The stress and temperature sensitivites of the rupture life and secondary creep rate were examined in detail for a single heat of type 304 stainless steel (9T2796). Assuming that the rupture life has a power law stress dependency, relatively small differences in the stress exponent were observed over a broad range of stress and temperature. In contrast, large changes were observed for equivalent parameter for secondary creep rate. As a result of these differences, the Monkman-Grant correlation was sensitive to stress and temperature below 650 C. Metallurgical studies based on light and transmission electron microscopy suggested that the temperature and stress sensitivities of secondary creep rate at temperatures below 650 C were related to features of the substructure not present at higher temperature. Specifically, the presence of a fine dislocation network stabilized by precipitates altered the stress and temperature sensitivities relative to what might be expected from high temperature studies