The effect of cold rolling to 80% thickness reduction and annealing at 973-1373 K for 1h our on the microstructure and mechanical properties of a C-containing CoCrFeNiMn high-entropy alloy was studied. Cold rolling significantly strengthened the alloy to the yield strength of 1310 MPa. Annealing at 973 K or 1073 K resulted in incomplete recrystallization of an fcc matrix and M23C6-type carbide precipitations aligned with highly elongated grains/subgrains. Complete recrystallization occurred during annealing at 1173-1373