Spin-coated La0.8Sr0.2Ga0.8Mg0.2O3-δ Electrolyte on Infiltrated Anodes for Direct Methane Fuel Cells

Abstract

Dense micrometric La0.8Sr0.2Ga0.8Mg0.2O3-δ (LSGM) films were deposited by spin-coating on porous LSGM scaffolds characterized by homogeneous pore structure. Porous anodes were infiltrated with aqueous nickel and nickel/copper nitrate solutions, dried and fired at 700°C. Homogeneous metal coating with proper interconnection was observed by SEM, chemical stability was confirmed by XRD, and electrical characterization of anodic substrates was performed. Catalytic activity of different anodes was evaluated ex-situ in a quartz micro-reactor fed with CH4:CO2 mixtureat range 650 and 700°C. To investigate the redox properties of the metallic phases, the anodic substrates were subjected to redox ageing cycles and characterized by H2-TPR