CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
Effect of Rare Earth Element Cerium on Properties and Microstructure of Hot Dip Aluminum Coating on Q235 Steel
Authors
于升学
夏原
姚枚
Publication date
1 January 2006
Publisher
Abstract
研究了稀土铈对热浸镀铝层组织结构、耐蚀和耐热性能的影响。结果表明:稀土铈质量分数低于0.3%时,热浸镀铝层的耐蚀性能和高温抗氧化性能都得到提高,超过此含量镀层的性能下降。稀土铈使得过渡层由锯齿形结构转变为平滑结构,使镀层中FeAl3析出相在表层中呈网状分布,随其含量增加过渡层厚度减小。稀土含量超过0.3%时,稀土化合物在表层中呈条块状第二相析出并偏聚,并且随著稀土铈含量增加,表面层中稀土化合物呈块状,且偏聚程度加大
Similar works
Full text
Available Versions
Institute Of Mechanics,Chinese Academy of Sciences
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:dspace.imech.ac.cn:311007/...
Last time updated on 12/02/2018