ESTUDO DA OBTENÇÃO E CARACTERIZAÇÃO DE MATERIAIS ABSORVEDORES DE RADIAÇÃO ELETROMAGNÉTICA (8,2 - 12,4 GHz) BASEADOS EM FILMES FINOS DE ÓXIDO DE COBRE, COBRE E ALUMÍNIO
The aim of this work is to study electromagnetic radiation absorbing thin films in the frequency range between 8.2 - 12.4 GHz, based on the copper and aluminum chemical elements, with thicknesses between 30 and 100 nm (in steps of 10 nm). , deposited on poly (ethylene terephthalate) polymer substrate by the magnetron sputtering technique. The results show that copper films with thicknesses between 30nm and 100nm have average values of absorbed energy between 10% (- 0.50 dB) to 48% (- 2.85 dB), and for aluminum between 2.2%. (- 0.10 dB) to 10% (- 0.50 dB). The lower absorption of aluminum compared to copper is related to the lower electrical conductivity of aluminum, which decreases the energy dissipated by the process of electrical depolarization, causing a lower absorption of electromagnetic wave energy.O presente trabalho tem como objetivo estudar filmes finos absorvedores de radiação eletromagnética na faixa de frequências compreendidas entre 8,2 - 12,4 GHz, baseados nos elementos químicos cobre e alumínio, com espessuras entre 30 e 100 nm (em passos de 10 nm), depositados sobre substrato do polímero poli (tereftalato etileno), pela técnica magnetron sputtering. Os resultados obtidos demonstram que filmes de cobre com espessuras entre 30nm a 100nm possuem valores médios da energia absorvida entre 10 % (- 0,50 dB) a 48 % (- 2,85 dB), e para o alumínio entre 2,2% (- 0,10 dB) a 10% (- 0,50 dB). A menor absorção do alumínio em relação ao cobre está relacionada a menor condutividade elétrica do alumínio, o que diminui a energia dissipada pelo processo de despolarização elétrica, provocando uma menor absorção da energia da onda eletromagnética