CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
溶胶-凝胶法制备光波导薄膜及性质的研究
Authors
姜永睿
杨沁清
+5 more
杨澜
王红杰
胡雄伟
谢二庆
郑金红
Publication date
1 January 2004
Publisher
Abstract
采用有机改性硅酸盐制备了光敏性溶胶-凝胶,并在凝胶中加入四丙氧基锆作为调节折射率的材料;用该凝胶在硅片上提拉成膜.为了增加薄膜与硅片的粘附性,成膜前先用干氧热氧化法在硅片上生长了一层厚度约为1500的二氧化硅;样品的原子力相片表明薄膜的表面非常平整,在5×5 μm2的范围内最大表面起伏只有0.657 nm.利用波导阵列掩膜版, 对制备的薄膜在紫外光波段下曝光,得到了表面平坦、侧墙光滑、陡直的沟道波导阵列.研究发现:紫外曝光时间和坚膜时的后烘温度都会使薄膜的折射率增大.通过对样品红外吸收谱的分析,从微观机理上解释了折射率随工艺条件变化的原因
Similar works
Full text
Available Versions
Knowledge Repository of SEMI,CAS
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:ir.semi.ac.cn:172111/17413
Last time updated on 15/03/2019