CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
锰含量对LiNi_(0.85-x)Co_(0.15)Mn_xO_2结构及形貌的影响
Authors
刘秀波
王翠玲
谷亦杰
黄小文
Publication date
15 August 2007
Publisher
Abstract
采用共沉淀法先合成出氢氧化物前驱体Ni0.85-xCo0.15Mnx(OH)2,其中X=0、0.1、0.2和0.4,前驱体与Li2CO3在空气气氛中固相烧结制得正极材料LiNi0.85-xCo0.15MnxO2。用XRD、SEM研究了锰含量对材料结构和形貌的影响。研究发现,LiNi0.85Co0.15O2的X射线衍射图中存在微量第二相,而锰掺杂有利于减小反应过程中锂离子损失和镍离子占据锂位,容易形成有序层状结构材料。随着Mn离子替代Ni离子量的增加,晶胞参数a减小,晶胞参数c、c/a及I003/I104值增大。SEM结果表明前驱体和最终产物形貌均随锰含量增加颗粒均匀性增强,粒子尺寸变小,粒径分布变窄
Similar works
Full text
Available Versions
Institute Of Mechanics,Chinese Academy of Sciences
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:dspace.imech.ac.cn:311007/...
Last time updated on 12/02/2018