Inner diameter (ID) wafering of ingot rotation reduce the ID saw blade diameter was investigated. The blade thickness can be reduced, resulting in minimal kerf loss. However, significant breakage of wafers occurs during the rotation wafering as the wafer thickness decreases. Fracture mechanics was used to develop an equation relating wafer thickness, diameter and fracture behavior at the point of fracture by using a model of a wafer, supported by a center column and subjected to a cantilever force. It is indicated that the minimum allowable wafer thickness does not increase appreciably with increasing wafer diameter and that fracture through the thickness rather than through the center supporting column limits the minimum allowable wafer thickness. It is suggested that the minimum allowable wafer thickness can be reduced by using a vacuum chuck on the wafer surface to enhance cleavage fracture of the center core and by using 111 ingots