The purpose of this research is to investigate the characteristics of import Ball Mill which is used at cement mills in Indonesia. There were two kind of import Ball Mill from PT. Semen Gresik, Tbk that used in this research which are A type (Ø 30 mm) and B type (Ø 40 mm). Visual investigation, chemistry composition, distribution of hardness, and microstructure photograph was conducted characterize these ball mill. Visually, the import Ball Mill has rough surface, white coloring when cut off, and small cracks at all specimens. Type A ball mill contains of 2,934% C, 11,231% Cr, and 0,177% Mo, where type B Ball Mill contains of 2,693% C, 12,31% Cr, and 1,103% Mo. Both are martensitic white cast iron ASTM A532 Class II type A. The surface are harder then the its core. The highest hardness on the surface are 720,82 kg/mm2 (type A) and 746,5 kg/mm2 (type B), where as lowest hardness on the core are 631,1 kg/mm2 (type A) and 544,0 kg/mm2 (type B). Microstructure investigation shows Perlit, Cementit, and Martensit