Cu(In,Ga)Se2 (CIGS) photovoltaic (PV) cells require a highly conducting and transparent electrode for optimum device performance. ZnO:Al films grown from targets containing 2.0 wt.% Al2O3 are commonly used for this purpose. Maximum carrier mobilities of these films grown at room temperature are ~20-25 cm2V-1s-1. Therefore, relatively high carrier concentrations are required to achieve the desired conductivity, which leads to free carrier absorption in the near infrared (IR). Lightly doped films (0.05 - 0.2 wt.% Al2O3), which show less IR absorption, reach mobility values greater than 50 cm2V-1s-1 when deposited in H2 partial pressure. We incorporate these lightly doped ZnO:Al layers into CIGS PV cells produced at the National Renewable Energy Laboratory (NREL). Preliminary results show quantum efficiency values of these cells rival those of a past world-record cell produced at NREL that used 2.0 wt.% Al-doped ZnO films. The highest cell efficiency obtained in this trial was 18.1%