Dewetting and Segregation of Zn-Doped InSb in Microgravity Experiments

Abstract

In directional solidification, dewetting is characterized by the lack of contact between the crystal and the crucible walls, due to the existence of a liquid meniscus at the level of the solid-liquid interface. This creates a gap of a few tens of micrometers between the crystal and the crucible. One of the immediate consequences of this phenomenon is the dramatic improvement of the quality of the crystal. This improvement is partly due to the modification of the solid-liquid interface curvature and partly to the absence of sticking and spurious nucleation at the crystal-crucible interface. Dewetting has been, commonly observed during the growth of semiconductors in crucibles under microgravity conditions where it appears to be very stable: the gap between the crystal and the crucible remains constant along several centimetres of growth. The physical models of the phenomenon are well established and they predict that dewetting should not occur in microgravity, if sufficient static pressure is imposed on the melt, pushing it towards the crucible. We present the results of InSb(Zn) solidification experiments conducted at the International Space Station (ISS) where, in spite of a spring exerting a pressure on the liquid, partial dewetting did occur. This surprising result is discussed in terms of force exerted .by the spring on the liquid and of possibility that the spring did not work properly. Furthermore, it appears that the segregation of the Zn was not affected by the occurrence of the dewetting. The data suggest that there was no significant interference of convection with segregation of Zn in InSb

    Similar works