Structure and electrical properties of sodium tungsten bronzes thin films
- Publication date
- Publisher
- Elsevier
Abstract
Highly oriented thin films of NaxβWO3β(x=0.25β0.7) are grown on sapphire (1 1 0 2) and SrTiO3β (1 0 0) substrates by pulsed laser deposition. The colour of the films changes from blue through red to bronze yellow on varying the sodium content. The films are composed of particles less than 100 nm size. As in bulk NaxβWO3β, the resistivity is found to decrease on increasing the sodium content, and at around x=0.25, a non-metal to metal transition is clearly observed. The conductivity measurement of Na_0_._2_5WO_3 shows a crossover from temperature-activated Arrhenius behaviour at high temperatures to a variable range hopping mechanism near 70 K. The metallic samples show linear dependence of resistivity above 50 K. XPS studies confirm the presence of sodium in +1 and tungsten in +5 and +6 oxidation states