In this work, we did different austempering´s heat treatments in a ductile iron alloyed with 0.45% Cr and 0.2% V to determinate the window process. The ductile iron was treated in a temperature of 900°C in 60 minutes; after that it moved to another oven with times between 15 to 90 minutes and a temperature of 285°C. In this heat treatment we get two known phases called acicular ferrite and austenite with a major part of carbon. The last phase is analyzed using X-rays´s diffraction in the samples treated in different times. Austenite´s major value was obtained in 60 minutes with a percentage of 35%; meanwhile the minor value was obtained in 15 minutes with 21.7%. Additionally, the samples were evaluated in hardness test. The hardness ´highest value was obtained in 30 minutes (59.9 HRC) and the lowest value was obtained in 90 minutes (53.9 HRC). According with the test was determinate the window process between 60 and 90 minutes.En este trabajo se llevaron a cabo tratamientos térmicos de austemperizado a un hierro dúctil con 0.45 % Cr y 0.2 %V para determinar la ventana óptima de proceso. El hierro dúctil se austenitizó a 900 °C durante 60 min; posteriormente se austemperizó a 285 °C por diferentes tiempos entre 15 a 90 minutos. Durante el tratamiento térmico se obtienen dos fases conocidas como ferrita acicular y austenita con alto contenido de carbono. Esta última fase se cuantifica con rayos X. El valor más elevado de austenita (35%) se obtuvo en la muestra tratada a 60 minutos; mientras que el menor (21.7%) se obtuvo a los 15 minutos. Adicionalmente, se evaluó la dureza de las muestras. El mayor valor de dureza (59.9 HRC) se obtuvo en la muestra tratada a 30 minutos; mientras que la dureza más baja (53.9 HRC) se obtuvo a los 90 minutos. Evaluando los datos la ventana del proceso se encuentra entre 60 y 90 minutos