CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
Influence of Cr content on the microstructure and mechanical properties of CrxFeNiCu high entropy alloys
Authors
Sirui Huang
Hao Wu
+3 more
Zonghan Xie
Chengyan Zhu
Heguo Zhu
Publication date
1 January 2020
Publisher
Edith Cowan University, Research Online, Perth, Western Australia
Doi
Cite
Abstract
© 2020 Chinese Materials Research Society The effect of Cr content on the microstructure and mechanical properties of CrxFeNiCu high entropy alloys (HEAs) was firstly studied by first-principles calculations. The calculated results show that the hardness of the alloys increased with the expense of its plasticity decrease, if the content of Cr in the alloy increased. In order to verify the calculated results, CrxFeNiCu (x = 0.8, 1, 1.5 and 2) high entropy alloys were synthesized by vacuum induction melting in the present study. The results show that as the value of x increased from 0.8 to 2, the crystal structure changed from single phase face centered cubic (FCC) phase to a mixture of FCC and body centered cubic (BCC) phases. For the single phase FCC (x = 0.8) structure, both the tensile strength and hardness values were low, which were 491.6 MPa and 322.2 HV respectively, however, the plasticity was high, reaching 33.2%. With the formation and growth of BCC phase (x = 2) the tensile strength and hardness of the alloy were significantly improved, which were 872.6 MPa and 808 HV, respectively
Similar works
Full text
Open in the Core reader
Download PDF
Available Versions
Research Online @ ECU
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:ro.ecu.edu.au:ecuworkspost...
Last time updated on 19/11/2020
Adelaide Research & Scholarship
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:digital.library.adelaide.e...
Last time updated on 12/12/2021