CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
research
Critical moisture conditions for fungal decay of modified wood by basidiomycetes as detected by pile tests
Authors
Christian Brischke
Pia Larsson-Brelid
Linda Meyer
Andreas Treu
Publication date
1 January 2016
Publisher
Berlin : De Gruyter
Doi
Cite
Abstract
The aim of cell wall modification is to keep wood moisture content (MC) below favorable conditions for decay organisms. However, thermally modified, furfurylated, and acetylated woods partly show higher MCs than untreated wood in outdoor exposure. The open question is to which extent decay is influenced by the presence of liquid water in cell lumens. The present paper contributes to this topic and reports on physiological threshold values for wood decay fungi with respect to modified wood. In total, 4200 specimens made from acetylated, furfurylated, and thermally modified beech wood (Fagus sylvatica L.) and Scots pine sapwood (sW) (Pinus sylvestris L.) were exposed to Coniophora puteana and Trametes versicolor. Piles consisting of 50 small specimens were incubated above malt agar in Erlenmeyer flasks for 16 weeks. In general, pile upward mass loss (ML) and MC decreased. Threshold values for fungal growth and decay (ML≥2%) were determined. In summary, the minimum MC for fungal decay was slightly below fiber saturation point of the majority of the untreated and differently modified materials. Surprisingly, T. versicolor was able to degrade untreated beech wood at a minimum of 15% MC, and growth was possible at 13% MC. By contrast, untreated pine sW was not decayed by C. puteana at less than 29% MC. © 2016 by De Gruyter 2016
Similar works
Full text
Open in the Core reader
Download PDF
Available Versions
Institutionelles Repositorium der Leibniz Universität Hannover
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:www.repo.uni-hannover.de:1...
Last time updated on 02/05/2018