This work analyzed the phase transformations that occur in the advanced high strength steel (AHSS) 0.41%C- 0.7%Mn- 2.15%Si - 0.013%Al, this material is widely applied to the automobile industry for manufacture vehicle’s body and chassis as a result their excellent mechanical properties such as impact energy absorption and toughness. The Thermo-Calc software enabled us to predict the formation of the following phases: ferrite and carbides from received steel and the presence from austenite, bainite and carbides after heat treatment. The Thermo-Calc calculated results; TTT diagram agrees with micrographs and XRD. The results from austempering heat treatment present a microstructure composed of fine bainite, retained austenite and carbides M7C3, improving their mechanical properties, mainly hardness and ultimate tensile strength, 61 HR30N and 1513 MPa, respectively, compared to the initial condition, 45 HR30N and 856 MPa.En este trabajo se analizó las transformaciones de fase que ocurren en un acero avanzado de alta resistencia (AHSS) 0.41%C - 0.7%Mn - 2.15%Si - 0.013%Al, que se emplea en la industria automotriz para la fabricación de chasis y carrocería debido a sus optimas propiedades mecánicas como absorción de energía de impacto y tenacidad. El software Thermo-Calc permitió predecir las fases presentes como ferrita y carburos en estado inicial y la presencia de austenita, ferrita, bainita y carburos después del tratamiento térmico. Los resultados calculados por Thermo Calc; diagrama TTT concuerdan con lo observado en las micrografías y DRX. Los resultados del tratamiento térmico de austemperizado indican una microestructura compuesta de bainita fina, austenita retenida y carburos M7C3, mejorando sus propiedades mecánicas, principalmente dureza y resistencia máxima, 61 HR30N y 1513 MPa, respectivamente, en comparación con el estado inicial, 45 HR30N y 856 MPa