Deformability of a textile fabric is studied experimentally using a) friction test, b) out-of-plane compression, and c) bending. These tests reveal that a grafting of the fabric with carbon nano-fibres can significantly deteriorate its deformability. Therefore an optimal CNF mass fraction should be chosen for a particular production case, to obtain a compromise between improved strength and decreased drapability

Akkerman, R.

Gorbatikh, L.

Koissin, V.

Kotanjac, Z.

Lomov, S.V.

Warnet, L.

English

Koysin, V.

Kotanjac, Zeljko

Warnet, Laurent

Akkerman, Remko

University of Twente Research Information

TEXCOMP 10 Int. Conference, Lille, France, October 26-28 2010  181    Deformability of a Textile Reinforcement Modified with Nanofibres    V. KOISSINa, Ž. KOTANJACb, S.V. LOMOVc, L. GORBATIKHc, L. WARNETa, and R. AKKERMANa     ABSTRACT  Deformability of a textile fabric is studied experimentally using a) friction test, b) out-of-plane compression, and c) bending. These tests reveal that a grafting of the fabric with carbon nano-fibres can significantly deteriorate its deformability. Therefore an optimal CNF mass fraction should be chosen for a particular production case, to obtain a compromise between improved strength and decreased drapability.   INTRODUCTION  When producing 3D shaped textile composites, deformability of the fabric is a crucial manufacturing issue. Even for a flat part it is not always possible to attain the target fibre content. Sometimes the fabric is grafted with carbon nanotubes (CNTs) or nanofibres (CNFs), e.g., by their in-situ growth. On the one hand, this modification is expected to improve the fibre-matrix interface and crack bridging and, consequently, the damage resistance [1]. On the other hand, the deformability is foreseen to be altered by numerous inter-fibre links. The present study focuses on a particular case of a carbon-fibre fabric having in-situ grown carbon CNFs and aims to detect experimentally the effect of grafting, using 1) friction 2) out-of-plane compression, and 3) bending tests. For comparison, the base fabric (without CNFs) is tested also. All tests are conducted at the ambient conditions (~20°C, ~70% RH).  MATERIALS  Typical woven carbon reinforcement is used as the base material. This 5-harness satin weave, Fig.1 (left), is made of 3K untwisted tows of Torayca T300J 7 µm diameter fibres. Areal weight of the fabric is 285 g/m2. The fibres are de-sized.                                                         a University of Twente, Dept. of Design, Production & Management, Chair of Production Technology, P.O. box 217, 7500 AE Enschede, The Netherlands b University of Twente, Faculty of Science and Technology, Chair of Catalytic Processes and Materials, P.O. box 217, 7500 AE Enschede, The Netherlands c Katholieke Universiteit Leuven, Dept. of Metallurgy and Materials Engineering, Composite Materials Group, Kasteelpark Arenberg 44, B 3001 Heverlee, Belgium TEXCOMP 10 Int. Conference, Lille, France, October 26-28 2010  182   The grafted fabrics (sheets of approximately 26×31 cm) are manufactured using the Chemical Vapor Deposition (CVD) technique. First, the base fabric is impregnated with Nickel nitrate dissolved in acetone and subsequently placed into a gas chamber, where Ni(NO3)2 is reduced with hydrogen at 600°C to obtain Ni particles needed for CNF growth. Subsequently the CNFs are grown at the same temperature in a hydrocarbon gas mixture. The CNF weight fraction (wt.%) is controlled by varying the reaction time. The wt.% is calculated as (MN – M0)/MN, where M0 and MN are the initial and after-grafting weights of the specimen, respectively.  Figure 1 shows typical SEM images. It is seen that the distribution of grafting is mostly uniform on the fibres. Higher magnification images show its several constituents. First, there are large CNFs (diameter about 100 nm). Second, there are thinner CNFs (diameter about 50 nm) with characteristic morphology of branched structure. Finally, there are thin 5…20 nm diameter objects; TEM pictures allow surmising that they are CNFs too. SEM reveals also that the Ni particles are positioned at the ends of CNFs, and that there is no amorphous carbon phase.      Figure 1. The fabric (left) and SEM images of a Ni-loaded (centre) or 6.5wt.% grafted fibres (right).   FRICTION  Simple slope test is performed to measure the dry friction coefficient between the pairs fabric-aluminium and fabric-fabric, where either the base or grafted (6.5 wt.%) fabric is used. A flat plate is covered with the fabric; “naked” or “dressed” aluminium block is placed on it, and then the slope of the plate is changed gradually. The onset of slippage is detected visually, and then the corresponding slope is measured and directly recalculated into the friction coefficient. Different fabric orientations and their combinations are studied as shown symbolically in Fig.2. Six measurements are done and averaged for every case; the standard deviation is small, in spite of a non-automated way of testing. The results show that the grafting significantly increases the friction coefficient in the most of the cases. However, for several fabric-fabric orientations, the friction decreases after the grafting, Fig 2(b). Reasons of this discrepancy are not yet clear for the authors. The measurements are done for two contact pressures, to reveal a possible effect of nesting. The first assumption was that the nesting (if any) would increase the contact surface and, therefore, would increase the friction coefficient too. However Fig.2 shows a small but statistically constant decrease of this parameter along with increased contact pressure; this phenomenon is also not yet clear. TEXCOMP 10 Int. Conference, Lille, France, October 26-28 2010  183    Figure 2. Coulomb friction coefficient (mean values) for fabric-aluminium (left) and fabric-fabric (right) pairs. Red symbols – base fabric, blue symbols – grafted fabric. The fabric orientation is denoted as "|" for 0° = weft (the weft yarn floats over 4 warp ones), "–" for 90° = warp, "/" for +45°, and "\" for -45°.    COMPRESSIBILITY  Out-of-plane compression tests are performed at a 0.5 mm/min displacement rate, using a self-aligning compression rig (with a ball-pivot bottom platform). The first loading is applied without a specimen, to align the platform with the upper plate fixed in the moving crosshead. Then several tests are done without a specimen, to establish a calibration curve accounting for the rig compliance. Finally three successive compression cycles are applied to the specimen to measure its initial and “set” compressibility. Series of 2-3 specimens of about 45x45 mm in-plane size are tested for each variant of the fabric: virgin, loaded with Ni particles, 6.5 wt.% grafted, and 39 wt.% grafted. The maximum pressure (0.3 MPa) is limited by the used 1 kN load cell. Figure 3 shows typical results; scatter between different specimens of the same type is less than 10%. Fig.3 (left) reveals a consistent decrease of compressibility or increase of the fabric thickness for a given pressure after grafting.  The Ni-loaded specimen shows the highest compressibility. For a sized fabric this could be attributed to the loss of sizing burnt out at 600°C. However the used fabric is already de-sized, and the gas analysis does not show any foreign components during the heating. TGA supports this too, showing no loss of the specimen mass at this stage. The CNF-grafted specimens show a prominent difference between the first loading and the two succeeding cycles; this effect may probably be attributed to weaker nano-links crushed during the first loading. For the base fabric as well as for the Ni-loaded one this effect is much milder.  When expressed in the terms of the fibre volume fraction (including the weight of grafting), as shown in Fig.3 (right) for the 1st compression cycle, the trend is as follows. For a 0.1 MPa pressure (1 bar, corresponding to the vacuum forming), Vf of TEXCOMP 10 Int. Conference, Lille, France, October 26-28 2010  184  the virgin fabric is 52% and decreases to about 38% after the grafting. For these approximate calculations of Vf the densities of micro-fibres (MFs) and CNFs are assumed to be 1.76 g/cm3. It is also interesting to note that the stiffness curves of 6.5 and 39 wt.% specimens are close to each other in this figure; this can of course change if a higher density would be assigned for CNFs. Figure 3 (right) shows also that the higher compression resistance of the CNF-grafted specimens is not the result of just adding more carbon material inside the fabric. If we would virtually add the same mass of MFs into the fabric, its compression response would be the same as for the base fabric. But since the real response curves go below the base fabric curve, this means that CNFs give a higher resistance than the same mass of MFs. This is especially obvious for the 5 wt.% curve which would not noticeably approach the base curve even if a twice larger CNF density is used in the calculations. Probably this effect can be explained by different fibre re-arrangement mechanisms during the compression; while the normal MFs have smooth surfaces and thus are able to slide easily, the grafted fibres can be mechanically linked by CNFs and thus experience higher friction when sliding on the adjacent MFs.    Figure 3. Thickness for 3 cycles (left) and Vf for the 1st cycle (right) under compression, vs. pressure.    BENDING  A variation of the Pierce cantilever test is used to estimate the bending rigidity. A narrow (2.5-3.5 cm wide) stripe cut of the fabric is rigidly clamped at one of the ends and subjected to the action of its own weight. The weft yarns (=zero direction, they float over 4 warp yarns) are oriented along the stripe at its upper (convex) side. The curved geometry is captured by a camera equipped with a low-distortion lens. The picture is committed into a Matlab applet collecting coordinates of a number of points chosen manually along the curve. The curves are shown in Fig.4 visually revealing a prominent effect of grafting on the bending stiffness. TEXCOMP 10 Int. Conference, Lille, France, October 26-28 2010  185    Figure 4. Bent shapes for the base (left) and 6.5 wt.% grafted (right) fabrics.  Then the elastica numerical solution developed in [2] is employed, being subjected to the condition of minimal least squares of the differences with the test data, having a constant bending stiffness as the design variable. The calculated results are collected in Table 1 which shows that even a small CNF-grafting can significantly increase the bending stiffness. It is also seen that a 200 mm span length results in a reduced "average" bending stiffness, presumably indicating its nonlinearity in the areas of high curvature (near the clamp), while 100 mm and 150 mm spans give quite consistent results. Thus the present measurements should be considered as rather qualitative than quantitative for severely bent specimens (200, 250 mm spans).  TABLE I. BENDING STIFFNESS span length, mm 100 150 200 base fabric, D0, N·m2 32.5E-6 30.4E-6 16.1E-6 de-sized, Dd, N·m2 12.9E-6 12.0E-6 12.2E-6 grafted 6.5 wt.%, D6, N·m2 58.3E-6 52.4E-6 73.4E-6 grafted 39 wt.%, D39, N·m2 --- 7.8E-4 12.4E-4 ratio D6 / D0; D39 / D0 1.9; 1.7; 25.7 4.4; 75.1  Actually, the grafted fabric should be compared with the Ni-loaded one and not with the material just taken from a bobbin. This would show the full effect of the grown CNFs. Such a comparison is not performed in the present study because the yarns of the Ni-loaded fabric are very movable and do not allow to keep a good specimen geometry. However the Ni-loaded fabric is by touch yet more flexible, so the real stiffening effect of CNFs is yet more pronounced than that shown in Table 1.   CONCLUSIONS  Deformability of the tested carbon woven reinforcement is seriously affected by its grafting with CNFs, as shown by the following examples: • the fibre volume fraction, achievable by compaction under a 0.1 MPa pressure, decreases from 65% for the base fabric to 41% for CNF-grafted (6.5 wt.%) TEXCOMP 10 Int. Conference, Lille, France, October 26-28 2010  186  one. Such a poor compressibility can lower the achievable fibre volume fraction for economical vacuum-assisted light-RTM techniques or increase the pressure requirements in an autoclave processing. • the bending stiffness of a dry fabric is also deteriorated by the grafting, being increased by a factor of about 4 even for a 6.5 wt.% of CNFs. • the fabric-aluminium and fabric-fabric friction coefficient is also made worse by the grafting, being increased in the most of the cases; however, a lower friction is detected for several fabric-fabric orientations.    ACKNOWLEDGEMENTS  The work in the University of Twente is done within Transforce (’Transverse Reinforcement of Carbon Fibre Composites with Carbon Nano Fibres’) project primary funded by STW, The Netherlands. The work in K.U.Leuven was funded by GOA/10/004 project ’New model-based concepts for nano-engineered polymer composites’, funded by the Research Council of K.U.Leuven. Vitaly Koissin is very thankful to Mr. Bo Cornelissen (University of Twente) for his valuable comments on the bending tests. Mr. Gert Jan Nevenzel and Mr. Ruben Lubkemann (ibid) are gratefully acknowledged for their help.    REFERENCES  1. Koissin,V., Warnet,L., and Akkerman,R. “Experimental characterization of CFRP composites improved with nanofibres,” presented at the 14 th Int. Conference on Experimental Mechanics, Poitiers, France, July 5-8 2010. 2. Campanile,L.F. and Hasse,A. 2008. “A simple and effective solution of the elastica problem,” Journal of Mechanical Engineering Science , 222(C12):2513-2516. 

Deformability of a textile reinforcement modified with nanofibres

A simple and effective solution of the elastica problem,”

Experimental characterization of CFRP composites improved with nanofibres,” presented at

https://ris.utwente.nl/ws/files/5389283/texcomp10_koissin.pdf

Deformability of a textile reinforcement modified with nanofibres

Abstract