CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
化学气相传输法生长ZnO单晶
Authors
李晋闽
段满龙
+3 more
董志远
赵有文
魏学成
Publication date
1 January 2006
Publisher
Abstract
利用化学气相传输法生长了ZnO单晶.通过控制源区和生长端的温度梯度,使用碳辅助增强质量传尊挚应,在无籽晶自发成核的条件下,得到了晶粒尺寸达5mm×8mm的ZnO晶体.利用长有GaN层的蓝宝石号片待为籽晶,得到了直径32mm、厚4mm左右的ZnO单晶体.用光致发光谱和X射线双晶衍射研究了ZnO晶体的性质并对生长的热力学过程和现象进行了分析
Similar works
Full text
Available Versions
Knowledge Repository of SEMI,CAS
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:ir.semi.ac.cn:172111/16727
Last time updated on 15/03/2019