CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
research
Controlled release of vascular endothelial growth factor from spray-dried alginate microparticles in collagen-hydroxyapatite scaffolds for promoting vascularization and bone repair.
Authors
Sally-Ann Cryan
Alan Hibbitts
+4 more
Adolfo López-Noriega
Fergal O\u27Brien
Elaine Quinlan
Emmet M Thompson
Publication date
1 April 2017
Publisher
e-publications@RCSI
Abstract
A major limitation with current tissue-engineering approaches is creating functionally vascularized constructs that can successfully integrate with the host; this often leads to implant failure, due to avascular necrosis. In order to overcome this, the objective of the present work was to develop a method to incorporate growth factor-eluting alginate microparticles (MPs) into freeze-dried, collagen-based scaffolds. A collagen-hydroxyapatite (CHA) scaffold, previously optimized for bone regeneration, was functionalized for the sustained delivery of an angiogenic growth factor, vascular endothelial growth factor (VEGF), with the aim of facilitating angiogenesis and enhancing bone regeneration. VEGF was initially encapsulated in alginate MPs by spray-drying, producing particles of \u3c 10 µm in diameter. This process was found to effectively encapsulate and control VEGF release while maintaining its stability and bioactivity post-processing. These VEGF-MPs were then incorporated into CHA scaffolds, leading to homogeneous distribution throughout the interconnected scaffold pore structure. The scaffolds were capable of sustained release of bioactive VEGF for up to 35 days, which was proficient at increasing tubule formation by endothelial cells in vitro. When implanted in vivo in a rat calvarial defect model, this scaffold enhanced vessel formation, resulting in increased bone regeneration compared to empty-defect and VEGF-free scaffolds. This biologically functionalized scaffold, composed entirely of natural-based materials, may offer an ideal platform to promote angiogenesis and tissue regeneration. Copyright © 2015 John Wiley \u26 Sons, Ltd
Similar works
Full text
Open in the Core reader
Download PDF
Available Versions
RCSI Repository
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:figshare.com:article/10766...
Last time updated on 15/11/2023