium hypoeutectic berkadar
6.23% Si. Bahan pengaduk yang digunakan antara lain karbon, baja karbon
rendah, dan tembaga dengan variasi kecepatan putar 100 rpm, 150 rpm, 200 rpm.
Perhitungan nilai kebulatan dan ukuran butir menggunakan program image
analysis.
Hasil penelitian menunjukkan bahwa nilai kebulatan maksimal 0,666 dan
ukuran butir 69,25 µm didapat pada variasi kecepatan putar 200 rpm dengan
menggunakan batang pengaduk karbon.
Kata kunci : rheocasting, kecepatan putar, bahan batang pengaduk, globular, faktor bentu