The purpose of this work is the characterization of a master alloy of metal glass based on iron Fe48Cr15Mo14C15B6Y2. Two types of alloys studied B1 which has been prepared by the use of pure element and the other B2 which has been prepared by the use of raw materials. The thermal and structural properties of the samples are   measured by a combination of high temperature differential scanning calorimeter (HTDSC), X-ray diffraction and scanning electron microscopy (SEM). Chemical compositions are checked by energy dispersive spectroscopy analysis.Fil: Bendjemil, Badis.  University of Badji -Mokhtar; Argelia. Faculty of Sciences and Technology; ArgeliaFil: Seghairi, Nassima. Faculty of Sciences and Technology; ArgeliaFil: Lavorato, Gabriel Carlos. Dipa rtimento di Chimica Universita' di Torino; Italia. Comisión Nacional de Energía Atómica. Gerencia del Área Investigaciones y Aplicaciones no Nucleares; ArgentinaFil: Castellero, Alberto. Dipa rtimento di Chimica Universita' di Torino; ItaliaFil: Bougdira, Jamal. Université de Nancy, Faculté des Sciences et. Techniques; FranciaFil: Vinai, Franco. Instituto Nazionale di Ricerca Metrologica; ItaliaFil: Baricco, Marcello. Dipa rtimento di Chimica Universita' di Torino; Itali

Baricco, Marcello

Bendjemil, Badis

Bougdira, Jamal

Castellero, Alberto

Lavorato, Gabriel Carlos

Seghairi, Nassima

Vinai, Franco

Chemical and Materials Engineering

English

Institutional Research Information System University of Turin

Chemical and Materials Engineering 2(7): 155-159, 2014 http://www.hrpub.org DOI: 10.13189/cme.2014.020702 Preparation and Characterization of Master Alloys Fe48Cr15Mo14C15B6Y2 Metallic Glasses Badis Bendjemil1,2,*, Nassima Seghairi2, Gabriel Lavorato3, Alberto Castellero3, Jamal Bougdira5,   Franco Vinai4, Marcello Baricco3 1LASEA, Department of Chemistry, University of Badji-Mokhtar, 23000 Annaba, Algeria 2 Department of Mechanical engineering, Faculty of Sciences and Technology, University of 08 mai 1945 Guelma, 24000 Guelma, Algeria 3Dipartimento di Chimica Universita' di Torino Via P. Giuria 9, I-10125 Torino, Italy 4Instituto Nazionale di Ricerca Metrologica Strada delle Cacce 91 I-10135 Torino, Italy 5Institut Jean Lamour, Département CP2S, UMR 7198 CNRS–Université de Nancy, Faculté des Sciences et. Techniques, Boulevard des aiguillettes, B.P. 70239 - 54506 Vandoeuvre-lès-Nancy, France *Corresponding Author: Badis23@ymail.com Copyright © 2014 Horizon Research Publishing All rights reserved. Abstract  The purpose of this work is the characterization of a master alloy of metal glass based on iron Fe48Cr15Mo14C15B6Y2. Two types of alloys studied B1 which has been prepared by the use of pure element and the other B2 which has been prepared by the use of raw materials. The thermal and structural properties of the samples are measured by a combination of high temperature differential scanning calorimeter (HTDSC), X-ray diffraction and scanning electron microscopy (SEM). Chemical compositions are checked by energy dispersive spectroscopy analysis.  Keywords  Master Alloy, High Temperature Differential Scanning Calorimeter, Structural Characterization, X-Ray Diffraction, Scanning Electron Microscopy, Energy Dispersive Spectroscopy Analysis, Fe-Based Metallic Glasses  1. Introduction The metallic glasses are amorphous alloys obtained by quenching from the liquid phase [1] that have been discovered in 1960 [2]. Most of the alloys can be produced in the form of ribbons of thickness approximately 0.03mm by quenching on a wheel. In the last 20 years have been discovered of alloys that can be produced in massive form, i.e. in the form of bars with a minimum diameter of 1 mm [3-5]. The amorphous alloys can also be obtained by other techniques such as: the grinding [6], the rolling [7], the thin film deposition [8], or the electrochemical deposition [9]. Our study is therefore committed to investigate the thermal properties and the structural characteristics of the two molten alloys for Fe-based metallic glasses whose purpose the possibility to obtain industrial a ribbon and bulk metallic glass form by using the raw materials. The work in this area and on the composition Fe48Cr15Mo14C15B6Y2b shows the possibility of obtaining metallic glasses in the form ribbons and bulk with the use of pure elements [10-11]. 2. Experimental All the elements of the sample master alloy of a metallic glass Fe48Cr15Mo14C15B6Y2 were selected with a high purity, 99.8% (alloy B1). The metals in the form massive are cleaned of any trace of oxide visible to the eye by abrasion of the surface. The compositions are obtained by taking the appropriate quantities in stoichiometric proportions. The metal pieces are then washed in alcohol to 95° in an ultrasonic bath for one to two minutes and then weighed to new. Finally, they are placed in the enclosure of the arc furnace (Bühler) in a controlled atmosphere, free of oxygen. This step of preparation is done as quickly as possible, to avoid to the maximum the re-oxidation of metals. The sample obtained by this process is called sample "molten alloy". In the framework of the possibility of industrial manufacture of metallic glasses from the raw materials, it has prepared a sample molten alloy of a metallic glass (B2) with the same composition. We used a steel AISI430 (55.7 wt %) and the commercial alloy FeB (7.3 wt %) and added the elements pure Mo (25.7 wt % ), Cr (5.4 wt % ), C(3.4 wt %) and Y(3.4 wt % ). The sample "molten alloy" is generally crystal clear sound, it is then necessary to the recast in order to soak the glass to get a metal. The crystalline state has been verified by pairing x-ray diffraction, thermal analysis and scanning electron microscopy. The diffraction was carried out on apparatus of Philips brand type PW1830 (Co-Kα, λ=1.7897 Å). The microstructure has been examined by scanning electron microscopy (SEM) of type Leica stereoscan 4200 and the chemical composition of the alloy has been verified by the dispersion spectroscopy in energy of the x-ray (EDS). The thermal analysis was detected the 156 Preparation and Characterization of Master Alloys Fe48Cr15Mo14C15B6Y2 Metallic Glasses   thermal effects related to the transformations by high temperatures differential scanning calorimeter (HTDSC) of speed of rise in temperature 0.17K/s. It has used the means of the laboratory of Department of Chemistry at the University of Torino, Italy 3. Results and Discussion Figure 1 shows XRD patterns of the molten alloy B1. The XRD patterns  presents several peaks of diffractions corresponding to the following phases crystalline, indicating that this sample is not amorphous but is fully crystalline: solid solution α- (Fe, Mo, Cr), (Cr, Fe)23C6 , Mo and Fe carbides.  Figure1.  XRD of sample B1 The microstructure of the sample of the molten alloy B1 has been observed by SEM (fig. 2). The quantitative determination of the composition of each local crystalline phase is done from a spectrum EDS. Figure 3 shows the EDS spectrum of the crystalline phase of the black point. We found that this phase is an yttrium oxide that is not visible by XRD because the quantity is very small. The second finding of the analysis of the EDS spectrum (fig. 5) which corresponds to the crystalline phase in dark gray (fig. 4), and shows the phase of the chrome and iron carbide whose chemical composition is the following (Cr, Fe) 23 C6.  Figure 2.  Image of SEM for B1  Figure3.  EDS spectrum of the black phase  Figure 4.  Image of SEM for B1  Figure5.  EDS Spectrum phase of the dark gray  Figure 6.  Image of SEM for B1  Figure 7.  EDS Spectrum phase of the dark gray  30 40 50 60 70 80 90 100 110 120 130   Carbure Mo+Fe  Carbure (Cr,Fe)23C6 (MoCr)+Feintensity2θ Chemical and Materials Engineering 2(7): 155-159, 2014 157  We present in figure 6 the image SEM from same sample with their spectral analysis EDS (fig. 7) of the crystalline phase in average gay, the interpretation of this result indicates that this phase is the solid solution α  (Fe, Mo, Cr). The spectrum analysis of the crystalline phase in light gray (fig. 9) that corresponds to the image of SEM (fig. 8), shows that this phase is molybdenum and iron carbide whose chemical composition is Fe3 Mo3 C.   Figure 8.  Image of SEM for B1  Figure 9.  EDS Spectrum phase of the dark gray Figure 10 shows XRD patterns of the molten alloy B2. The composition presented several peaks of diffractions corresponding to the crystalline phases; therefore this composition is fully crystallized.  Figure 10.  XRD of sample B1 The microstructure of the sample of the molten alloy B2 has been observed by SEM (fig. 11). Figure 12 shows the EDS spectrum of the crystalline phase of the black point. We found that this phase is an yttrium oxide.  Figure 11.  Image of SEM for B2  Figure 12.  EDS spectrum of the black phase The second finding of the EDS analysis spectrum of the alloy B2 (fig. 14) corresponds to the crystalline phase in dark gray (fig. 13), and shows the phase of the chrome and iron carbide.  Figure 13.  Image of SEM for B2  Figure 14.  EDS Spectrum phase of the dark gray The spectrum analysis of the white crystalline phase (fig. 16) that corresponds to the image of SEM (fig. 15) shows  30 40 50 60 70 80 90 100 110 120 130   Fe3Mo3C (Cr,Fe)23C6 (Mo Cr)+Fe B4CrMo Y2O3intensity2θ158 Preparation and Characterization of Master Alloys Fe48Cr15Mo14C15B6Y2 Metallic Glasses   that this is a solid phase α in chemical composition (Mo Cr) +Fe.  Figure 15.  Image of SEM for B2  Figure 16.  EDS spectrum of the white phase We present in figure 17 the SEM image of a sample of the alloy B2, with their spectral analysis EDS (fig. 18) of the crystalline phase in average gay; the interpretation of this result indicates that this phase is molybdenum and iron carbide.  Figure 17.  Image of SEM for B2  Figure 18.  EDS spectrum of the phase average gray The high temperature differential scanning calorimeter HTDSC relies on the comparison of heat flux as a function of temperature between a reference inert (here a door empty sample) and a sample to characterize which undergoes transformations of phase exothermic or endothermic.  In the case of the alloy mother of a metallic glass these measurements used to determine the melting temperatures (endothermic) and solidification (exothermic). The behavior of the merger of the two molten alloys B1 and B2 is studied by HTDSC (fig. 19). The analysis of this thermo gram shows that for the two alloys B1and B2, the results are non-eutectic of the merger. For the alloy B1, the first melting temperature (Tm) and the final temperature of fusion (Tl) are 1093 °C and 1214 °C respectively. For the alloy B2, the first melting temperature (Tm) and the final temperature of fusion (Tl) are 1120.4 °C and 1233 °C respectively.  Figure19.  HTDSC traces the fusion of the alloy B1 and B2 We present in figure 20, HTDSC who trace the solidification of the two molten alloys B1 and B2. During the cooling, two peaks of exothermic alloy solidification for the B1 are observed whose temperatures are the following: 1122.4 C° and 1128.9 °C. For the alloy B2, there are three peaks of solidification whose temperatures are the following: 1127. 6, 1138 and 1171.2 °C.  Figure20.  HTDSC traces the solidification of the alloy B1 and B2  1000 1050 1100 1150 1200 1250 1300 1350Exothermique B2_Fusion B1_Fusionflux de chaleurtempérature(°c) 1000 1050 1100 1150 1200 1250 1300Exothermique B2_Solidification B1_SolidificationFlux de chaleurtempérature(°c) Chemical and Materials Engineering 2(7): 155-159, 2014 159  4. Conclusion Our study is therefore committed to study the structural and thermal properties of two master alloys for Fe-based metallic glasses and to better understand the existing crystalline phases in these alloys and make a comparison between the latter whose goal is the possibility of industrial manufacture of metallic glasses from the raw materials. We have seen, according to the results of XRD in combination with the SEM and EDS that there are four crystalline phases are the same for the two alloys B1 and B2 which are carbide (molybdenum + iron), carbide (iron + chromium), solid α ((Mo Cr) +Fe) and yttrium oxide, it is for this reason, we can say that there is similarity between the two masters alloys. It must be noted after the results of HTDSC that the temperatures of the fusion and solidification of the alloy B2 are higher in comparison with that of the alloy B1.This is due to the homogeneity of the alloy B1 because these elements are pure. Acknowledgments We thank the Groups of Pr. Marcello Baricco and Pr. Franco Vinai for the synthesis of the samples and the obtained results.   REFERENCES [1] Á.Révész, AConcustell., L.K.Varga, S.Suriñach, M.D.Baró, Mat. Sci. Eng. 375–377 (2004) 776 [2] W. Klement, R.H. Willensand P. Duwez, Nature 187 (1960) 869 [3] A. Inoue, T. Zhangand T. Masumoto, Mater. Trans. JIM31 (1990) 425 [4] A. Pekerand W.L. Johnson, Appl. Phys. Lett. 63(1993) 2342 [5] B. Bendjemil, N. Seghairi, A. Bouchareb, A. Hafs and M. Baricco, Int. Journals of Nanoelectronics and materials 3(2010) 35-42 [6] H.Zhang, D.G.Naugle, Appl.Phys. Lett.60 (1992) 2738 [7] J.Koike, D.M.Parkin,M.Nastasi, Journal of MaterialsResearch5 (1990) 1414 [8] A.Iljinas, D.Milcius, J.Dudonis, Vacuum 81 (2007) 1213 [9] C.A.C.Souza, J.E.May, A.T.Machado,A.L.R.Tachard., E.D.Bidoia,  Surface & Coatings Technology 190 (2005) 75 [10] T. Baser, M.Baricco, J.Alloycompd. 190 (2006) [11] A. Bouchareb, B. Bendjemil, R. Piccin and M. Baricco, Int. Journal of Nanoelectronic and Materials 3(2010) 63-70  

Preparation and Characterization of Master Alloys Fe48Cr15Mo14C15B6Y2 Metallic Glasses

LAReferencia - Red Federada de Repositorios Institucionales de Publicaciones Científicas Latinoamericanas

CONICET Digital

http://ri.conicet.gov.ar/bitstream/11336/36689/2/CONICET_Digital_Nro.5dde6671-baed-44aa-b1a5-0a94cae3cf3b_A.pdf

Preparation and Characterization of Master Alloys Fe48Cr15Mo14C15B6Y2 Metallic Glasses

Abstract

Similar works

Full text

Available Versions

Institutional Research Information System University of Turin

LAReferencia - Red Federada de Repositorios Institucionales de Publicaciones Científicas Latinoamericanas

CONICET Digital