Crocker, James E.

Geiss, Erik

Ghayad, Ibrahim M.

Marcus, Harris L.

English

Texas ScholarWorks

SPOT JOINING OF Si3N4 AND SIC CERAMICS USING SELECTIVEAREA LASER DEPOSITION  (SALD) TECHNIQUEIbrahim M. Ghayad*, Erik Geiss , James E. Crocker, and Harris L. MarcusInstitute of Materials Science, University of Connecticut, Storrs, Connecticut*Central Metallurgical Research and Development Institute, Cairo, EgyptKeywords, Silicon Nitride, Silicon Carbide, Laser Spot Joining of CeramicsIntroductionAn important approach to forming difficult and intricate ceramic products is the joining ofsimple ceramic shapes together to build up to the desired design and hence the economic andtechnological barriers in manufacturing complex ceramic designs could be avoided. The traditionalmanner of metal welding by melting the base material is extremely difficult with the typical ceramichigh melting temperature or impossible due to thermal decomposition.   Brazing of an intermediatematerial to stick two objects together at a seam also has complications because ceramics are poorlywet by most metals and the resulting operating temperature is lowered (1).A new, promising manufacturing path involves a gas-phase decomposition approach, knownas Selective Area Laser Deposition (SALD) joining.  SALD is a gas-phase Solid Free Form (SFF)process in which a specific gas mixture decomposes either thermally or photolytically from theenergy input of a laser beam to form a solid reaction product (1,2,3,4).  The chemical process issimilar to Chemical Vapor Deposition (CVD) but the product is selectively deposited locally underthe laser spot, which can be scanned, and therefore controlled.The present paper focuses on deposition of silicon nitride or silicon carbide filler materialsto spot join silicon nitride and silicon carbide ceramic materials.  Chemical and structuralcharacterization of joints was performed.ExperimentalThe SALD work-station consists of a vacuum chamber, a 150 watt continuous waveNd:YAG (1.06 micron wavelength) laser beam, an xy table, scanning mirrors, and an opticalpyrometer temperature probe.  During SALD experiments the surface temperature was measured byan optical pyrometer and was used in a feedback loop to adjust the laser output power to establishthe conditions to maintain a constant surface temperature throughout the experiment.  These laserpower conditions were then used in the spot joining experiments.  The laser beam spot size isnominally 1 mm in diameter and approximately Gaussian in shape.Specimens of fully dense silicon nitride from Norton (NBD 200), 0.8 x 0.8 x 0.2 inchsamples were used for joining experiments.  Other experiments were carried out using siliconcarbide infiltrated Mo powder specimens prepared using the Selective Area Laser Deposition VaporInfiltration (SALDVI) technique which shares many attributes of SALD.   The main difference isthat SALDVI uses the pyrolytic products of gas precursor decomposition to infiltrate into layers ofpowder rather than forming a completely free standing shape associated with SALD (2). The170specimens were held together with a clamp (Fig. 1) prior to exposing them to laser.  The precursorgases as well as the processing parameters are summarized in Table 1.  These conditions were usedin the previous work of Shay Harrison (1) for the deposition of SiC and Si3N4 whose XRD patternsare shown in Figures 2 and 3.  Metallographic cross-sections of the formed joints were investigatedusing an Environmental Scanning Electron Microscope (ESEM).                                                                                Figure 1: The clamp used to hold the samples.Table 1: Precursor gases and the processing parameters of experimentsDeposited Material Gas Precursors Pressure (torr) Temperature, °CSilicon Carbide Tetramethylsilane (TMS) and H2 20 TMS and 20 H2 800-1000Silicon Nitride TMS and NH3 20 TMS and 30 NH3 900-1100   Si3N4171ResultsSpecimens of SALDVI silicon carbide/Mo composite were held together and exposed to thelaser under conditions of silicon carbide deposition.  A tight spot joint (Fig. 4) was formed throughthe deposition of silicon carbide.                                                   Figure 4: SiC joint formed over SiC/Mo composite sample.When thin specimens of fully dense silicon nitride materials were exposed to the laser asuccessful spot joint was formed under the conditions of either silicon carbide or silicon nitridedeposition (Figs. 5, 6). Thick fully dense silicon nitride samples were exposed to the laser under theabove experimental conditions.  Unfortunately no joining could be obtained with these specimens.Deposition occurred on one side of the joint but not the other.  Several experiments were carried outwith exposing the samples to the laser in different geometries without forming a spot joint. Figure 5: SiC joint formed over Si3N4 samples.    Figure 6: Si3N4 joint formed over Si3N4 samples.172The microstructures of the silicon carbide and silicon nitride spot joints, as well as thesilicon nitride substrate, are shown in Figures 7, 8, and 9.Fig. 7: A cross section of SiC joint over SiC/Mo composite.   Fig. 8: Si3N4 deposition over Si3N4 substrate.            A, B: Substrate       C: Deposit                  A: Substrate      B: Deposit Fig. 9: Microstructure of Si3N4 substrate DiscussionThe results of this study demonstrate that spot joining of silicon nitride and silicon carbideusing the SALD joining process is possible.  A question that arose is; why did the thin specimensspot join while the thicker specimens did not?  The answer to this question is related to the thermalconductivity of the sample and the available laser power.  The heat sink and resulting thermalgradient of the thinner specimens is much smaller than that of thicker specimens.  The laser wasable to uniformly heat the thinner specimens effectively, allowing deposition to occur on both sidesof the joint at the same time with same deposition rate leading to a successful joint.  For the thickerABABC173specimens, heating and therefore deposition occurred preferentially on one side resulting in a poorspot joint.Future work will concentrate on the formation of a complete joint between silicon nitrideflat samples and silicon nitride tubes.  Other factors that influence joining will be studied, includingthe laser scan speed and laser wavelength.Conclusions1. Spot joints were obtained for the thin fully dense silicon nitride samples and for SALDVIsilicon carbide samples.2. The factors that affect the successful spot joining process are the laser power, the thermalconductivity of the substrate, and the substrate size.References:1. Selective Area Laser Deposition (SALD) Joining of Silicon Carbide With Silicon Carbide Filler,Shay L. Harrison, Ph.D. Dissertation, 1999.2 .  In Situ Thermocouples in Macro-Components Fabricated Using SALD and SALDVITechniques,  I. Evaluation of Processing Parameters, Lianchao Sun, Kevin J. Jakubenas, JamesE. Crocker, Shay Harrison, Leon L. Shaw, and Harris L. Marcus, Materials and ManufacturingProcesses, vol. 13, No. 6, p 859-882, 1998.3 .  In Situ Thermocouples in Macro-Components Fabricated Using SALD and SALDVITechniques, II. Evaluation of Processing Parameters, Lianchao Sun, Kevin J. Jakubenas, JamesE. Crocker, Shay Harrison, Leon L. Shaw, and Harris L. Marcus, Materials and ManufacturingProcesses, vol. 13, No. 6, p 883-907, 1998.4. Gas-Phase Solid Freeform Fabrication of SiC Ceramics Using SALDVI, James E. Crocker,Leon L. Shaw, and Harris L. Marcus, Solid Freeform Fabrication Symposium Proceedings2000, p 168-175.174

Spot Joining of Si3N4 and SIC Ceramics using Selective Area Laser Deposition (SALD) Technique

https://repositories.lib.utexas.edu/bitstream/2152/76161/2/2001-19-Ghayad.pdf

Spot Joining of Si3N4 and SIC Ceramics using Selective Area Laser Deposition (SALD) Technique

Abstract

Similar works

Full text

Available Versions

Texas ScholarWorks