Impact tests were conducted on uncoated 2D and 2.5D MI SiC/SiC composite specimens at room temperature and 1316 C in air. The specimens were analyzed before and after impact using optical microscopy, pulsed thermography (PT) and computed tomography (CT). Preliminary results indicate the following. Both 2-D and 2.5D composites show increase in surface and volumetric damages with increasing impact velocity. However, 2-D composites are prone to delamination cracks. In both 2D and 2.5D composites, the magnitude of impact damage at a fixed impact velocity is slightly greater at room temperature than at 1315 C. At a fixed projectile velocity and test temperature, the depth of penetration of the projectile into the substrate is significantly lower in 2.5D composites than in 2D composites. Fiber architecture plays a significant role controlling impact damage in MI SiC/SiC composites