and bio-based solutions in shoe manufacturing, including the use
of biodegradable materials. As a first step towards the proposal
of such solutions, in this work different microorganisms were
screened for their intrinsic capacity to degrade a base TPU. The
biodegradability was tested using the agar plate method against
different bacteria, fungi and a consortium of both. The most
promising results, corresponding to higher weight-loss
percentages of the TPU sample, were obtained using the
consortium of Pseudomonas aeruginosa and Aspergillus niger.
These best conditions were thereafter applied to TPU samples
compounded with biobased additives.info:eu-repo/semantics/publishedVersio

Amaral, Joana S.

Barbosa, Mariana Martinho

Barreiro, M.F.

Fernandes, I.P.

Ferreira, Maria José

Pinto, V.

Fernandes, Isabel P.

Pinto, Vera

Biblioteca Digital do IPB

  10 – 12 Sept. 2014 PORTO PORTUGAL 12th International Chemical and Biological  Engineering Conference Effect of Edible Composite Coatings on Color Change in Tomato (Solanumlycopersicum L.) Fruits during Storage 10-52 P-BE19 A.R.M. Barreto, E.M.M. Aroucha, F.K.G. Santos, R.H.L. Leite, T.A. Oliveira Poly(3-hydroxybutyrate) production by Cupriavidus necator DSM 545, from a byproduct of the ethanol production process 10-55 P-BE20 K. Zanfonato, L.K. Quines, M. Schmidt, C.S. Gai, F.M. Martinhago, W. Schmidell, G.M.F. Aragão Exploring the Use of Heparin as First Capture Step in the Purification of Monoclonal Antibodies from Cell Culture Supernatants 10-58 P-BE21 I.F. Pinto, S.A.S.L. Rosa, M.R. Aires-Barros, A.M. Azevedo Screening of different microorganisms for their biodegradation capacity regarding polyester-based thermoplastic polyurethanes 10-61 P-BE22 I.P. Fernandes, M. Barbosa, J.S. Amaral, V. Pinto, M.J. Ferreira, M.F. Barreiro Development of a prototype to access biodegradability of TPU shoe soles under controlled conditions 10-63 P-BE23 I.P. Fernandes, M. Barbosa, J.S. Amaral, V. Pinto, M.J. Ferreira, M.F. Barreiro Covalent immobilization of crosslinked trypsin onto electrospun poly(ethylene terephthalate)/poly(lactic acid) nanofiber mats 10-65 P-BE24 T.R. Silva, J.M.S. Rocha, M.H. Gil, S.C.S. Pinto, J.A. Lopes da Silva, A.J. Guiomar Optimization of Initial Moisture and Temperature in Solid State Fermentation to Produce Cellulases by Aspergillus Uvarum on Olive Mill and Winery Wastes 10-68 P-BE25 J.M. Salgado, L. Abrunhosa, J.M. Domínguez, A. Venâncio, I. Belo Cellulase and Xylanase Production by A. uvarum in Solid-State Fementation Using a Packed-Bed Bioreactor 10-70 P-BE26 J.M. Salgado, L. Abrunhosa, J.M. Domínguez, A. Venâncio, I. Belo MSAT Strategies in Pharmaceutical Engineering 10-72 P-BE27 T.A. Carvalho, A.J. Almeida, R.S. Gaspar, J.C. Menezes   ChemPort2014 Poster session - Biological Engineering 10-61 Screening of different microorganisms for their biodegradation capacity regarding polyester-based thermoplastic polyurethanes  P-BE22 I.P. Fernandes1, M. Barbosa1, J.S. Amaral2, V. Pinto3, M.J. Ferreira3, M.F. Barreiro1, * (1) LSRE, Associate Laboratory LSRE/LCM, Polytechnic Institute of Bragança, Campus Sta. Apolónia Ap. 1134, 5301-857, Bragança, Portugal, (2) ESTiG/Polytechnic Institute of Bragança, Campus Sta. Apolónia Ap. 1134, 5301-857, Bragança, Portugal and REQUIMTE, Department of Chemical Sciences, Faculty of Pharmacy, University of Porto, Rua Jorge Viterbo Ferreira, 228, 4050-31, Porto, Portugal, (4) CTCP, Rua de Fundões - Devesa Velha, 3700-121 S. João da Madeira, Portugal; *barreiro@ipb.pt. t = 0 days37ºCt = 30 days  Nowadays the footwear industry is seeking for more sustainable and bio-based solutions in shoe manufacturing, including the use of biodegradable materials. As a first step towards the proposal of such solutions, in this work different microorganisms were screened for their intrinsic capacity to degrade a base TPU. The biodegradability was tested using the agar plate method against different bacteria, fungi and a consortium of both. The most promising results, corresponding to higher weight-loss percentages of the TPU sample, were obtained using the consortium of Pseudomonas aeruginosa and Aspergillus niger. These best conditions were thereafter applied to TPU samples compounded with biobased additives.  Introduction At present, footwear is considered as one of the most internationalised sectors of the Portuguese industry with a significant importance for the national economy. This sector seeks to affirm itself in market niches with greater technical and scientific requirement, value-added and high quality standards, resulting in research and technological development investment. Moreover, there has been an increasing interested in reducing the environmental impact of this sector by seeking for more sustainable and bio-based solutions. Among the wide variety of materials employed in shoes’ production, different polymers are frequently used as they exhibit a versatile array of properties in terms of strength, lightness, durability and resistance to degradation, with thermoplastic polyurethanes (TPUs) being one of the most widely used [1]. In what concerns footwear industry it is estimated that TPU footwear components represent about 60% of the whole production in Europe. On the other hand, the use of a wide variety of additives in TPUs formulation (e.g. pigments, coatings, and fillers) limits the possibility of recycling. In such scenario, biodegradable polymers could offer an excellent solution to the environment hazard posed by conventional polymers [2]. Therefore, given the widespread use of TPUs and associated waste management problems, it makes sense to invest on the development of more biodegradable and environmental compatible solutions. As a first step towards the proposal of such solutions, encompassing for example the production of modified TPUs by compounding with natural additives, in this work different microorganisms, including bacteria, fungi and an association of both (consortium), were screened for their intrinsic capacity in degrading a TPU sample used in the footwear industry.  Materials and Methods Samples: A polyester-based TPU used in footwear industry was chosen for the screening assays. For testing the best conditions 2 commercial additives and 3 natural substances (lignin, cellulose and starch) have been selected. Biodegradation assays: The degradation assays were performed in agar plates by sample inoculation using bacteria, fungi and different consortia (Table 1). The culture media and incubation conditions used for each assay are also presented in Table 1.  Table 1. Microorganisms and culture conditions used in the biodegradation assays in agar plates.  Microorganisms Culture media Incubation Bacteria Bacillus subtilis ATCC 1234 Nutrient agar 30 days 37ºC Bacteria Pseudomonas aeruginosa  ATCC 9027 Nutrient agar 30 days 37ºC Fungi Aspergillus niger ATCC 16404 Sabouraud dextrose agar 30 days 30ºC Fungi Penicillium chrysogenum ATCC 1234 Sabouraud dextrose agar 30 days 30ºC Consortium A. niger + P. chrysogenum Sabouraud dextrose agar 30 days 30ºC Consortium A. niger + P. aeruginosa Sabouraud dextrose agar 30 days 37ºC  ChemPort2014 Poster session - Biological Engineering 10-62 For the assays with bacteria, the inoculum was adjusted to approximately 0.5 McFarland turbidity standard and spread over the agar plates. The TPU sample was aseptically transferred to the agar surface and inoculated with 100 µL of the bacterial inoculum (Figure 1A). The degradation assays with fungi were performed as previously described [3]. Briefly, a concentrated spore suspension was prepared by scraping the fungi mycelium with a sterilized loop. The suspension was filtered to remove agar and mycelium residues and centrifuged (15 min, 4000 rpm). The obtained pellet was re-suspended in 5mL sterile distilled water, used for spore count in a Neubauer chamber and diluted to a final concentration of approximately 1x106 spores/mL. The agar plates were spread with the spore suspension which was also used for sample inoculation (100 µL) (Figure 1B). In the assay performed with the consortium of bacteria and fungi, the bacteria inoculum was spread over the agar and square samples (1x1 cm) of A. niger mycelium were transferred to the agar surface. The TPU samples were inoculated with both bacteria inoculum and fungi mycelium (Figure 1C). After incubation, the TPU samples were collected, washed with ethanol and dried at ambient conditions before weighing. The biodegradation was estimated based on the weight-loss of the samples. All TPU samples were tested in duplicate.  Figure 1. Biodegradation assays of TPU samples after 30 days of incubation (A and B) and at the beginning of the assay (C). Plates were inoculated with B. subtilis (A), consortium of A. niger and P. chrysogenum (B) and consortium of P. aeruginosa and A.niger (C).  Results and Discussion As expected, and regardless of the tested microorganism, modest weight losses percentages were achieved for the TPU samples under evaluation. In general, the sample degradation was slightly higher in the assays performed with fungi when compared to bacteria, with best results being achieved for A. niger (Figure 2). Among the two tested bacteria, the higher weight loss was achieved with P. aeruginosa. Similar results to the ones performed with the individual microorganisms were obtained with the fungi consortium. By the contrary, the weight loss % improved significantly when using the consortium aeruginosa + A. niger (Figure 2). These results evidence the existence of a synergistic activity between fungal and bacterial degradation that could be further explored in this field of TPUs biodegradation. In what concerns the tested additives lignin gave the best results.  0,00,51,01,52,02,53,03,54,04,55,0TPUWeight loss (%)P.aeruginosaB.subtillisA.nigerP.chrysogenumA.niger+P.chrysogenumA.niger+P.aeruginosa Figure 2. Results of the TPU samples weight loss tested with different microorganisms.  Conclusion The use of a consortium comprised of bacteria and fungi, namely P. aeruginosa and A. niger, led to better results in what concerns weight loss % of the tested TPU samples. The preparation of TPU samples modified by compounding with biobased additives pointed out for the best results achieved with natural substances such as lignin, starch and cellulose (data not shown).  Acknowledgements Financial support from COMPETE, QREN and EU (project QREN SI I&D Co-promoção 13850 NEWALK) is acknowledged. The authors also thank FCT and FEDER under Programe COMPETE for the financial support LSRE (PEst-C/EQB/LA0020/2011 strategic project). A special thanks to Procalçado for having provided the base TPU used in this study.   References [1] T. Staikos, R. Heath, B. Haworth, S. Rahimifard, Proceedings of the 13th CIRP International Conference on Lyfe Cycle Engineering (2006) 497-502. [2] M. Flieger, M. Kantorová, A. Prell, T. Rezanka, J. Votruba, Folia Microbiologica, 48 (2003) 27-44. [3] J.S. Amaral, M. Sepulveda, C.A Cateto, I. P. Fernandes, A.E. Rodrigues, M.N. Belgacem, M.F. Barreiro, Polymer Degradation and Stability, 97 (2012) 2069-2076. 

Screening of different microorganisms for their biodegradation capacity regarding polyester-based thermoplastic polyurethanes

http://bibliotecadigital.ipb.pt/bitstream/10198/14225/1/RESUMO-CHEMPOR%20P-BE22%20%28Porto%202014%29.pdf

Screening of different microorganisms for their biodegradation capacity regarding polyester-based thermoplastic polyurethanes

Abstract

Similar works

Full text

Available Versions

Biblioteca Digital do IPB