CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
Effects of microstructure change on corrosion resistance of dissimilar stainless steel joint by laser welding
Authors
夏原
姚星
李光
段红平
Publication date
1 January 2013
Publisher
Abstract
为了研究异种材料焊缝的耐腐蚀性能, 对316L与304不锈钢进行了激光焊接。通过组织观察和XRD技术检测了母材及焊缝微区的组织结构, 采用动电位极化的方法测试了316L和304奥氏体不锈钢及其激光对接焊缝的耐腐蚀性能, 并分析了焊缝耐腐蚀性提高的原因。结果表明, 在室温3.5%NaCl溶液中, 焊缝及母材的腐蚀均以点腐蚀为主, 且点蚀基本在晶界处萌生, 焊缝的耐腐蚀性相对母材有了明显的提高;激光焊缝组织的晶粒尺寸较母材明显细化, 相成分以奥氏体为主, 有明显的择优生长取向, 且奥氏体含量相对母材有所增加, 这种相结构特征的变化是焊缝耐腐蚀性提高的主要原因
Similar works
Full text
Available Versions
Institute Of Mechanics,Chinese Academy of Sciences
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:dspace.imech.ac.cn:311007/...
Last time updated on 12/02/2018