A predetermine amount of segregation is introduced into a molten sample of a composite that exhibits the Soret effect, such amount approximating the amount of segregation resulting from directional solidification of the sample. The molten sample is then directionally solidified starting at the end opposite the end richer in the constituent that would migrate toward the cooler part of a liquid solution of the composite maintained in a temperature gradient. Since solidification commences at the end deficient in such constituent, its migration toward the interface between the solid and liquid during the solidification will compensate for the deficiency, yielding a more homogeneous product