Zircaloy-4(Zr-1.5%Sn-0.2%Fe-0.1%Cr wt%)is usedas nuclear fuel cladding materials and hydride embrittlementis amajor failure mechanism. To explore the effect of δ-hydrideon plastic deformation and performance of Zircaloy-4, in situhigh angular resolution electron backscatter diffraction(HR-EBSD)was used to quantify stress andgeometrically necessarydislocation(GND)density during bending tests of hydride-free and hydride-containingsingle crystalZircaloy-4 microcantilevers. Results suggest that while the stress applied was accommodated by plastic slip in the hydride-free cantilever,the hydride-containing cantilever showedprecipitation-induced GND pile-up at hydride-matrix interfacepre-deformation, andconsiderable locally-increasing GNDdensity under tensile stressupon plastic deformation