We describe a method to form glass like thin film barrier in polydimethylsiloxane (PDMS) microcavities. The reactive fragments for the surface reaction were created from O2 and hexamethyldisiloxane (HMDS) in RF plasma environment. The reaction is based on migration of the reactive fragments into the microcavities by diffusion, to form a glass like thin film barrier to conceal the naked surface of PDMS. The barrier successfully blocked penetration of a fluorescent dye rhodamine B (RhB) into PDMS. The thickness of the barrier could be controlled by the time of reaction and the pressure inside the reaction chamber. There is a wide range of applications of such a technique in various fields, e.g. for coating the covered surfaces of microfluidic channels, tubes, capillaries, medical devices, catheters, as well as chip-integrated capillary electrophoresis and advanced electronic and opto-fluidic packaging

Basabe-Desmonts, Lourdes

Daniels, Stephen

Dimov, Ivan Krastev

Ducrée, Jens

Gandhiraman, Ram Prasad

Lee, Luke P.

Riaz, Asif

Ricco, Antonio J.

English

Name not available

THIN FILM DIFFUSION BARRIER FORMATION IN PDMS MICROCAVITIES  Asif Riaz1,2, Ram P. Gandhiraman1, Ivan K. Dimov1, Lourdes Basabe-Desmonts1, Antonio J. Ricco1,  Jens Ducrée1, Stephen Daniels1, and Luke P. Lee1,2 1Biomedical Diagnostics Institute, National Centre for Sensor Research,  Dublin City University, Glasnevin, Dublin, IRELAND 2 Biomolecular Nanotechnology Center, Berkeley Sensor and Actuator Center,  Department of Bioengineering, University of California, Berkeley, CA, USA  ABSTRACT We describe a method to form glass like thin film barrier in polydimethylsiloxane (PDMS) microcavities.  The reactive fragments for the surface reaction were created from O2 and hexamethyldisiloxane (HMDS) in RF plasma environment.  The reaction is based on migration of the reactive fragments into the microcavities by diffusion, to form a glass like thin film barrier to conceal the naked surface of PDMS.  The barrier successfully blocked penetration of a fluorescent dye rhodamine B (RhB) into PDMS.  The thickness of the barrier could be controlled by the time of reaction and the pressure inside the reaction chamber. There is a wide range of applications of such a technique in various fields, e.g. for coating the covered surfaces of microfluidic channels, tubes, capillaries, medical devices, catheters, as well as chip-integrated capillary electrophoresis and advanced electronic and opto-fluidic packaging.  KEYWORDS Polydimethylsiloxane, diffusion barrier, microfluidics, plasma enhanced vapor deposition, hexamethyldisiloxane  INTRODUCTION Materials like glass, silicon, and plastics have been used for the fabrication of microfluidic devices. In particular, the elastomeric material PDMS has been a popular for the fabrication of microfluidic devices [1, 2] because of its numerous advantages such as, its amenability for rapid prototyping, its inertness, biocompatibility, optical transparency, and (gas) permeability.  However, PDMS provides a hydrophobic surface which promotes nonspecific adsorption or even absorption of small molecules into the bulk mass. Thus, the surface chemistry of the microfluidic channels in PDMS remains a major issue, and it is desirable to create hydrophilic surface of the channels to conceal hydrophobic nature of the surface for a range of applications in chemical and biological analyses [3, 4].  Usually, PDMS channels are made hydrophilic by exposing them to UV ozone or oxygen plasma for a short time before assembling the devices. But such a treatment is temporary and the hydrophobic character returns in less than an hour [5, 6]. For this purpose, various wet chemical strategies have been reported such as graft polymerization, silanization, adsorption of detergents, proteins, poly-electrolytes [3, 7-9], and sol-gel based coating [10, 11]. However, these techniques are tedious, require skilful handling and, moreover, multiplexing of such methods on a large scale may perhaps induce complications in the process parameters. Gas phase chemical reactions to modify the surfaces in microfluidic devices are relatively unexplored. Chemical vapor deposition is a useful technique which provides reactive chemicals in the gas phase for surface reaction. Various strategies have been reported for functionalized and non-functionalized surface polymerization in microfluidic devices [12-14].  In this paper, we describe a novel method of creating a glass-like thin film barrier in deep PDMS microcavities/channels. The method is based on gas phase fragmentation of O2 and HMDS in RF plasma environ-ment. The reactive fragments created in the plasma migrate into the cavities and react to form a glassy thin-film barrier, presumably composed of oxides of silicon. This barrier created in this way shows excellent blocking to the penetration of small molecules like rhodamine B.   RESULTS AND DISCUSSION Soft photolithography was used to create microfluidic features in PDMS substrate which was bonded to glass surfaces to form the microcavities.  The SiOx barrier formation reaction was performed in a plasma chamber. The microcavities bearing devices were placed in the plasma environment of a computer controlled PECVD reactor Europlasma, model CD300. Then O2 and HMDS gases were released into the plasma in a desired volume ratio.  The impact of energetic electrons and ions on O2 and HMDS molecules in the plasma resulted into fragmentation and a stable source of the reactants such as ions, radicals and elemental species.  Reactive species produced in the gas phase diffuse into the channels and react with the walls, resulting in the formation of a thin film that acts as a barrier between the wall that forms the fluidic channels and the contents flowing through them. The formation of thin-film SiOx on the channel wall reduced the contact angle from 120º to 60º. We characterized this coating layer by studying the penetration of RhB into PDMS, as shown in Figure 1. An aqueous solution of RhB was stored in a bare and a SiOx 978-1-4244-4193-8/09/$25.00 ©2009 IEEE Transducers 2009, Denver, CO, USA, June 21-25, 20091051T3P.043Authorized licensed use limited to: DUBLIN CITY UNIVERSITY. Downloaded on July 12,2010 at 11:39:39 UTC from IEEE Xplore.  Restrictions apply. barriered channel. Fluorescent images showed that RhB molecules penetrated into the bare PDMS (Fig.1a), resulting into a successive increment in the fluorescent region with time. However, in the treated channels, the fluorescence of RhB molecules remained confined to the channel region due to SiOx barrier (Fig. 1b). Fragmentation of O2 and HMDS in plasma provides various ionic, neutral radicals, and elemental species.  We could observe the presence of Si radicals and elemental oxygen through their characteristic emission lines near 519 nm, 777 nm, and 884 nm, respectively, as also reported by others [15]. Since the microcavities are in a strong dielectric medium, we suggest that the radicals or elemental species of Si and O are more likely to migrate by diffusion into the cavities rather than the ionic species.   For fixed conditions as given in Fig. 1, the efficiency of the barrier to block RhB penetration into PDMS drastically improved with increasing cross sectional area of the inlet of the cavity (Fig. 2). Efficient barriers in wider microcavities could be attributed to the fact that the net flux ‘Jnet’ of the particles diffusing into the cavities increases with increasing the cross section ‘A’ as given in relation (1) [16], dxdnDAJnet −≈   (1) where ‘D’ is the diffusion coefficient, and ‘n’ the density of the particles.    Figure 2. Fluorescence of RhB vs. time, in SiOx-coated channels of various dimensions (a). Effect of cross-sectional area of channels on efficiency of the thin film formation (b). Solid line shows the exponential fitting of the data points (y = yo + A1e(-x/t1)), yo = 0.8186, A1 = 702.5, and t1= 0.4694, R2= 0.987). Schematic illustration of thin film formation with cross section of the channels. Reaction conditions as in Figure 1.  Diffusive migration of reactive molecules during the PECVD process was evident from the fact that the long and meandering channels could be coated with SiOx. In Figure 3, an image taken at ~ 2.3 cm beyond a 357º (180º + 177º) turn shows blocking of RhB diffusion (Figure 3d). A qualitative 2D simulation of concentration profiles along the cavity wall is also shown in Fig. 3f, which shows a similar trend as for the experimentally determined thickness profiles of the barrier along the length of the cavity (Fig. 4).     (f)   Figure 3. (a) A long meandering microfluidic channel (50 μm x 30 μm x 20 cm), exposed to reaction conditions as given in Figure 1, for 120 min. (b & c) Schematic representation of thin-film deposition. (d) Region of channel showing a good barrier to RhB penetration. (e)  Region of channel showing poor barrier to RhB penetration. (f) Qualitative gas diffusion concentration profile (COMSOL simulation) through microfluidic channel when both sides are reactive.   The thickness of the barrier was physically measured by using a surface profilometer. A piece of PDMS bearing micro-grooves was reversibly bonded on a Si wafer to form the microcavities and the reaction was performed. After formation of the barrier the PDMS was removed and  Figure 1. Formation of thin-film SiOx barrier on the walls of PDMS channel and characterization by Rhodamine B diffusion. (a) Native PDMS, (b) PDMS channel with SiOx barrier. Scale bar: 50 μm. The channel was filled and stored with RhB solution (10 μM) and after 3 hours it was microscopically examined. Conditions: RF 300 W, O2: HMDS 500 : 16 sccm, 270 mTorr, 40 min, 50 ºC. 1052Authorized licensed use limited to: DUBLIN CITY UNIVERSITY. Downloaded on July 12,2010 at 11:39:39 UTC from IEEE Xplore.  Restrictions apply. Si wafer was used for measuring the thickness of the barrier. Experimental results in Figure 4 show a trend towards increasing film thickness with increasing time of the reaction and pressure. The pressure was varied in the reaction while the flow ratio of O2 and HMDS gases was fixed (31.3 : 1). These results reveal that increasing the time of the reaction and pressure provides more reactant species to be deposited, hence forming a thicker barrier.   Figure 4. Effect of reaction time (a), and the concentration of HMDS (b), on the thickness and coating distance of SiOx thin film. In this experiment, PDMS-coated channels (50 μm x 100 μm x 10 cm) were bonded to a Si wafer instead of a glass substrate, and after thin film deposition the device was disassembled. The Si wafer was used to measure the thickness of SiOx film mechanically using a profilometer.     The SiOx could be created quite reproducibly.  Reproducibility of the barrier formation was studied in a multiplex of a longer (~ 20 cm) meandering cavities of 40 individual units (Figure 5). This multiplex platform was subjected to the barrier formation and efficiency of the barrier was studied using RhB penetration into PDMS.  The distances coated with the barrier in the cavities could be clearly discerned from the fluorescence of RhB, which is indicated by arrows.  The SiOx coated distances in the multiplex channels were highly reproducible (60 mm ± 5, n = 10). The significance of HMDS in the formation of the SiOx barrier could be established as shown in Fig. 6, when the reactions were performed in the absence and presence of HMDS supply to the reaction chamber. The efficiency of the barrier was examined by storing a solution of RhB in the channels. The channels which were treated in the absence of HMDS showed penetration of RhB into PDMS. However, the channels treated in the presence of HMDS showed an efficient protection to RhB molecules from penetrating into the PDMS.      Figure 6. (a) Penetration of RhB through O2 plasma and O2 plasma + HMDS-treated PDMS channels. Other conditions as in Figure 1.   CONCLUSIONS We report a novel method of thin film formation in deep microcavities/channels using a plasma-enhanced chemical vapor deposition (PECVD) technique. The field of gas-phase reaction is relatively unexplored for surface modification within assembled microfluidic devices. We have demonstrated for the first time a gas-phase chemical process for creating a glass-like surface in assembled PDMS microfluidic channels. Our aim is to further investigate such thin-films in assembled microfluidic devices for surface bio-functionalization and capillary electrophoresis applications. Reactive species produced in the gas phase diffuse into the channels and react with the walls, resulting in the formation of a thin film that can act as a barrier between the materials that form the walls of the fluidic channels in touch with the liquids. Successful deposition of thin-film oxides of silicon (SiOx) deep into microchannels is attributed to the diffusion of reactant molecules into the channels. Since thin film formation is attributed to molecular diffusion, this method allows coating of long, meandering channels as well as straight channels. The extent of thin film formation along the channels and its thickness are controlled by the time of reaction and concentration of the reactant precursor hexamethyl-disiloxane (HMDS). We show that thin-film SiOx formation in microfluidic channels cast in polydimethyl-siloxane (PDMS) effectively blocks the penetration of Figure 5. Thin film formation in a multiplexed platform of 40 individual channels (1/4 shown). White arrows show the SiOx coated distance of the thin film barrier. (b) Close view of approaching penetration of the thin film barrier. (c) Schematic illustration of transition to RhB diffusion zones in the channels from both sides of the channel. Reaction time 120 min, other conditions as in Figure 1. 1053Authorized licensed use limited to: DUBLIN CITY UNIVERSITY. Downloaded on July 12,2010 at 11:39:39 UTC from IEEE Xplore.  Restrictions apply. rhodamine B (RhB) from aqueous solution within the channels into the PDMS that comprises the channel walls. This method of formation of thin film SiOx in micro-cavities is simple and robust, and up-scaling may be more straightforward than for conventional wet chemical methods. ACKNOWLEDGEMENTS This work was supported by the Science Foundation Ireland under Grant No. 05/CE3/B754.  CONTACT *Luke P. Lee Tel: +1510 642 5855; lplee@berkeley.edu  REFERENCES [1] McDonald, J. C., Whitesides, G. M., Poly(dimethylsiloxane) as a material for fabricating microfluidic devices. Acc. Chem. Res., vol. 35, pp.  491-499. 2002 [2] Whitesides, G. M., The origins and the future of microfluidics. Nature, vol. 442, pp.  368-373. 2006 [3] Makamba, H., Kim, J. H., Lim, K., Park, N., Hahn, J. H., Surface modification of poly(dimethylsiloxane) microchannels. Electrophoresis, vol. 24, pp.  3607-3619. 2003 [4] Wu, L. Y., Di Carlo, D., Lee, L. P., Microfluidic self-assembly of tumor spheroids for anticancer drug discovery. Biomed. Microdevices, vol. 10, pp.  197-202. 2008 [5] Berdichevsky, Y., Khandurina, J., Guttman, A., Lo, Y. H., UV/ozone modification of poly(dimethylsiloxane) microfluidic channels. Sens. Actuators, B, vol. 97, pp.  402-408. 2004 [6] Bhattacharya, S., Datta, A., Berg, J. M., Gangopadhyay, S., Studies on surface wettability of poly(dimethyl) siloxane (PDMS) and glass under oxygen-plasma treatment and correlation with bond strength. J. Microelectromech. Syst., vol. 14, pp.  590-597. 2005 [7] Heyries, K. A., Blum, L. J., Marquette, C. A., Direct poly(dimethylsiloxane) surface functionalization with vinyl modified DNA. Chem. Mater., vol. 20, pp.  1251-1253. 2008 [8] Hu, S. W., Ren, X. Q., Bachman, M., Sims, C. E., et al., Tailoring the surface properties of poly(dimethylsiloxane) microfluidic devices. Langmuir, vol. 20, pp.  5569-5574. 2004 [9] Orhan, J. B., Parashar, V. K., Flueckiger, J., Gijs, M. A. M., Internal modification of poly(dimethylsiloxane) microchannels with a borosilicate glass coating. Langmuir, vol. 24, pp.  9154-9161. 2008 [10] Abate, A. R., Lee, D., Do, T., Holtze, C., Weitz, D. A., Glass coating for PDMS microfluidic channels by sol-gel methods. Lab Chip, vol. 8, pp.  516-518. 2008 [11] Roman, G. T., Culbertson, C. T., Surface engineering of poly(dimethylsiloxane) microfluidic devices using transition metal sol-gel chemistry. Langmuir, vol. 22, pp.  4445-4451. 2006 [12] Chen, H. Y., Elkasabi, Y., Lahann, J., Surface modification of confined microgeometries via vapor-deposited polymer coatings. J. Am. Chem. Soc., vol. 128, pp.  374-380. 2006 [13] Lahann, J., Vapor-based polymer coatings for potential biomedical applications. Polym. Int., vol. 55, pp.  1361-1370. 2006 [14] Martin, I. T., Dressen, B., Boggs, M., Liu, Y., et al., Plasma modification of PDMS microfluidic devices for control of electroosmotic flow. Plasma Processes Polym. , vol. 4, pp.  414-424. 2007 [15] Goujon, M., Belmonte, I., Henrion, G., OES and FTIR diagnostics of HMDSO/O-2 gas mixtures for SiOx deposition assisted by RF plasma. Surf. Coat. Technol., vol. 188, pp.  756-761. 2004 [16] Pendlebury, J. M., Kinetic Theory, Adam Hilger, S. Ed., Brewer, D. F., Bristol, 1985.   1054Authorized licensed use limited to: DUBLIN CITY UNIVERSITY. Downloaded on July 12,2010 at 11:39:39 UTC from IEEE Xplore.  Restrictions apply. 

Thin film diffusion barrier formation in PDMS microcavities

Asif Riaz

Ram P. Gandhiraman

Ivan K. Dimov

Lourdes Basabe-Desmonts

Antonio J. Ricco

Jens Ducree

Stephen Daniels

Luke P. Lee

Crossref

DCU Online Research Access Service

Authorized licensed use limited to:

Direct poly(dimethylsiloxane) surface functionalization with vinyl modified DNA.

Glass coating for PDMS microfluidic channels by sol-gel methods.

Internal modification of poly(dimethylsiloxane) microchannels with a borosilicate glass coating.

Microfluidic self-assembly of tumor spheroids for anticancer drug discovery.

OES and FTIR diagnostics of HMDSO/O-2 gas mixtures for SiOx deposition assisted by RF plasma.

Plasma modification of PDMS microfluidic devices for control of electroosmotic flow.

Poly(dimethylsiloxane) as a material for fabricating microfluidic devices.

Studies on surface wettability of poly(dimethyl) siloxane (PDMS) and glass under oxygenplasma treatment and correlation with bond strength.

Surface engineering of poly(dimethylsiloxane) microfluidic devices using transition metal sol-gel chemistry.

Surface modification of confined microgeometries via vapordeposited polymer coatings.

Surface modification of poly(dimethylsiloxane) microchannels.

Tailoring the surface properties of poly(dimethylsiloxane) microfluidic devices.

The origins and the future of microfluidics.

UV/ozone modification of poly(dimethylsiloxane) microfluidic channels.

Vapor-based polymer coatings for potential biomedical applications.

Irish Universities

Thin film diffusion barrier formation in PDMS microcavities

Abstract

Similar works

Full text

Available Versions

Name not available

Crossref

DCU Online Research Access Service

Irish Universities