Functionalized Multi-Walled Carbon Nanotube-Reinforced Epoxy-Composites: Electrical And Mechanical Characterization

Abstract

Carbon nanotubes (CNTs) got great attention because of their interesting physical and mechanical properties. Due to these interesting properties observed at the nanoscale have motivated scientific community to utilize CNTs as reinforcement in composite materials. In the present study, different CNTs and epoxy nano-composites with different wt% (1, 2, 3, and 4%) of f-MWCNTs were prepared and their surface morphology and orientation has been investigated in detail. Further, the surface investigation, electrical and mechanical tests were carried out on CNTs-filled and unfilled epoxy at maximum sonication time 30 minute to identify the loading effect on the properties of the materials. Experimental results depicts well dispersion of f-MWCNTs, significant improvement that the resistivity of pure epoxy decreased from 108 .m to average value 103 .m with 1, 2, 3, and 4wt% f-MWCNTs. The 4.5wt% CNTs/epoxy was attributed to poor dispersion of f-MWCNTs in the nanocomposte. The hardness of nanocomposite loading 1, 2, 3, 4wt% of CNTs, increased 20.7%, 23.02%, 25.62%, 29.09% respectively as compared to pure epoxy. We believe that our strategy for obtaining CNT–reinforced epoxy nanocomposites is a very promising technology and will open a new doors in fields of aviation, aerospace, marine and sporting goods