Fabrication of composite structures using vacuum assisted resin transfer molding (VARTM) is generally more affordable than conventional autoclave techniques. Recent efforts have focused on adapting VARTM for the fabrication of high temperature composites. Due to their low melt viscosity and long melt stability, certain phenylethynyl terminated imides (PETI) can be processed into composites using high temperature VARTM (HT-VARTM). However, one of the disadvantages of the current HT-VARTM resin systems has been the high porosity of the resultant composites. For aerospace applications, a void fraction of <2% is desired. In the current study, two PETI resins, LARC. PETI-330 and LARC. PETI-8 have been used to fabricate test specimens using HT-VARTM. The resins were infused into carbon fiber preforms at 260 C and cured between 316 and 371 C. Photomicrographs of the panels were taken and void contents were determined by acid digestion. Modifications to the thermal cycle used in the laminate fabrication have reduced the void content significantly; typically .3% for carbon fiber biaxially woven fabric and less than 2% for carbon fiber uniaxial fabric. Mechanical properties (short beam shear and flexure) of the panels were determined at both room and elevated temperatures. The results of this work are presented herein. This paper is declared a work of the U.S. Government and is not subject to copyright protection in the United States