CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
HF/CrO_3溶液对AlGaAs的选择性湿法刻蚀应用于楔型结构的制备
Authors
任晓敏
罗丽萍
+4 more
马骁宇
高俊华
黄永清
黄辉
Publication date
1 January 2002
Publisher
Abstract
利用动态掩膜腐蚀技术,研究了HF/CrO_3腐蚀液对各种不同组分的Al_xGa_(1-x)As (x = 0.3, 0.5, 0.65)的腐蚀速率及腐蚀表面形貌。随着HF(48wt%)/CrO_3(33wt%)的体积比由0.01变化到0.138,相应的腐蚀液对Al_(0.8)Ga_(0.2)As/Al_(0.3)Ga_(0.7)As的选择性由179降到8.6;通过调节腐蚀液的选择性,在Al_(0.3)Ga_(0.7)As外延层上制备出了倾角从0.32°到6.61°的各种斜面。当HF(48wt%)/CrO_3(33wt%)的体积比为0.028时,Al组分分别为0.3、0.5和0.65时,相应的腐蚀表面的均方根粗糙度为1.8、9.1和19.3nm。另外,还分析了腐蚀机理与腐蚀表面形貌之间的关系
Similar works
Full text
Available Versions
Knowledge Repository of SEMI,CAS
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:ir.semi.ac.cn:172111/18103
Last time updated on 15/03/2019