Spindle-like Mesoporous α‑Fe₂O₃ Anode Material Prepared from MOF Template for High-Rate Lithium Batteries

Abstract

Spindle-like porous α-Fe₂O₃ was prepared from an iron-based metal organic framework (MOF) template. When tested as anode material for lithium batteries (LBs), this spindle-like porous α-Fe₂O₃ shows greatly enhanced performance of Li storage. The particle with a length and width of ∼0.8 and ∼0.4 μm, respectively, was composed of clustered Fe₂O₃ nanoparticles with sizes of <20 nm. The capacity of the porous α-Fe₂O₃ retained 911 mAh g^–1 after 50 cycles at a rate of 0.2 C. Even when cycled at 10 C, comparable capacity of 424 mAh g^–1 could be achieved