In this work, powders of Cu and Al were milled with a proportion equal to 24 atomic % Al, using low and medium energy mills. The initial, intermediate and final stages of the resulting powder are analyzed using scanning electron microscopy, X-ray diffraction and different transmission electron microscopy techniques. The structure and microstructure achieved in each step of the milling process are compared to the results of Cu-16at.%Al and Cu-30at.%Al obtained under the same conditions of reactive milling. At the final stage of milling, it was detected that the obtained intermetallic is not the equilibrium phase of the Cu-Al system.Fil: Giordana, María Florencia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Centro Atómico Bariloche; ArgentinaFil: Muñoz Vásquez, Natalia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; ArgentinaFil: Garro González, M.. Universidad de Costa Rica; Costa RicaFil: Esquivel, Marcelo Ricardo Oscar. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Centro Atómico Bariloche; Argentina. Universidad Nacional del Comahue. Centro Regional Universitario Bariloche; ArgentinaFil: Zelaya, Maria Eugenia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Centro Atómico Bariloche; Argentin