Clothing can provide safety and comfort for persons exposed to both cold and hot thermal environments. To assess the potential impact of clothing moisture and wetness on fabric cooling, a series of wind-tunnel tests was conducted to quantify the evaporative cooling capacity of selected fabric samples. Single-layer cotton, polyester, nylon and silk were evaluated. The results showed that onset and magnitude of evaporative cooling was determined by the amount of water contained in a fabric sample. The results also showed that an exposed  skin  exhibited more cooling when covered with a fabric than when it was not. The information obtained helps better understand the evaporative cooling process for fabrics and assist in the selection of garment materials that optimize worker comfort and safety

Goonetilleke, Ravindra S.

Reischl, Uwe

Boise State University - ScholarWorks

Boise State UniversityScholarWorksCommunity and Environmental Health FacultyPublications and PresentationsDepartment of Community and EnvironmentalHealth1-1-2016Fabric Cooling by Water EvaporationUwe ReischlBoise State UniversityRavindra S. GoonetillekeHong Kong University of Science and TechnologyThis document was originally published by Textile Bioengineering and Informatics Society in Journal of Fiber Bioengineering and Informatics. Copyrightrestrictions may apply. doi: 10.3993/jfbim00251Journal of Fiber Bioengineering and Informatics 9:4 (2016) 237–245doi:10.3993/jfbim00251Fabric Cooling by Water EvaporationUwe Reischl a,∗, Ravindra S. Goonetilleke baBoise State University, 1910 University Ave., Boise, Idaho 83725, USAbThe Hong Kong University of Science and Technology, Clear Water Bay, Hong KongAbstractClothing can provide safety and comfort for persons exposed to both cold and hot thermal environments.To assess the potential impact of clothing moisture and wetness on fabric cooling, a series of wind-tunneltests was conducted to quantify the evaporative cooling capacity of selected fabric samples. Single-layer cotton, polyester, nylon and silk were evaluated. The results showed that onset and magnitude ofevaporative cooling was determined by the amount of water contained in a fabric sample. The resultsalso showed that an exposed “skin” exhibited more cooling when covered with a fabric than when it wasnot. The information obtained helps better understand the evaporative cooling process for fabrics andassist in the selection of garment materials that optimize worker comfort and safety.Keywords: Evaporative Cooling; Fabrics Moisture; Protective Clothing1 BackgroundEvaporation of water from the skin can provide significant cooling benefits for individuals exposedto hot and / or dry environments. However, clothing can complicate the evaporation process bycreating a barrier to metabolic heat loss through the insulation created by the clothing itself.This, in turn, can create a humid microclimate that reduces the evaporative cooling efficiencyof sweat from the skin [1]. Assessing the cooling effect of evaporation in clothing systems isvery complex. Sweat may evaporate directly from the skin surface or wick into the fabric whereevaporation takes place on the surface of the garment rather than on the skin surface. Bothof these processes can occur simultaneously. Furthermore, excessive sweat may roll off the skinor remain trapped in the clothing system. It is assumed that sweat evaporated from the skinsurface can deliver more cooling than when sweat evaporates from a garment [2]. When sweatevaporates from a garment, the location of the evaporative phase change is moved from the skinto the outer surface of the garment where heat is extracted from the external environment ratherthan from the surface of the skin. The overall cooling effects of sweat evaporation for clothedpersons has been carried out on human subjects as well as using thermal manikins [3-6]. However,the outcomes have been difficult to related to clothing design and fabric selection because the∗Corresponding author.Email address: ureischl@boisestate.edu (Uwe Reischl).1940–8676 / Copyright © 2016 Textile Bioengineering and Informatics Society2016238 U. Reischl et al. / Journal of Fiber Bioengineering and Informatics 9:4 (2016) 237–245data are confounded by heat loss due to the latent heat of vaporization which cannot be assessedseparately [7]. The cooling generated by wet clothing, independent of body metabolic heat loss,and the associated latent heat of vaporization, have not been separated. To address this issue,a series of tests was carried out to measure the cooling created by evaporation not impacted bymetabolic heat production or subsequent sweating.2 Methods and ProceduresWind-tunnel tests were conducted on cotton, polyester, nylon and silk fabric samples to determinethe cooling generated by water evaporation from the fabric samples under controlled temperature,humidity, and air velocity conditions. The temperature drop due to water evaporation was mea-sured using a thermocouple temperature probe imbedded into the surface of a mounting platform.A “control” configuration which did not include a fabric sample placed on the temperature sensorwas used as a reference. All tests were performed three times and the data averaged.2.1 Wind TunnelA negative pressure laminar air flow wind-tunnel was used for this study. The wind-tunnelmeasured 2.3 meters in length, 40.5 cm in height and 30.5 cm in width. Fabric samples wereplaced onto a mounting platform which was positioned in the center of the wind-tunnel 1.2 metersfrom the inlet. The air velocity was maintained at 1.5 m/sec. Air temperature was maintainedat 22 ◦C (±2 ◦C) and relative humidity maintained at 15% (±5%).2.2 Fabric SamplesFour types of fabric materials were tested. These included 100% cotton, 100% polyester, 100%nylon, and 100% silk. Each sample was 5.0 cm×6.0 cm in size.2.3 Mounting PlatformFabric samples were placed onto a convex shaped mounting platform made of water impermeableStyrofoam. Samples were placed onto the platform surface at a 45◦ angle relative to the horizontaland oriented into the wind-tunnel airflow. The platform allowed a fabric sample to lay smoothlyon the surface. To prevent potential displacement of the fabric sample by the air flow, each samplewas secured to the platform by four corner pins. The platform provided gravity run-off for allexcess water. A precision type K fine-wire glass insulated thermocouple was embedded into thesurface of the mounting platform which provided a temperature measurement of the underside ofthe fabric sample. The digital thermometer provided an accuracy of ±0.1 ◦C2.4 Test ProtocolFabric samples were spray irrigated with water 10 seconds prior to the start of each test run. Theirrigation water was maintained at room-temperature prior to application and was applied untilU. Reischl et al. / Journal of Fiber Bioengineering and Informatics 9:4 (2016) 237–245 239a fabric sample was saturated. Saturation was determined when the water was dripping freelyfrom the mounting platform. The fabric samples tested for the “moist” condition were initiallysaturated with the irrigation water but then manually squeezed to remove all excess water. Thisprocedure was subjective. No water was added to any of the samples later during the tests.The temperature drop created by each sample was measured for duration of 15 minutes. Thetemperature on the surface of the platform and bottom of the fabric sample was recorded at 0.5minute, 1.0 minute, 1.5 minutes, 2 minutes, 5 minutes, 10 minutes and 15 minutes. All fabricsamples, including the saturated and moist conditions, were tested three times.3 Results3.1 ControlTable 1 summarizes the evaporative cooling observed for the “control” condition in comparisonto the saturated cotton fabric sample. The temperature drop seen for the control condition was5.1 ◦C during the first five minutes and declined to 4.4 ◦C afterwards. However, the temperaturedrop observed for the cotton sample was 8.6 ◦C during the first 10 minutes but showed no declineafterwards.Table 1: Temperature drop observed for the “control” condition and saturated cotton sample. Valuesrepresent the average of three trialsExposure Time (Minutes) “Control” Configuration (◦C) Cotton Sample (◦C)0 0 00.5 3.4 4.21.0 4.4 6.21.5 4.7 7.32 4.8 7.95 5.1 8.510 4.5 8.615 4.4 8.63.2 Water ContentTable 2 summarizes the evaporative cooling observed for the “moist” and the “saturated” cottonsamples. During the first 1.5 minutes of exposure, cooling created by the “moist” sample wassubstantially greater than by the “saturated” sample. However, after two minutes of exposure,the “saturated” cotton sample exhibited substantially greater cooling than the “moist” cottonsample.3.3 Fabric MaterialsTable 3 summarizes the evaporative cooling for the cotton, polyester, nylon and silk saturatedfabric samples. During the first 1.5 minutes the temperature drop measured was greater for240 U. Reischl et al. / Journal of Fiber Bioengineering and Informatics 9:4 (2016) 237–245Table 2: Cotton sample temperature drop observed for the “moist” and “saturated” conditions. Valuesrepresent the average of three trialsExposure Time (Minutes) Cotton Sample (Moist) (◦C) Cotton Sample (Saturated) (◦C)0 0 00.5 6.7 5.71.0 7.8 7.41.5 8.3 8.22 8.4 8.55 8.5 8.810 8.5 8.815 8.5 8.8Table 3: Evaporative cooling observed for the saturated cotton sample, polyester sample, nylon sample,and silk sample. Values represent the average of three trialsExposure Time (Minutes) Cotton Sample (◦C) Polyester Sample (◦C) Nylon Sample (◦C) Silk Sample (◦C)1.5 8.5 8.3 9.1 9.22 9.1 8.9 9.2 9.35 9.6 9.5 9.3 9.410 9.7 9.6 9.2 9.415 9.7 9.6 9.0 9.4the Nylon and silk samples in comparison to the temperature drop measured for the cotton andpolyester samples. However, this relationship was reversed after five minutes when the cottonand polyester cooling was observed to be greater than that for the nylon and silk samples.4 AnalysisComparing the temperature drop created by the cotton sample with the temperature drop createdby the “control” condition suggests that the improved cooling for the saturated cotton fabricsample was due to the water contained in the fabric sample. Since the testing platform was madeof non-absorbing material, water applied to the platform flowed off the surface freely with onlya surface layer of water remaining due to the surface adhesion. This condition provided only alimited amount of water for evaporation. As shown in Fig. 1, the “control” cooling decreasedover time while the cotton fabric sample exhibited no such decrease. This difference in coolingsuggests that the amount of water retained by the fabric sample determined the final coolingcapacity as well as the duration of the cooling process. The T-test applied to the equilibriumconditions, i.e., the 2-15 minute time segments, yielded p = 0.001.The relationship between water retention in a fabric and the evaporative cooling capacity of thesample is illustrated in Fig. 2. The saturated (high water content) cotton sample exhibited thegreatest overall cooling than the moist sample. However, the moist sample exhibited a greatertemperature drop during the first 1.5 minutes while the saturated sample exhibited a greatertemperature drop afterwards. The dynamics of the relative cooling advantages offered over timeU. Reischl et al. / Journal of Fiber Bioengineering and Informatics 9:4 (2016) 237–245 241CottonControl1098765432100 2 4 6 8 10Time (minutes)12 14 16Temperature DropFig. 1: Evaporative cooling for the saturated cotton sample in comparison to the “control” over a 15minute period8.98.88.78.68.58.48.38.28.10 2 4 6 8 10Time (minutes)12 14 16MoistSaturatedTemperature DropFig. 2: Evaporative cooling observed for the saturated and the moist cotton samples. The moist samplegenerated a greater temperature drop during the first 1.5 minutes while the saturated sample generateda greater temperature drop afterwardsby each of the fabric samples is illustrated in Fig. 3. This suggests that the maximum coolingdoes not always occur when the water retained in a sample is high. The T-test applied to theequilibrium conditions, i.e., the 5-15 minute time segments, yielded p = 0.007.A comparison of the cooling dynamics exhibited by the cotton, polyester, nylon, and silk samplesis illustrated in Fig. 4. It is seen that the cotton and polyester samples offered greater evaporativecooling overall than the silk and nylon samples. It is important to note, however, the nylon andsilk samples initially provided greater evaporative cooling. These differences were statisticallysignificant. The T-test was again applied to the equilibrium conditions. The cotton/polyestercomparison yielded p = 0.05, the cotton/silk comparison yielded p = 0.001, and the cotton/nyloncomparison yielded p = 0.006 This finding again supports the concept illustrated in Fig. 2 andFig. 3 where the moist sample exhibited greater initial evaporative cooling than the saturatedsample.242 U. Reischl et al. / Journal of Fiber Bioengineering and Informatics 9:4 (2016) 237–245Time (minutes)Relative temperature difference (°C)0 5 10 15 201.21.00.80.60.40.20−0.2−0.4Fig. 3: Illustration of the relative evaporative cooling advantage offered by the moist sample relative tothe saturated sample during the first 1.5 minutes followed by a cooling disadvantage afterwardsTime (minutes)Temperature drop (°C)CottonPolyesterNylonSilk9.89.69.49.29.08.88.68.48.20 2 4 6 8 10 12 14 16Fig. 4: Evaporative cooling observed for the cotton, polyester, silk and nylon fabric samples after 1.5minutes of air flow exposure5 DiscussionThe water introduced into a fabric is dispersed and also retained in response to the interaction ofwater molecule surface tension, cohesion and adhesion to the fabric fibers. These forces interactU. Reischl et al. / Journal of Fiber Bioengineering and Informatics 9:4 (2016) 237–245 243with the water droplets and the fabric fibers which influence the total amount of water that isstored in the fabric and also determines the surface area over which the water can evaporate.The ability of a fabric to capture water and distribute the water over the material will dictatethe evaporation capacity of the material. The distribution of the water over the fabric materialdetermines the evaporation capacity of the fabric material which will be greater than the evapo-ration capacity of the skin where the water remains attached to the skin in the form of dropletsas illustrated in Fig. 5. Fig. 6 illustrates the mechanism by which fibers promote the spread ofwater over a larger area in a fabric that increases the overall cooling capacity through evaporation.This is illustrated in Fig. 3 showing the cooling advantage offered by wet fabrics. However, theevaporation efficiency of water from a fabric can also be influenced by the total amount of waterthat is retained within the fabric. As seen in Table 2 and Fig. 3, the cooling efficiency is optimalat lower “wetness“ levels, i.e., moist conditions, while cooling over an extended period of time ispromoted by higher water content levels.Fig. 5: Sweat droplets accumulating on the surface of the human skin as a result of water moleculecohesion and adhesion. This limits the spread of water over the skin and reduces the potential ofevaporative cooling from the skinWaterFabric fibersDry threadsHeat loss by conductionWater exposurecapillary actionWet threadscomplete wettingSkinVaporizationFig. 6: Interaction of water droplets with fabric fibers that increases the available surface area forevaporation and subsequent skin coolingThe results of this study suggest that a person wearing an appropriate garment experiences bet-ter cooling and more comfort than a person without a garment. Such an approach is observed forexperienced athletes who wear a shirt when engaged in athletic competitions. This is illustratedin Fig. 7.244 U. Reischl et al. / Journal of Fiber Bioengineering and Informatics 9:4 (2016) 237–245Fig. 7: Runner wearing a T-shirt to maximize cooling through garment sweat evaporation (Hong KongSports Photography Association Photo)6 ConclusionsBased on the results obtained in this study, the following conclusions can be reached:• Wet clothing can create cooling that is significantly greater than cooling generated by waterevaporating directly from the skin• Initial cooling by wet fabrics is greatest when a fabric contains a minimal amount of water(moist) while cooling is optimal over a longer period of time when the fabric contains highlevels of water (saturated).• The level of cooling created by wet clothing over time is dictated by the total water contentin the fabric. The greater the amount of water, the longer the cooling effect over time.This study also helps explain why persons frequently report improved comfort in hot environ-ments when wearing single-layered clothing that does not absorb much sweat. The materials thatabsorb little water such as nylon and silk provide immediate cooling while cotton provides bettercooling later. Application of this information can help in the design and development of futureclothing systems that create both immediate and long-term improvements in comfort and safetyfor the users.References[1] Nunnaly S. Heat Stress in Protective Clothing, Scan. J. Work Environ Health 1989; 15 (suppl 1):52-57U. Reischl et al. / Journal of Fiber Bioengineering and Informatics 9:4 (2016) 237–245 245[2] Craig FN, Moffit JJ. Efficiency of Evaportive Cooling from Wet Clothing. J Appl Physiol 1974;36: 313-316[3] Lotens WA, Havenith G, Van de Linde FJG. Effects of Condensation in Clothing on Heat Transfer.Ergonomics 1995; 38: 1114-1131[4] Lotens WA, Havenith G. Effects of Moisture Absorption in Clothing on the Human Heat-Balance,Ergonomics 1995; 38: 1095-1113[5] McLellan TM, Pope JL, Cain JB, Cheung SS. Effects of Metabolic Rate and ambient VaporPressure on Heat Strain in Protective Clothing, Eur J Appl Physiol 1996; 74: 518-527[6] Mitchell D, Wyndham CH, Atkins AR, Vermeulen AJ, Hofmeyer HS, Strydom NB, Hodgson T.Direct Measurement of Thermal Responses of Nude Men Resting in Dry Environments. Arch GesPhysiol 1968; 74: 324-343[7] Havenith G, Brode P. Den Hartog E, Kuklane K., Homer I, Rossi RM, Richards M, Farnworth B,Wang X. Evaporative Cooling: Effective Latent Heat of Evaporation in Relation to EvaporationDistance from the Skin, J Appl Physiol 2013; 114: 778-785

Fabric Cooling by Water Evaporation

Abstract

Similar works

Full text

Available Versions

Boise State University - ScholarWorks