LiFePO{sub 4} has several potential advantages in comparison to the transition metal oxide cathode materials used in commercial lithium-ion batteries. However, its low intrinsic electronic conductivity ({approx} 10{sup -9} S/cm) is problematic. We report here a study by soft x-ray absorption/emission spectroscopy of the electronic properties of undoped LiFePO{sub 4} and Li-doped LiFePO{sub 4} in which Li{sup +} ions are substituted for Fe{sup 2+} ions in an attempt to increase the intrinsic electronic conductivity. The conductivities of the Li{sub 1+x}Fe{sub 1-x}PO{sub 4} samples were, however, essentially unchanged from that of the undoped LiFePO{sub 4}. Nonetheless, evidence for changing the electronic properties of LiFePO{sub 4} by doping with excess Li+ was observed by the XAS/XES spectroscopy. New pre-edge features the O-1s XAS spectrum of Li{sub 1.05}Fe{sub 0.95}PO4 is a direct indication that the charge compensation for substitution of Fe{sup 2+} by Li{sup +} resides in the unoccupied O-2p orbitals. A charge transfer (CT) excitation was also observed in the doped material implying that the unoccupied O-2p orbitals created by doping are strongly hybridized with unoccupied Fe-3d orbitals of neighboring sites. However, the strong covalent bonding within the (PO{sub 4}){sup 3-} anions and the large separation of the Fe cations means that the charge created by doping is not delocalized in the manner of electrons or holes in a semiconductor